Rubber comprehensive accelerator and method for preparing same

A technology of accelerators and thiazole accelerators, which is applied in the field of rubber comprehensive accelerators and its preparation, and can solve problems such as poor mechanical properties

Active Publication Date: 2016-06-15
YONGJIA WEICHENG RUBBER IND & TRADE CO LTD
View PDF2 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] The reference document only states that the prior art can give full play to the advantages of various accelerators added, but its mechanical properties are not good

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Rubber comprehensive accelerator and method for preparing same
  • Rubber comprehensive accelerator and method for preparing same
  • Rubber comprehensive accelerator and method for preparing same

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0033] The preparation method of the present invention is as follows:

[0034] (1) Take high-activity zinc oxide, post-effect sulfenamide accelerator, thiazole accelerator and ultra-high-speed accelerator successively according to the parts by weight in Table 1, and mix the above raw materials;

[0035] (2) design and take dispersant according to the parts by weight in table 1;

[0036] (3) According to the parts by weight design in Table 1, take respectively EPDM rubber and organic active agent, put it into the kneader and knead for 6-9 minutes and then discharge the material;

[0037] (4) Put the weighed and mixed raw materials in (1) and (2) into the internal mixer, and discharge the material when the temperature of the internal mixer rises to 81-89°C;

[0038] (5) After fully mixing the mixture produced in (3) and (4) to form a plastic object, put it into an open mill for dispersion and cooling;

[0039] (6) Put the material after the cooling treatment into the granulati...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a rubber comprehensive accelerator and a method for preparing the same.The rubber comprehensive accelerator mainly comprises, by weight, 40-75 parts of high-activity zinc oxide, 2-9 parts of after-effectiveness sulfenamide accelerators, 7-15 parts of thiazole accelerators, 10-21 parts of ultrahigh-speed accelerators and 8-19 parts of macromolecular carriers.The rubber comprehensive accelerator and the method have the advantages that different types of additives can be sufficiently mixed with one another by the aid of a step-by-step adding process, accordingly, the rubber comprehensive accelerator is excellent in aging resistance and yellowing resistance, and mechanical properties of rubber products further can be improved.

Description

technical field [0001] The invention relates to the field of rubber industry, more specifically, it relates to a comprehensive rubber accelerator and a preparation method thereof. Background technique [0002] Rubber accelerator is also called rubber vulcanization accelerator. In the rubber vulcanization process, sulfur and rubber are mainly used for vulcanization reaction. However, the crosslinking reaction between sulfur and rubber is very slow. Therefore, adding the rubber vulcanization accelerator to the rubber compound can promote the activation of the vulcanizing agent, thereby accelerating the reaction speed of the vulcanizing agent and rubber molecules, shortening the vulcanization time, reducing the vulcanization reaction temperature, and reducing the amount of vulcanizing agent. [0003] The application of rubber accelerators in the rubber vulcanization process can greatly improve the production efficiency of rubber products, reduce product costs, improve the physi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L23/16C08L23/06C08L71/02C08K13/02C08K5/47C08K3/22C08K5/5398C08K5/053
CPCC08K3/22C08K5/053C08K5/47C08K5/5398C08K13/02C08K2003/2296C08K2201/014C08L23/16C08L2205/03C08L23/06C08L71/02
Inventor 章兴武
Owner YONGJIA WEICHENG RUBBER IND & TRADE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com