A kind of carbon paper composite material and preparation method thereof for laser lamination

A lamination molding and composite material technology, which is applied in the field of laser lamination carbon paper composite materials and its preparation, can solve the problems of few optional raw materials, poor mechanical strength of parts, complex post-processing technology, etc., and achieve shortening The effect of production cycle, fast molding speed and cost reduction

Active Publication Date: 2018-11-13
HEFEI GENIUS NEW MATERIALS
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] But at the same time, the existing materials of laser lamination technology are mainly composite materials such as paper, resin materials and clay, which have shortcomings such as few types of raw materials to choose from, poor mechanical strength of the parts, and high moisture absorption rate of the parts, and often require complicated Post-processing technology, it is difficult to shorten the production cycle while ensuring product quality

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] (1) Prepare raw materials according to the following proportions:

[0034] 95 parts of polypropylene resin,

[0035] 1 part of coupling agent γ-aminopropyltriethoxysilane,

[0036] Antioxidant tetrakis[β-(3,5-di-tert-butyl-4-hydroxyphenyl)propionic acid]pentaerythritol ester 0.2 parts,

[0037] Antioxidant tris [2.4-di-tert-butylphenyl] phosphite 0.3 parts,

[0038] Heat stabilizer calcium stearate 0.5 parts,

[0039] Lubricant ethylene bis stearamide 0.5 parts,

[0040] 5 copies of carbon paper;

[0041] (1) Mix polypropylene resin, coupling agent, antioxidant, heat stabilizer and lubricant uniformly to obtain a premix;

[0042] (2) Lay a layer of premixed material on the upper and lower surfaces of the carbon paper with a molding machine, and mold it into a foil with a thickness of 0.5 mm at 180 ° C to obtain a carbon paper composite material.

Embodiment 2

[0044] (1) Prepare raw materials according to the following proportions:

[0045] 93 parts of polypropylene resin,

[0046] 2 parts of coupling agent γ-aminopropyltriethoxysilane,

[0047] Antioxidant tetrakis[β-(3,5-di-tert-butyl-4-hydroxyphenyl)propionic acid]pentaerythritol ester 0.5 parts,

[0048] Antioxidant tris [2.4-di-tert-butylphenyl] phosphite 0.8 parts,

[0049] Heat stabilizer calcium stearate 1 part,

[0050] Lubricant ethylene bis stearamide 1 part,

[0051] 7 copies of carbon paper;

[0052] (1) Mix polypropylene resin, coupling agent, antioxidant, heat stabilizer and lubricant uniformly to obtain a premix;

[0053] (2) Lay a layer of premixed material on the upper and lower surfaces of the carbon paper with a molding machine, and mold it into a foil with a thickness of 1 mm at 190 ° C to obtain a carbon paper composite material.

Embodiment 3

[0055] (1) Prepare raw materials according to the following proportions:

[0056] 91 parts of polypropylene resin,

[0057] 3 parts of coupling agent γ-aminopropyltriethoxysilane,

[0058] Antioxidant tetrakis[β-(3,5-di-tert-butyl-4-hydroxyphenyl)propionic acid]pentaerythritol ester 0.8 parts,

[0059] Antioxidant tris [2.4-di-tert-butylphenyl] phosphite 1.2 parts,

[0060] 3 parts of heat stabilizer calcium stearate,

[0061] Lubricant ethylene bis stearamide 3 parts.

[0062] 9 copies of carbon paper;

[0063] (1) Mix polypropylene resin, coupling agent, antioxidant, heat stabilizer and lubricant uniformly to obtain a premix;

[0064] (2) Lay a layer of premixed material on the upper and lower surfaces of the carbon paper with a molding machine, and mold it into a foil with a thickness of 2 mm at 200 ° C to obtain a carbon paper composite material.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention provides a carbon paper composite material for laser lamination molding and a preparation method thereof, which is composed of the following raw materials in the following mass ratio: 5-20 parts of carbon paper, 80-95 parts of resin matrix, coupling agent 1-5 parts, 0.5-3 parts of antioxidant, 0.5-5 parts of heat stabilizer and 0.5-5 parts of lubricant. The carbon paper composite material for laser lamination prepared by the present invention has the characteristics of simple preparation process, high mechanical strength, fast forming speed and low water absorption rate, greatly shortens the production cycle and reduces costs, and can be directly applied and promoted in In the field of laser lamination manufacturing technology, it can be directly processed into structural parts.

Description

technical field [0001] The invention belongs to the technical field of laser lamination molding, and in particular relates to a carbon paper composite material for laser lamination molding and a preparation method thereof. Background technique [0002] Laser lamination technology relies on CAD simulation technology and computer control technology. The feeding system transports the raw materials to the workbench in sections, cuts the foil along the vertical and horizontal directions to the desired contour, and finally compresses the multi-layer foil by a hot press Three-dimensional artifacts are obtained. This molding technology has the characteristics of fast molding speed, no support structure and no pollution, and can directly prepare large-sized parts. [0003] But at the same time, the existing materials of laser lamination technology are mainly composite materials such as paper, resin materials and clay, which have shortcomings such as few types of raw materials to cho...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/12C08K13/04C08K7/06C08K5/544C08K5/5435C08K5/098C08K5/134C08K5/526B29C43/18
Inventor 杨桂生李袅
Owner HEFEI GENIUS NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap