A kind of flame-retardant melt-blown nonwoven material and preparation method thereof

A non-woven material and melt-blown technology, which is applied in the manufacture of non-woven fabrics, fire-resistant and flame-retardant filaments, textiles and papermaking, etc., can solve the problems of poor flame retardancy, achieve good flame-retardant durability, promote development, and expand use range effect

Active Publication Date: 2018-06-29
ZHANGJIAGANG JUNMA NON WOVEN CO LTD
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In order to overcome the deficiencies of the prior art, the object of the present invention is to provide a flame-retardant melt-blown nonwoven material, which effectively solves the problem of poor flame retardancy of the melt-blown non-woven material in the prior art, making it more widely used. Can effectively promote the development of melt blown nonwovens industry

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of flame-retardant melt-blown nonwoven material and preparation method thereof
  • A kind of flame-retardant melt-blown nonwoven material and preparation method thereof
  • A kind of flame-retardant melt-blown nonwoven material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] 20% by mass of ultrafine aluminum hydroxide, 30% of ultrafine magnesium hydroxide, 20% of nano-scale attapulgite, 20% of nano-zinc oxide, 3% of surfactant, 3% of coupling agent Add 4% smoke suppressant to a high-speed mixer, heat up and mix at a high speed to obtain a composite flame retardant; wherein, the particle size of ultrafine aluminum hydroxide and ultrafine magnesium hydroxide is 20-100nm, and nano-scale attapulgite The particle size of the nano-zinc oxide is 50-100nm, the particle size of the nano-zinc oxide is 10-50nm, the surfactant is a carboxylate anionic surfactant, the coupling agent is a silane coupling agent, and the smoke suppressant is molybdenum trioxide .

[0030] Blend and granulate the composite flame retardant and PBT chips prepared above at 220°C to make flame-retardant melt-blown PBT chips, wherein the composite flame retardant accounts for 10% by mass; the flame-retardant melt-blown PBT The slices are fed into the screw extruder for melt-blo...

Embodiment 2

[0033] 30% by mass of ultrafine aluminum hydroxide, 30% of ultrafine magnesium hydroxide, 15% of nano-scale attapulgite, 15% of nano-zinc oxide, 4% of surfactant, 3% of coupling agent Add 3% smoke suppressant to a high-speed mixer, heat up and mix at a high speed to obtain a composite flame retardant; wherein, the particle size of ultrafine aluminum hydroxide and ultrafine magnesium hydroxide is 50-150nm, and nano-scale attapulgite The particle size of the zinc oxide is 50-100nm, the particle size of the nano-zinc oxide is 50-100nm, the surfactant is a carboxylate anionic surfactant or a sulfate anionic surfactant, and the coupling agent is a silane coupling agent Or titanate coupling agent, smoke suppressant is molybdenum trioxide or ammonium octamolybdate.

[0034] Blend and granulate the composite flame retardant and PBT chips prepared above at 230°C to make flame-retardant melt-blown PBT chips, wherein the composite flame retardant accounts for 15% by mass; the flame-retar...

Embodiment 3

[0037] 30% by mass of ultrafine aluminum hydroxide, 30% of ultrafine magnesium hydroxide, 20% of nano-scale attapulgite, 10% of nano-zinc oxide, 2% of surfactant, 3% of coupling agent Add 5% smoke suppressant to a high-speed mixer, heat up and mix at high speed to obtain a composite flame retardant; among them, the particle size of ultrafine aluminum hydroxide and ultrafine magnesium hydroxide is 300-500nm, and nano-scale attapulgite The particle size of the nano-zinc oxide is 100-200nm, the particle size of the nano-zinc oxide is 70-100nm, the surfactant is a carboxylate anionic surfactant or a sulfate anionic surfactant, and the coupling agent is a silane coupling agent Or titanate coupling agent, smoke suppressant is molybdenum trioxide or ammonium octamolybdate.

[0038] Blend and granulate the composite flame retardant and PBT chips prepared above at 250°C to make flame-retardant melt-blown PBT chips, wherein the composite flame retardant accounts for 15% by mass; the fla...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a flame-retardant melt-blowing nonwoven material which is prepared from, by weight, 80%-90% of PBT slices and 10%-20% of a composite flame retardant. The composite flame retardant is prepared from, by weight, 20%-30% of superfine aluminum hydroxide, 20%-30% of superfine magnesium hydroxide, 10%-20% of nanoscale attapulgite, 10%-20% of nano-zinc oxide, 1%-5% of a surfactant, 1%-5% of a coupling agent and 1%-5% of a smoke inhibitor. According to the flame-retardant melt-blowing nonwoven material, the problem that in the prior art, the flame retardancy of a melt-blowing nonwoven material is poor is effectively solved, therefore, the using range of the flame-retardant melt-blowing nonwoven material is wider, and development of a melt-blowing nonwoven material industry can be effectively promoted.

Description

technical field [0001] The invention relates to the field of nonwoven material manufacturing, in particular to a flame-retardant melt-blown nonwoven material and a preparation method thereof. Background technique [0002] With the continuous improvement of domestic living standards, the performance requirements of textiles are also getting higher and higher. Among them, flame retardancy has attracted more and more attention. Some industrially developed countries have formulated flame-retardant regulations for textiles very early, stipulating that curtains and curtains in public places such as theaters, hospitals, hotels, and clothing fabrics for the elderly, children, and disabled must meet certain flame-retardant standards. A survey report pointed out that the probability of fire accidents caused by flame-retardant textiles will be reduced by at least 20%. How to improve the flame retardancy of meltblown nonwoven materials, expand the application field of meltblown nonwove...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): D01F6/92D01F1/07D04H1/55
CPCD01F1/07D01F6/92D04H1/55
Inventor 闵懂
Owner ZHANGJIAGANG JUNMA NON WOVEN CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap