Composition for improving glossiness of polypropylene and reducing haze of polypropylene and application thereof

A composition and technology of polypropylene, applied in the field of compositions for improving the gloss of polypropylene and reducing the haze of polypropylene, and its application field, which can solve problems such as difficulty in improving gloss, reducing haze, and difficulty in lowering processing temperature , to achieve the effect of improving gloss, reducing haze, and low processing temperature

Inactive Publication Date: 2016-06-01
GCH TECH
View PDF5 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] In order to solve the problems that the processing temperature is difficult to reduce, the haze is reduced and the gloss is difficult to improve in the production of polypropylene, the present invention provides a transparent nucleating agent composition with a low eutectic point, which comprises 1,3:2 ,4-di-O-(p-chlorobenzylidene)-D-sorbitol and 1,3:2,4-bis(3,4-dimethylbenzylidene)-D-sorbitol, In this composition, 1,3:2,4-bis-O-(p-chlorobenzylidene)-D-sorbitol and 1,3:2,4-bis(3,4-dimethylbenzylidene The weight ratio of base)-D-sorbitol satisfies the eutectic point of 240°C-245°C

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composition for improving glossiness of polypropylene and reducing haze of polypropylene and application thereof
  • Composition for improving glossiness of polypropylene and reducing haze of polypropylene and application thereof
  • Composition for improving glossiness of polypropylene and reducing haze of polypropylene and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] Example 1 Survey and draw the binary solid-liquid equilibrium phase diagram of the NA-2+NA-98 composition, and determine the eutectic temperature and composition of the NA-2+NA-98 composition.

[0037] Determination of 1,3:2,4-bis-O-(p-chlorobenzylidene)-D-sorbitol (NA-2) and 1,3:2,4-bis(3,4- The melting curves of dimethylbenzylidene)-D-sorbitol (NA-98) and NA-2 and NA-98 in different proportion compositions can be drawn according to the principle of phase equilibrium thermodynamics NA-2+NA- 98 binary composition solid-liquid equilibrium phase figure 1 . Point E in the binary phase diagram is the eutectic point of the NA-2+NA-98 binary composition, the eutectic temperature is 240.29°C, and the composition of the binary composition is W NA-2 70%, that is, the weight ratio of NA-2 to NA-98 is 7:3.

[0038] The specific ratio of NA-2 and NA-98 and their melting peak temperature data are shown in Table 1.

[0039] Table 1NA-2 and NA-98 composition melting peak temperatu...

Embodiment 2

[0045] Embodiment 2 nucleating agent composition prepares polymkeric substance

[0046] 0.2% of the composition was added to the polymer base material. The ratio of NA-2 and NA-98 in the composition was mixed according to the composition number, and the haze of the polymer was measured at different temperatures. For details, see Table 3 below. The base material used therein is random copolymerized polypropylene MI=25g / 10min.

[0047] Table 3 Haze of polymers prepared from NA-2 and NA-98 compositions under different processing temperatures

[0048]

[0049] NA-2 can reduce the haze of NA-98 at a processing temperature of 180-190°C, and the reduction of haze is very obvious. The temperature of composition 11 is the processing temperature of single NA-98. At 180°C, the haze It is 36.2, and it is 30.1 at the processing temperature of 190°C, and the composition added with NA-2 and NA-98, such as composition 1-9, composition 12-13, can be processed at 180°C and 190°C Reduce haz...

Embodiment 3

[0055] Example 3 Comparison of haze properties using polymers comprising NA-98 compositions

[0056] Add 0.2wt% composition in the polymer base material, the ratio of NA-2 and NA-98 in the composition, the ratio of NA-98 and 1,3:2,4-di-p-methylbenzylidene sorbitol (MDBS) Ratio, mix according to the ratio corresponding to the serial number of the composition, and measure the haze of the polymer at different temperatures. For details, see Table 5 below. The base material used therein is random copolymerized polypropylene MI=25g / 10min.

[0057] Table 5 Effect of different compositions on polymer haze properties at different processing temperatures

[0058]

[0059]

[0060] The composition of NA-2 and NA-98 has little effect on PP haze when processed at low temperature. However, if MDBS and NA-98 are mixed, it will be difficult to reduce the haze at low temperature.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a composition for improving the glossiness of polypropylene and reducing the haze of polypropylene and application thereof.The composition is prepared from two different types of transparent polyolefin nucleating agents 1,3:2,4-2-bi-(p-chlorophenyl methylene)-D-sorbose and 1,3:2,4-bi(3,4-dimethyl benzylidene)-D-sorbitol, can unexpectedly improve the glossiness of the polypropylene and reduce the haze of the polypropylene, meanwhile can effectively reduce the injection and extrusion temperatures of the polypropylene and achieves the effects of improving the transparency quality of polypropylene products and reducing the production cost.

Description

technical field [0001] The invention relates to a composition for improving the glossiness of polypropylene and reducing the haze of polypropylene and its application. The composition consists of two different polyolefin transparent nucleating agents 1,3:2,4-di-O-( p-chlorobenzylidene)-D-sorbitol and 1,3:2,4-bis(3,4-dimethylbenzylidene)-D-sorbitol combination. Background technique [0002] Chinese patent application number 02805064.9 discloses a polyolefin additive composition containing a mixture of bis(3,4-dimethylbenzylidene) sorbitol and bis(p-methylbenzyl) sorbitol, wherein bis (3,4-Dimethylbenzyl)sorbitol accounts for 5-95% by weight of the entire mixture and bis(p-methylbenzyl)sorbitol accounts for 5-95% by weight of the entire mixture. The problem it solves is to provide a lower cost alternative to 3,4-DMDBS-only polyolefin clarifiers that exhibit haze measurements below 10% for the same polyolefin articles and compositions. Olefin compositions or articles. [000...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L23/14C08K5/1575
CPCC08K5/1575C08L23/14C08K2201/014C08L2205/24
Inventor 赵文林莫志华黄秀娴
Owner GCH TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com