Auxiliary capable of improving printing performance of composite ivory board and preparation method thereof

A technology of composite white cardboard and additives, which is applied in the field of papermaking, can solve the problems of composite white cardboard such as difficult adhesion, printing, and high static electricity, and achieve the effects of increasing antistatic function, improving ink absorption, and improving printing performance

Active Publication Date: 2016-05-11
贵州金马包装材料有限公司
View PDF7 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] In order to solve the problem of difficult adhesion and printing of composite white cardboard in the printing process, the need for special inks and the existence of high static electricity in the printing process, and to further improve the ink absorption of composite white cardboard in the printing process, the embodiments of the present invention provide An auxiliary agent and a preparation method for improving the printing performance of composite white cardboard, by adopting the surface-modified ZnO nano thorn ball particles having a siphon microstructure, and at the same time using an active agent for chemical surface modification, and the present invention can further Improving Ink Absorption of Composite White Cardboard

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Auxiliary capable of improving printing performance of composite ivory board and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] This embodiment includes the following steps:

[0031] 1) Preparation of ZnO nano thorn ball particles;

[0032] Under the condition that the temperature of the deionized water is raised to 30°C, high-purity argon gas with a purity of 99.95% is passed into the deionized water for 0.5 h, and after the oxygen in the pure water is removed, an inorganic zinc salt is added, And keep stirring, set the stirring speed to 800rpm, and the stirring time to 0.2h, then add the dispersant, stir for 0.2h to make the solution mix evenly, and obtain the mixed liquid A;

[0033] Add inorganic additives to the mixed solution A, adjust the pH value to 8, continue to stir for 0.3h, and pass argon into the mixed solution A, heat the mixed solution A, and evaporate the mixed solution A After moisture, reflux and cool down to room temperature to obtain solution B containing ZnO nano thorn ball particles, wherein the heating rate is set to 6-8°C / min, and the cooling rate is set to 5-8°C / min. ...

Embodiment 2

[0039] This embodiment includes the following steps:

[0040] 1) Preparation of ZnO nano thorn ball particles;

[0041] Under the condition that the temperature of the deionized water is raised to 50°C, high-purity argon gas with a purity of 99.95% is introduced into the deionized water for 1 hour, after the oxygen in the pure water is removed, an inorganic zinc salt is added, and Stir continuously, set the stirring speed to 1000rpm, and the stirring time to 0.2h, then add the dispersant, stir for 0.2h to mix the solution evenly, and obtain the mixed liquid A;

[0042] Add inorganic additives to the mixed solution A, adjust the pH value to 8.5, continue to stir for 0.4h, and pass argon into the mixed solution A, heat the mixed solution A, and evaporate the mixed solution A After moisture, reflux and cool down to room temperature to obtain solution B containing ZnO nano thorn ball particles, wherein the heating rate is set to 6-8°C / min, and the cooling rate is set to 5-8°C / min...

Embodiment 3

[0048] This embodiment includes the following steps:

[0049] 1) Preparation of ZnO nano thorn ball particles;

[0050] Under the condition that the temperature of the deionized water is raised to 70°C, high-purity argon gas with a purity of 99.95% is introduced into the deionized water for 1 hour. After the oxygen in the pure water is removed, an inorganic zinc salt is added, and Stir continuously, set the stirring speed to 1500rpm, and the stirring time to 0.2h, then add the dispersant, stir for 0.2h to make the solution mix evenly, and obtain the mixed liquid A;

[0051] Add inorganic additives to the mixed solution A, adjust the pH value to 9, continue to stir for 0.5 h, and pass argon into the mixed solution A, heat the mixed solution A, and evaporate the mixed solution A After moisture, reflux and cool down to room temperature to obtain solution B containing ZnO nano thorn ball particles, wherein the heating rate is set to 6-8°C / min, and the cooling rate is set to 5-8°C...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
lengthaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses an auxiliary capable of improving printing performance of a composite ivory board and a preparation method thereof. The auxiliary is prepared from, by weight, 10-20 parts of inorganic zinc salt, 10-20 parts of inorganic additive, 0.5-1 part of surfactant, 0.5-1 part of dispersant and 60-80 parts of deionized water. ZnO nano acanthosphere particles after surface modification are adopted as the auxiliary in the process of printing the composite ivory board; the ZnO nano acanthosphere particles have siphon microstructure, and an active agent is adopted for chemical surface modification, so that ink absorptivity of the composite ivory board can be further improved.

Description

technical field [0001] The invention relates to the technical field of papermaking, in particular to an additive for improving the printing ink absorption of composite white cardboard and a preparation method thereof. Background technique [0002] Paper is one of the indispensable and important supplies for human study, work and life. Traditional papermaking has caused great damage to the ecological environment due to excessive felling of trees and the three wastes produced in the traditional papermaking industry. The demand for environmental protection in raw materials and paper product processing is getting higher and higher. Composite white cardboard, that is, stone paper, is a new material between paper and plastic, which can replace some traditional functional paper, professional paper, and most of the traditional plastic packaging. And it has the characteristics of low cost and controllable degradation, which can save users a lot of cost and will not cause pollution. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08K9/06C08K3/22C08K3/26C08L23/12
CPCC08K3/22C08K3/26C08K9/06C08K2003/2296C08K2003/265C08L23/12
Inventor 陈庆曾军堂叶任海陈兵
Owner 贵州金马包装材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com