Aluminum oxide ceramic chip treatment technology

A technology of alumina ceramics and processing technology, applied in chemical instruments and methods, cleaning methods and utensils, cleaning methods using liquids, etc. Small problems, to achieve the effect of light weight, extended equipment life, strong surface adsorption

Inactive Publication Date: 2016-05-11
解伟伟
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The hardness of the ceramic patch is ≥ HRA85, second only to the hardness of diamond, and the surface is smooth, the friction coefficient is small, and the wear resistance is very ideal, especially in the high temperature oxidizing medium or corrosive medium, the material of the ceramic patch has better performance than other metal materials. It is much superior. Ordinary ceramic sheets and rubber cannot be bonded together. After using glue, the bond is not firm, and the ceramic sheets need to be processed.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A process for treating alumina ceramic sheets, the steps are as follows:

[0027] (1) Cleaning with distilled water: Place the ceramic piece in 100% pure water for cleaning and drying;

[0028] (2) Ketone washing: Soak the cleaned ceramic sheet in 70% acetone for half an hour and dry it;

[0029] (3) Alkaline cleaning: Soak the ketone-washed ceramic sheet in 10% sodium carbonate solution for half an hour and dry it;

[0030] (4) Pickling: Soak the ceramic sheet dried in step (3) in 8% sulfuric acid solution and dry.

Embodiment 2

[0032] A process for treating alumina ceramic sheets, the steps are as follows:

[0033] (1) Cleaning with distilled water: Place the ceramic piece in 100% pure water for cleaning and drying;

[0034] (2) Ketone washing: Soak the cleaned ceramic sheet in 75% acetone for half an hour and dry it;

[0035] (3) Alkaline cleaning: Soak the ketone-washed ceramic sheet in 15% sodium carbonate solution for half an hour and dry it;

[0036] (4) Pickling: Soak the ceramic sheet dried in step (3) in 10% sulfuric acid solution and dry.

Embodiment 3

[0038] A process for treating alumina ceramic sheets, the steps are as follows:

[0039] (1) Cleaning with distilled water: Place the ceramic piece in 100% pure water for cleaning and drying;

[0040] (2) Ketone washing: Soak the cleaned ceramic sheet in 80% acetone for half an hour and dry it;

[0041] (3) Alkaline cleaning: Soak the ketone-washed ceramic sheet in 20% sodium carbonate solution for half an hour and dry it;

[0042] (4) Pickling: Soak the ceramic sheet dried in step (3) in 12% sulfuric acid solution and dry.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
Login to View More

Abstract

The invention discloses an aluminum oxide ceramic chip treatment technology which comprises the following steps that 1, a ceramic chip is washed with distilled water, wherein the ceramic chip is placed in 100% pure water to be cleaned and then dried; 2, acetone washing is carried out, wherein the cleaned ceramic chip is placed in 70-80% acetone to be soaked and then dried; 3, alkali washing is carried out, wherein the ceramic chip washed with the acetone is placed in a 8-12% sodium carbonate solution to be soaked and then dried. The aluminum oxide ceramic chip treatment technology has the advantages that the ceramic chip is high in hardness, excellent in wear resistance, low in weight and high in surface adsorption capacity which is 10-20 times that of an untreated ceramic chip, and is quite firm and durable after being combined with rubber through glue.

Description

technical field [0001] The invention relates to the technical field of alumina ceramic sheet processing, in particular to an alumina ceramic sheet processing process. Background technique [0002] Alumina ceramics: high alumina content, relatively dense structure, and special properties, so it is called special ceramics. Al2O3. The ceramic material is a close-packed hexagonal structure composed of oxygen ions, and aluminum ions are filled in two-thirds of the octahedral gaps. This is the same stable α-Al2O3 structure as natural corundum, so the ceramic has a high melting point, high Hardness, with excellent wear resistance. The hardness of the ceramic patch is ≥ HRA85, second only to the hardness of diamond, and the surface is smooth, the friction coefficient is small, and the wear resistance is very ideal, especially in the high temperature oxidizing medium or corrosive medium, the material of the ceramic patch has better performance than other metal materials. It is much...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B41/80B08B3/04B08B3/08
CPCC04B41/00B08B3/04B08B3/08C04B41/009C04B41/80
Inventor 解伟伟
Owner 解伟伟
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com