Concrete air-added heat preservation brick and preparation method thereof

A technology of thermal insulation bricks and concrete, which is applied in the field of building materials, can solve problems such as inability to bear loads, and achieve the effects of good thermal insulation, high bending strength, and high compressive strength

Active Publication Date: 2016-05-04
吉安市第四建筑工程有限公司
View PDF4 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Lightweight concrete (full light concrete), such as foam concrete and aerated concrete, has the advantages of light weight, heat preservation, good sound absorption and easy processing, but it cannot bear weight

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] a. Take 40 kg of fly ash with a particle size of 20-30 μm, 10 kg of titanium nitride with a particle size of 10-20 μm, 20 kg of metakaolin with a particle size of 2-5 μm, and ceramic polishing with a particle size of 15-20 μm 35 kg of waste residue, mixed and stirred evenly;

[0023] b. Take the average diameter of 3.3 μm produced by Zhejiang Weiye Crystal Fiber Co., Ltd., 4 kilograms of F-1000 polycrystalline mullite fiber, and 4 kilograms of 6 mm glass fiber chopped strands produced by Zibo Bangsen Composite Materials Co., Ltd., mix Stir well;

[0024] c. Add 120 kg of ordinary Portland cement, 1 kg of ammonium polyphosphate, 1 kg of sodium dehydroacetate, 3 kg of pine tar, and SH-J type polycarboxylate high-performance water reducing agent produced by Zhoukou Sanhui Engineering Materials Co., Ltd. 4.5 kg of agent, mixed and stirred evenly;

[0025] D, get 58 kilograms of papermaking waste water, the powder in step a, join in the mixture in step c, stir;

[0026] e...

Embodiment 2

[0029] a. Take 38 kg of fly ash with a particle size of 20-30 μm, 9.5 kg of titanium nitride with a particle size of 10-20 μm, 19 kg of metakaolin with a particle size of 2-5 μm, and ceramic polishing with a particle size of 15-20 μm 33.5 kg of waste residue, mixed and stirred evenly;

[0030] B, get the average diameter of 3.3 μm produced by Zhejiang Weiye Crystal Fiber Co., Ltd., 3.5 kilograms of F-1000 polycrystalline mullite fiber, and 3.5 kilograms of 6 mm glass fiber chopped strands produced by Zibo Bangsen Composite Material Co., Ltd., mix Stir well;

[0031] c. Add 115 kg of ordinary Portland cement, 1 kg of ammonium polyphosphate, 1 kg of sodium dehydroacetate, 3 kg of pine tar, and SH-J type polycarboxylate high-performance water reducing agent produced by Zhoukou Sanhui Engineering Materials Co., Ltd. 4 kg of agent, mixed and stirred evenly;

[0032] D, get 55 kilograms of papermaking waste water, the powder in step a, join in the mixture in step c, stir;

[0033...

Embodiment 3

[0036] a. Take 42 kg of fly ash with a particle size of 20-30 μm, 11 kg of titanium nitride with a particle size of 10-20 μm, 21 kg of metakaolin with a particle size of 2-5 μm, and ceramic polishing with a particle size of 15-20 μm 36 kg of waste residue, mixed and stirred evenly;

[0037] B, get the average diameter of 3.3 μm produced by Zhejiang Weiye Crystal Fiber Co., Ltd., 4.5 kilograms of F-1000 polycrystalline mullite fiber, and 4.5 kilograms of 6 mm glass fiber chopped strands produced by Zibo Bangsen Composite Material Co., Ltd., mix Stir well;

[0038] c. Add 125 kg of ordinary Portland cement, 1 kg of ammonium polyphosphate, 1 kg of sodium dehydroacetate, 3 kg of pine tar, and SH-J type polycarboxylate high-performance water reducing agent produced by Zhoukou Sanhui Engineering Materials Co., Ltd. 5 kg of agent, mixed and stirred evenly;

[0039] d, get 62 kilograms of papermaking waste water, the powder in step a, join in the mixture in step c, stir;

[0040] e...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

A concrete air-added heat preservation brick is prepared from, by weight, 115-125 parts of ordinary Portland cement, 100-110 parts of composite filler, 7-9 parts of reinforced filler, 7-8 parts of composite forming agent, 9-10 parts of additive and 55-62 parts of papermaking wastewater. The composite filler is prepared from coal ash, titanium nitride, metakaolin and ceramic polishing waste. The reinforced filler is prepared from polycrystal mullite cellucotton and chopped glass fiber. The composite forming agent is prepared from dioctyl sodium sulfosuccinate, alkyl polyglucoside and pentaerythritol stearate. The additive is prepared from ammonium polyphosphate, sodium dehydroacetate, pine tar and a polycarboxylates high performance water-reducing agent. The concrete air-added heat preservation brick has the advantages of quite outstanding high pressure resistance and high bending strength, and is good in heat preservation effect.

Description

technical field [0001] The invention belongs to the technical field of building materials, in particular to a concrete aerated heat insulating brick and a preparation method thereof. Background technique [0002] Selection of exterior wall materials When selecting exterior wall materials, attention should be paid to the load-bearing, heat preservation, moisture-proof and economic requirements of the exterior wall. Clay solid brick walls have the advantages of low price, strong heat storage capacity, good thermal stability, and certain moisture absorption and moisture dissipation effects. However, this kind of wall material is heavy and thick, and construction is time-consuming. The thermal insulation performance of the clay hollow brick wall is about twice that of the solid brick wall, the weight is 20-40% lighter, and the strength is also higher. Concrete hollow bricks have similar thermal insulation properties to hollow bricks. Lightweight aggregate concrete walls have t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B38/02C04B28/04C04B14/10C04B14/32C04B14/42C04B14/46C04B18/08C04B18/16C04B22/16C04B24/08C04B24/16C04B24/34C04B24/38
CPCC04B28/04C04B18/08C04B14/325C04B14/106C04B18/165C04B14/42C04B14/4656C04B24/161C04B24/38C04B24/08C04B22/16C04B24/34C04B38/02Y02W30/91
Inventor 王湖彬
Owner 吉安市第四建筑工程有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com