Nanometer colorful thermal insulation mortar paint

A thermal insulation mortar and color technology, applied in the field of decorative coatings, can solve the problems of coatings that cannot meet the needs of the market and have single functions, and achieve the effects of bright colors, reduced burdens, and light weight

Inactive Publication Date: 2016-04-20
肖皖松
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Existing decorative coatings have single functions, and with the development of science and technology, coatings with single functions cannot meet the needs of the market gradually

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] In the embodiment of the present invention, a nano-color thermal insulation mortar paint is composed of the following raw materials in parts by weight: 133 parts of binder, 29 parts of dispersant, 160.05 parts of filler, 4.9 parts of auxiliary agent, and 0.9 part of color paste.

[0019] The dispersant is water.

[0020] The adhesive is composed of the following raw materials in parts by weight: 90.25 parts of silicone acrylic emulsion, 28.5 parts of epoxy emulsion, and 14.25 parts of acrylic emulsion.

[0021] The filler is composed of the following raw materials in parts by weight: 43.65 parts of inorganic hollow vitrified microspheres, 29.1 parts of heavy calcium, 29.1 parts of alumina, 43.65 parts of quartz sand, and 14.55 parts of wood fiber.

[0022] The auxiliary agent is composed of the following raw materials in parts by weight: 0.5 part of glycerol, 0.5 part of sodium lauryl sulfate, 1 part of hydroxyethyl cellulose, 1 part of nano titanium dioxide, and 1 part...

Embodiment 2

[0028] In the embodiment of the present invention, a nano-color thermal insulation mortar paint is composed of the following raw materials in parts by weight: 140 parts of binder, 29 parts of dispersant, 165 parts of filler, 5 parts of auxiliary agent, and 1 part of color paste.

[0029] The dispersant is water.

[0030] The adhesive is composed of the following raw materials in parts by weight: 90.25-99.75 parts of silicon-acrylic emulsion, 28.5-31.5 parts of epoxy emulsion, and 14.25-15.75 parts of acrylic emulsion.

[0031] The filler is composed of the following raw materials in parts by weight: 43.65-46.35 parts of inorganic hollow vitrified microspheres, 29.1-30.9 parts of heavy calcium, 29.1-30.9 parts of aluminum oxide, 43.65-46.35 parts of quartz sand, and 14.55-15.45 parts of wood fiber.

[0032] The auxiliary agent is composed of the following raw materials in parts by weight: 0.5 part of glycerol, 0.5 part of sodium lauryl sulfate, 1 part of hydroxyethyl cellulose,...

Embodiment 3

[0038] In the embodiment of the present invention, a nano-color thermal insulation mortar paint is composed of the following raw materials in parts by weight: 147 parts of binder, 29 parts of dispersant, 169.95 parts of filler, 5.1 parts of auxiliary agent, and 1.1 parts of color paste.

[0039] The dispersant is water.

[0040] The adhesive is composed of the following raw materials in parts by weight: 99.75 parts of silicone acrylic emulsion, 31.5 parts of epoxy emulsion, and 15.75 parts of acrylic emulsion.

[0041] The filler is composed of the following raw materials in parts by weight: 46.35 parts of inorganic hollow vitrified microspheres, 30.9 parts of heavy calcium, 30.9 parts of alumina, 46.35 parts of quartz sand, and 15.45 parts of wood fiber.

[0042] The auxiliary agent is composed of the following raw materials in parts by weight: 0.5 part of glycerol, 0.5 part of sodium lauryl sulfate, 1 part of hydroxyethyl cellulose, 1 part of nano titanium dioxide, and 1 par...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses nanometer colorful thermal insulation mortar paint. The nanometer colorful thermal insulation mortar paint is prepared from the following raw materials in parts by weight: 133-147 parts of a binder, 29 parts of a dispersing agent, 160.05-169.95 parts of fillings, 4.9-5.1 parts of an addition agent and 0.9-0.1 part of color paste. The thermal insulation mortar paint disclosed by the invention integrates thermal insulation, flame resistance, sterilization, crack resistance, water resistance, weather resistance and environmental protection; during construction, when the surface of a wall is clean and not greasy, the thermal insulation mortar paint can be used, and putty powder does not need to be used; the thermal insulation mortar paint is scrap coated twice at room temperature, so that the plasticity is high, and the construction is convenient; after the thermal insulation mortar paint is applied, the weight ratio of the thermal insulation mortar paint is only 2 kg / m<2>, and the weight of the thermal insulation mortar paint is lighter than that of conventional mortar, so that building burden is reduced; besides, the thermal insulation mortar paint is bright in color, so that decoration requirements are met.

Description

technical field [0001] The invention relates to a decorative coating, in particular to a nano-color thermal insulation mortar paint. Background technique [0002] Decorate and protect the outer wall of the building, so that the appearance of the building is beautiful and tidy, so as to achieve the purpose of beautifying the urban environment and giving people a refreshing space. At the same time, it can also protect the building wall and prolong its service life. Wall decoration coatings can be roughly divided into exterior wall coatings and interior wall coatings. Function of wall decoration coating: to decorate and protect the exterior wall of buildings, make the appearance of buildings beautiful and tidy, so as to achieve the purpose of beautifying the urban environment and giving people a refreshing space. At the same time, it can also protect the building wall and prolong its service life. Existing decorative coatings have single functions, and with the development o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D133/04C09D163/00C09D133/00C09D7/12
CPCC09D133/04C08K2201/011C08L2201/02C08L2205/035C09D7/61C09D7/63C09D7/70C08L63/00C08L33/00C08L97/02C08L1/284C08K13/04C08K7/28C08K2003/265C08K2003/2227C08K3/36C08K2003/2241C08K5/053
Inventor 肖皖松
Owner 肖皖松
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com