A kind of peelable nail polish and preparation method thereof

A technology for nail polish and curing resin, applied in the field of peelable nail polish and its preparation, can solve the problems that the durability is not as good as oily nail polish and the inconvenient production and use of nail polish, slow drying, etc., and achieves good peelability. , The effect of finishing is convenient, quick and easy to control

Inactive Publication Date: 2018-10-30
SHANGHAI INST OF TECH
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the current peelable nail polish is generally water-based and needs to be used with transparent water or sealant water; the durability is not as good as that of oil-based nail polish, and it dries slowly, and peelable nail polish is generally included in the formula of nail polish The addition of strippable components brings inconvenience to the production and use of nail polish

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of peelable nail polish and preparation method thereof
  • A kind of peelable nail polish and preparation method thereof
  • A kind of peelable nail polish and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A peelable nail polish, calculated in parts by weight, its raw material composition and content are as follows:

[0035]

[0036] Wherein said UV curable resin A is calculated in parts by weight, and its composition and content are as follows:

[0037]

[0038] The UV curable resin A is prepared according to the following steps: 20 parts of methylphenyl hydrogen-containing silicone oil and 10 parts of pentaerythritol triacrylate are added to a 500ml three-necked flask, and then 0.005 parts of polymerization inhibitor p-hydroxyanisole are added , pass in protective gas, stir and heat, raise the temperature to 60°C, add 0.03 parts of catalyst chloroplatinic acid / vinyl double-head complex, stir and keep the temperature for 3 hours, stop heating, and wait until the temperature of the flask drops to room temperature to obtain UV Curing Resin A.

[0039] Described UV curing resin B is a hyperbranched polyester acrylate prepolymer;

[0040] The reactive diluent is a mi...

Embodiment 2

[0053] A peelable nail polish, calculated in parts by weight, its raw material composition and content are as follows:

[0054]

[0055]

[0056] Wherein said UV curable resin A is calculated in parts by weight, and its composition and content are as follows:

[0057]

[0058] The UV curable resin A is prepared according to the following steps: 60 parts of methylphenyl hydrogen-containing silicone oil and 20 parts of pentaerythritol triacrylate are added to a 500ml three-necked flask, and then 0.01 part of polymerization inhibitor hydroquinone is added, Pass in protective gas, stir and heat, raise the temperature to 80°C, add 0.05 parts of catalyst chloroplatinic acid / isopropanol solution, keep stirring for 5 hours, stop heating, and wait until the temperature of the flask drops to room temperature to obtain UV curable resin A.

[0059] Described UV curing resin B is a hyperbranched polyester acrylate prepolymer;

[0060] The reactive diluent is a mixture of diethyle...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
peel strengthaaaaaaaaaa
peel strengthaaaaaaaaaa
peel strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses strippable nail polish gel and a preparation method thereof. The strippable nail polish gel is prepared from by weight, 50-80 parts of UV curing resin A, 50-80 parts of UV curing resin B, 50-80 parts of reactive diluents, 0.05-1 part of leveling agent, 1-10 parts of wetting agent, 0.2-1 part of antifoaming agent, 1-10 parts of UV color paste, 3-5 parts of photoinitiator A and 3-5 parts of photoinitiator B. The strippable nail polish gel has rapid curing capacity after being irradiated through 365 nm UV-LED lamps and can be widely applied to the technical field of nail care of various users.

Description

technical field [0001] The invention belongs to the technical field of polymer materials, and in particular relates to a strippable nail polish and a preparation method thereof. The strippable nail polish is particularly suitable for curing with a 365nm UV-LED light source. Background technique [0002] Women's love for nail art stems from a kind of love. Nail polish is applied to the nails with tools, and cross-linking polymerization occurs after being irradiated by ordinary UV light sources. The resulting cured nail polish is bright in color, crystal clear and full, and endlessly changing. It is the favorite of ladies. Compared with ordinary UV light source curing methods, UV-LED light source has many advantages such as high luminous efficiency, long life, fast response speed, less heat release, energy saving, environmental protection, etc., and has gradually replaced ordinary UV light source. With the enrichment of urban life and the acceleration of the pace of life, lad...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A61K8/895A61Q3/02C08G77/442
CPCA61K8/895A61K2800/544A61Q3/02C08G77/442
Inventor 张英强常文秀李烨
Owner SHANGHAI INST OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com