Fine surface treatment method for sand-contained type bituminous pavement

A kind of asphalt pavement and fine surface technology, which is applied to roads, roads, on-site paved condensate pavements, etc., can solve the problems of decreased anti-skid ability, aging of pavement, cracking, etc., to increase net height, improve adhesion, improve The effect of overall hardness

Inactive Publication Date: 2016-03-23
CHONGQING SINCERE BOND PAVEMENT MATERIALS
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] In order to solve the problems of asphalt pavement, such as the decrease of anti-skid ability, pavement aging, pockmarked surface, looseness, cracking, water seepage, polishing, etc. after many years of use, and prolong the service life of the road, the invention provides a fine surface of sand-containing asphalt pavement Treatment method to quickly restore road functions and beautify roads, and reduce road maintenance costs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] The AC-13 pavement is selected, and the original pavement detection conditions are that the structure depth is 0.5mm, the friction pendulum value is 45BPN, and the water seepage coefficient is 47mL / min.

[0023] Stir the components of the epoxy asphalt bonding material according to the requirements, then add 40% of its weight of fine sand and mix well, and then spray it evenly on the asphalt pavement with a certain pressure during continuous stirring to form waterproof and anti-skid protection layer. The fine sand is quartz sand, the specification of the fine sand is 40-70 mesh, and it is dry and clean. The spraying amount of the epoxy asphalt bonding material is 0.3kg / ㎡.

[0024] Cured at 30°C for 2 hours, according to the detection method specified in JTGE60-2008 roadbed and pavement field test regulations, the construction depth is 0.52mm, the friction pendulum value is 56BPN, and the water permeability coefficient is 0mL / min.

Embodiment 2

[0026] The AC-13 pavement is selected, and the original pavement detection conditions are that the structure depth is 0.5mm, the friction pendulum value is 45BPN, and the water seepage coefficient is 47mL / min.

[0027] Stir the components of the epoxy asphalt bonding material according to the requirements, then add 50% of its weight of fine sand and mix evenly, and then spray it evenly on the asphalt pavement with a certain pressure during continuous stirring to form waterproof and anti-skid protection layer. The fine sand is quartz sand, the specification of the fine sand is 40-70 mesh, and it is dry and clean. The spraying amount of the epoxy asphalt bonding material is 0.4kg / ㎡

[0028] Cured at 30°C for 2 hours, according to the detection method specified in JTGE60-2008 roadbed and pavement field test regulations, the construction depth is 0.54mm, the friction pendulum value is 58BPN, and the water permeability coefficient is 0mL / min.

Embodiment 3

[0030] The AC-13 pavement is selected, and the original pavement detection conditions are that the structure depth is 0.5mm, the friction pendulum value is 45BPN, and the water seepage coefficient is 47mL / min.

[0031] Stir the components of the epoxy asphalt bonding material according to the requirements, then add 60% of its weight of fine sand and mix evenly, and then spray it evenly on the asphalt pavement with a certain pressure during continuous stirring to form waterproof and anti-skid protection layer. The fine sand is quartz sand, the specification of the fine sand is 40-70 mesh, and it is dry and clean. The spraying amount of the epoxy asphalt bonding material is 0.5kg / ㎡

[0032] Cured at 30°C for 2 hours, according to the detection method specified in JTGE60-2008 roadbed and pavement field test regulations, the construction depth is 0.55mm, the friction pendulum value is 62BPN, and the water permeability coefficient is 0mL / min.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a fine surface treatment method for a sand-contained type bituminous pavement and belongs to the related field of bituminous road maintenance and repair. The fine surface treatment method comprises the steps that after all components of epoxy bituminous binding materials are stirred evenly as required, fine sand of a certain proportion is added, and the mixture is stirred evenly; and while continuously stirred, the mixture is evenly sprayed to the bituminous pavement with certain pressure to form a waterproof antiskid protective layer. According to the fine surface treatment method, the old bituminous pavement can be repaired fast, the antiskid capacity of the pavement and the road appearance are improved.

Description

technical field [0001] The invention relates to the related fields of asphalt pavement maintenance and repair, in particular to a fine surface treatment method for sand-containing asphalt pavement. Background technique [0002] As a seamless continuous pavement, asphalt pavement is widely used in high-grade highway construction because of its smooth surface, comfortable driving, wear resistance, low noise, short construction period, and convenient maintenance. [0003] Due to various reasons such as the complexity and variability of asphalt pavement engineering itself, structural design and construction quality control, coupled with factors such as increasing traffic volume, channelization of vehicles, aggravation of overloaded transportation and water damage, asphalt Early damage such as cracks, ruts, loose surfaces, potholes, etc. appear on the road surface (or bridge deck pavement layer) in varying degrees, which seriously reduces the performance of the road surface (or b...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): E01C7/35
CPCE01C7/353
Inventor 吴祥燕刘帮银
Owner CHONGQING SINCERE BOND PAVEMENT MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com