Adhesive for corrugated cardboard and preparation method

A technology of adhesive and corrugated cardboard, which is applied in the field of cardboard manufacturing, can solve the problems of complex glue making process, short storage period, and easy mildew, and achieve the effect of simple preparation process, fast bonding speed, and no mildew

Inactive Publication Date: 2016-03-16
NANJING ZHONGHEHENG IND EQUIP TECH DEV
View PDF0 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Existing adhesives for corrugated paper have disadvantages such as weak adhesion, easy mildew, short storage period and complicated glue making process, which cannot meet the current production needs of corrugated paperboard

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] Adhesive for corrugated cardboard of the present invention is made up of following weight percentage composition:

[0016] Sweet potato starch 35%, epoxy resin 2%, toughening agent 0.3%, sodium hydroxide solution 0.6%, carboxymethyl cellulose 0.6%, preservative 0.8%, ferrous ammonium sulfate 0.02%, and the balance is water.

[0017] making process:

[0018] 1), add sweet potato starch, epoxy resin hydrogen, sodium oxide solution, carboxymethyl cellulose, ferrous ammonium sulfate and water to the reactor and fully mix and stir;

[0019] 2) Gradually raise the temperature to 75°C, add toughening agent and preservative in turn after gelatinization, and mix and stir for 10-15 minutes;

[0020] 3), obtain adhesive after natural cooling.

Embodiment 2

[0022] Adhesive for corrugated cardboard of the present invention is made up of following weight percentage composition:

[0023] Tapioca starch 40%, epoxy resin 1%, toughening agent 0.1%, sodium hydroxide solution 0.4%, carboxymethyl cellulose 0.8%, preservative 0.5%, ferrous ammonium sulfate 0.01%, and the balance is water.

[0024] making process:

[0025] 1), add tapioca starch, epoxy resin hydrogen, sodium oxide solution, carboxymethyl cellulose, ferrous ammonium sulfate and water to the reactor and fully mix and stir;

[0026] 2) Gradually raise the temperature to 80°C, add toughening agent and preservative in turn after gelatinization, and mix and stir for 10-15 minutes;

[0027] 3), obtain adhesive after natural cooling.

Embodiment 3

[0029] Adhesive for corrugated cardboard of the present invention is made up of following weight percentage composition:

[0030] 30% mixture of magic yu starch and corn starch, 1.5% epoxy resin, 0.5% toughening agent, 0.5% sodium hydroxide solution, 0.5% carboxymethyl cellulose, 0.7% preservative, 0.01% ferrous ammonium sulfate, other The amount is water.

[0031] making process:

[0032] 1), add magic yu starch and cornstarch mixture, epoxy resin hydrogen, sodium oxide solution, carboxymethyl cellulose, ferrous ammonium sulfate and water to the reaction kettle and carry out thorough mixing and stirring;

[0033] 2) Gradually raise the temperature to 76°C, add toughening agent and preservative in turn after gelatinization, and mix and stir for 10-15 minutes;

[0034] 3), obtain adhesive after natural cooling.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an adhesive for a corrugated cardboard and a preparation method, and belongs to the technical field of cardboard manufacturing. The adhesive for the corrugated cardboard comprises, by weight: 30-40% of plant starch, 1-2% of an epoxy resin, 0.1-0.5% of a toughening agent, 0.4-0.8% of a sodium hydroxide solution, 0.5-0.8% of carboxymethyl cellulose, 0.5-1% of an antiseptic, and 0.01-0.02% of ammonium ferrous sulfate, with the balance being water. The adhesive for the corrugated cardboard has advantages of high bonding speed, firm bonding, quick drying, gelation simplicity, and easy and uniform application. The adhesive is simple to prepare and convenient to use; the manufacturing efficiency is high; and the cost is low. The adhesive does not precipitate and mould, and is stable in quality and long in service life. The firmness of the prepared corrugated cardboard can reach 5-6 kg / cm. The invention also discloses a preparation method of the adhesive for the corrugated cardboard.

Description

technical field [0001] The invention relates to a cardboard adhesive and a preparation method, in particular to an adhesive for corrugated cardboard and a preparation method, and belongs to the technical field of cardboard manufacturing. Background technique [0002] During the production process of corrugated cardboard, each layer needs to be bonded together with an adhesive, and its bonding strength is an important indicator for testing the physical properties of corrugated cardboard. In the existing technology, the adhesive used for tiles is generally starch glue. Starch glue is widely used in the corrugated paper industry at home and abroad for its advantages of low price, simple glue making process, fast drying speed, and adaptability to the production requirements of the Soviet Union. . Existing adhesives for corrugated paper have disadvantages such as weak adhesion, easy mildew, short storage period and complicated glue making process, which cannot meet the current p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J103/02C09J11/04
Inventor 于培勇张勇
Owner NANJING ZHONGHEHENG IND EQUIP TECH DEV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com