Al-Ca-Ba infrared glass provided with protective film and preparation method of Al-Ca-Ba infrared glass

A technology of infrared glass and protective film, applied in the field of aluminum calcium barium infrared glass with protective film and its preparation, can solve problems such as insufficient film base adhesion, large difference in expansion coefficient, etc., achieve simple structure and improve protective performance , easy-to-prepare effects

Active Publication Date: 2016-01-27
CHINA BUILDING MATERIALS ACAD
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But SiO 2 Compared with aluminum-calcium-barium infrared glass, there is a large difference in expansion coefficient, and the film base adhesion is not high enough.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0028] The preparation method of aluminum-calcium-barium infrared glass with a protective film is to ultrasonically clean the infrared glass substrate with acetone and ethanol for 15 minutes, put it into the substrate holder, and vacuumize to 2.0×10 -3 Pa, heated to 300°C, and held for 1 hour; Hall ion source was used to clean the Al-Ca-Barium infrared glass substrate before plating. Prepare the aluminum oxide layer by magnetron sputtering Al target, pass Ar into the vacuum chamber, keep the vacuum degree of the chamber at 0.5 Pa, start the glow, carry out backsputter cleaning on the Al target for 15 minutes; pass O 2 , where Ar / O 2 The ratio is 1:1.5, the indoor vacuum is 1Pa, and the thickness of the obtained alumina layer is 400nm; the silicon dioxide layer is prepared by radio frequency magnetron sputtering Si target, and Ar is introduced into the vacuum chamber to keep the indoor vacuum at 0.5Pa. , Qihui, backsplash cleaning the Si target, the time is 15 minutes. Access...

example 2

[0031] The preparation method of aluminum-calcium-barium infrared glass with a protective film is to ultrasonically clean the infrared glass substrate with acetone and ethanol for 15 minutes, put it into the substrate holder, and vacuumize to 3.0×10 -3 Pa, heated to 250°C, and kept warm for 1.5h; Hall ion source was used to clean the aluminum-calcium-barium infrared glass substrate before plating. Prepare the aluminum oxide layer by radio frequency magnetron sputtering Al target, pass Ar into the vacuum chamber, keep the vacuum degree of the chamber at 0.5 Pa, start the glow, carry out backsputter cleaning on the Al target for 18 minutes; pass O 2 , where Ar / O 2 The ratio is 1:1, the indoor vacuum is 2Pa, and the thickness of the obtained aluminum oxide layer is 650nm; the silicon dioxide layer is prepared by radio frequency magnetron sputtering Si target, and Ar is introduced into the vacuum chamber to keep the indoor vacuum at 1Pa. Start-up, carry out back-splash cleaning o...

example 3

[0034] The preparation method of aluminum-calcium-barium infrared glass with a protective film is to ultrasonically clean the infrared glass substrate with acetone and ethanol for 15 minutes, put it into the substrate holder, and vacuumize to 3.0×10 -3 Pa, heated to 280°C, and kept warm for 1.5h; Hall ion source was used to clean the aluminum-calcium-barium infrared glass substrate before plating. Prepare the aluminum oxide layer by radio frequency magnetron sputtering Al target, pass Ar into the vacuum chamber, keep the vacuum degree of the chamber at 1.5Pa, start the glow, carry out backsputter cleaning on the Al target for 20 minutes; pass O 2 , where Ar / O 2 The ratio is 1:2.5, the indoor vacuum is 5Pa, and the thickness of the obtained aluminum oxide layer is 800nm; the silicon dioxide layer is prepared by radio frequency magnetron sputtering Si target, and Ar is introduced into the vacuum chamber to keep the indoor vacuum at 1Pa. Start-up, carry out back-splash cleaning ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention relates to Al-Ca-Ba infrared glass provided with a protective film and a preparation method of the Al-Ca-Ba infrared glass. The Al-Ca-Ba infrared glass comprises an Al-Ca-Ba infrared glass base layer, an Al2O3 layer deposited in the Al-Ca-Ba infrared glass base layer and a SiO2 layer deposited in the Al2O3 layer. The Al-Ca-Ba infrared glass provided with the protective film is easy to prepare and simple in structure, the attachment performance is improved, and the protective performance of the Al-Ca-Ba infrared glass is enhanced.

Description

technical field [0001] The invention relates to an aluminum-calcium-barium infrared glass and a preparation method thereof, in particular to an aluminum-calcium-barium infrared glass with a protective film and a preparation method thereof. Background technique [0002] Aluminum-calcium-barium glass is an infrared material based on the Al-Ca-Ba system. It has infrared transmission properties similar to sapphire, and has the advantages of wide transmission range and excellent physical and chemical properties. It can be used as an infrared transmission window. Wave infrared photoelectric detection, guidance and other fields are widely used. [0003] As a window material for photoelectric detection, Al-Ca-Barium infrared glass is directly exposed to the atmosphere, while Al-Ca-Barium infrared glass is easily polluted by environmental impurities and moisture, which seriously affects the infrared transmission performance of the glass. In addition, the hardness of the material its...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C03C17/34
Inventor 金扬利祖成奎韩滨赵华赵慧峰刘永华王衍行陈江何坤
Owner CHINA BUILDING MATERIALS ACAD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap