Control method for surface oxidation pocking defects of hot-rolled pickled plate

A technology of hot-rolled pickling and surface oxidation, applied in the direction of contour control, etc., can solve problems such as oxidation pitting defects, achieve the effects of reducing the probability of occurrence, improving quality, and solving uniformity problems

Active Publication Date: 2016-01-20
SHOUGANG CORPORATION +1
View PDF5 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The embodiments of the present invention provide a method for controlling oxidation pitting defects on the surface of hot-rolled pickling sheets, which solves the problem of oxidation pitting defects in hot-rolled pickling sheets with a thickness of ≤2 mm and a tensile strength of ≥500 MPa in the prior art. Technical problems, reduced the probability of occurrence of oxidation pitting defects on hot-rolled pickled plates, and improved the quality of finished products of hot-rolled pickled plates

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Control method for surface oxidation pocking defects of hot-rolled pickled plate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] This embodiment provides a method for controlling oxidation pitting defects on the surface of a hot-rolled pickled plate, the thickness of the hot-rolled pickled plate is ≤2 mm, and the tensile strength is ≥500 MPa. The manufacturing process of the hot-rolled pickled plate is steel billet Heating, rough rolling, descaling, finish rolling and pickling. The method includes:

[0029] The chemical composition of the steel slab is controlled to contain Si: 0.06%, P: 0.008% in terms of mass percentage, and the rest is Mn, Nb, Ti and Fe matrix. Put the steel billet with a thickness of 200mm into the heating furnace for heating for 160min, control the temperature of the billet out of the furnace to 1200°C, and conduct rough rolling and high-pressure descaling water descaling treatment on the billet out of the furnace. 5 passes of rough rolling process, 3 passes of high-pressure descaling water descaling, for example, 1, 3 and 5 passes can be opened for high-pressure descaling ...

Embodiment 2

[0031] This embodiment provides a method for controlling oxidation pitting defects on the surface of a hot-rolled pickled plate, the thickness of the hot-rolled pickled plate is ≤2 mm, and the tensile strength is ≥500 MPa. The manufacturing process of the hot-rolled pickled plate is steel billet Heating, rough rolling, descaling, finish rolling and pickling. The method includes:

[0032] The chemical composition of the steel slab is controlled to contain Si: 0.1%, P: 0.006% in terms of mass percentage, and the rest is Mn, Nb, Ti and Fe matrix. Put the steel billet with a thickness of 200mm into the heating furnace for heating for 160min, control the temperature of the billet out of the furnace to 1200°C, and conduct rough rolling and high-pressure descaling water descaling treatment on the billet out of the furnace. 5 passes of rough rolling process, 3 passes of high-pressure descaling water descaling, for example, 1, 3 and 5 passes can be opened for high-pressure descaling w...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of hot rolling, in particular to a control method for surface oxidation pocking defects of a hot-rolled pickled plate. The control method includes the steps that the chemical components of a steel billet are controlled to include, by mass, 0.05-0.15% of Si, at most 0.01% of P and the balance Mn, Nb, Ti and a Fe substrate. In the heating process of the steel billet, the steel billet with the thickness being 135-250 mm is put into a heating furnace and heated for 160-200 min, and the tapping temperature of the steel billet is controlled to be 1180-1240 DEG C. The thickness of an intermediate billet is controlled to be 26-34 mm after a descaling process. In the precision rolling process, the precision rolling inlet temperature is controlled to be 980-1020 DEG C, and the finish rolling temperature is controlled to be 850-890 DEG C. The control method for surface oxidation pocking defects of the hot-rolled pickled plate can effectively restrain the occurrence of surface oxidation pocking defects of the hot-rolled pickled plate with the thickness being at most 2 mm and the tensile strength being at least 500 MPa.

Description

technical field [0001] The invention relates to the technical field of hot rolling, in particular to a method for controlling oxidation pit defects on the surface of a hot-rolled pickled plate. Background technique [0002] Hot-rolled pickled sheet is an intermediate product between cold-rolled and hot-rolled. It has a surface quality close to that of cold-rolled sheet while maintaining the mechanical properties of hot-rolled products. It has a wide range of applications. Hot-rolled pickled sheet has a good market prospect due to its high cost performance and economic benefits. [0003] The automotive structural steel used in the processing industry represented by the automotive industry is developing towards a trend of high strength and thin gauge. The demand for hot-rolled pickling plates with a thickness of ≤2mm and a tensile strength of ≥500MPa is increasing. This series of products has the characteristics of thin specifications and high strength. The surface of the pro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B21B37/32B21B37/28
CPCB21B37/28B21B37/32
Inventor 郭子峰于洋冯军陈斌王林周娜王畅吴科敏李玉鹏李文远惠亚军吕宝锋王学强陈波宋春华
Owner SHOUGANG CORPORATION
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com