Goodyear type foaming rubber material

A technology of styrofoam and Goodyear, which is applied in the field of Goodyear-type styrofoam, can solve the problems of plasticizing, poor toughness, labor and material resources, etc., to increase the mechanical intertwining force, improve the reinforcing effect, The effect of improving the adhesive strength

Inactive Publication Date: 2015-12-30
JIHUA 3515 LEATHER & SHOES
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the use of natural rubber, plastication is required, which consumes manpower and material resources and increases costs
On the other hand, it is difficult to control the acidity and alkalinity of the mixed rubber during the preparation process with carbon black for rubber reinforcement, and it is difficult to meet the requirements of the subsequent vulcanization process.
In order to increase the softness of rubber shoes, a foaming agent is often added to the rubber material, and then the foam holes generated by the use of the foaming agent affect the wear resistance of the shoe, and at the same time make the foam rubber have low tear strength and poor toughness. The degree of adhesion between the foamed compound and the upper surface is reduced

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A Goodyear-type foaming compound prepared from the following two parts of raw materials: the first part is prepared from the following raw materials in parts by weight: styrene-butadiene rubber 21.74-23.02, natural rubber 31.50-33.67, zinc oxide 2.50-2.85 , octadecanoic acid 1.08-1.13, magnesium oxide 0.51-0.56, N-isopropyl-N'-phenyl-p-phenylenediamine 0.51-0.56, 2,2,4-trimethyl-1,2-dihydrogenation Quinoline 0.70-0.77, reinforcing agent 28.16-30.69, coumarone resin 1.53-1.68, short fiber 1.62-1.95, foaming agent 2.00-2.15; Sulfur 6-7g, accelerator dibenzothiazole disulfide 0.5-1.5g, accelerator CZ7.5-8g, accelerator TMTD2-3g.

[0017] Through physical testing, the Goodyear-type foamed rubber product obtained in this example has a hardness of 46 Shore A, a tear strength of 7.5 MPa, and an adhesive strength of 5.3 N / mm.

Embodiment 2

[0019] A Goodyear-type foaming compound prepared from the following two parts of raw materials: the first part is prepared from the following raw materials in parts by weight: styrene-butadiene rubber 22.6, natural rubber 32.0, zinc oxide 2.7, octadecanoic acid 1.12 , magnesium oxide 0.55, N-isopropyl-N'-phenyl-p-phenylenediamine 0.54, 2,2,4-trimethyl-1,2-dihydroquinoline 0.73, carbon black N33929.52, Guma Long resin 1.62, short fiber 1.75, foaming agent 2.08; the second part is the amount added on the basis of the first part per kilogram, which is sulfur 6g, accelerator dibenzothiazole disulfide 1g, accelerator CZ8g, accelerator TMTD2g .

Embodiment 3

[0021] A Goodyear-type foaming compound prepared from the following two parts of raw materials: the first part is prepared from the following raw materials in parts by weight: styrene-butadiene rubber 21.74, natural rubber 33.67, zinc oxide 2.50, octadecanoic acid 1.13 , magnesium oxide 0.51, N-isopropyl-N'-phenyl-p-phenylenediamine 0.56, 2,2,4-trimethyl-1,2-dihydroquinoline 0.70, carbon black N33930.69, Guma Long resin 1.53, short fiber 1.95, foaming agent 2.00; the second part is the addition amount per kilogram of the first part, which is sulfur 7g, accelerator dibenzothiazole disulfide 0.5g, accelerator CZ8g, accelerator TMTD2g.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Shore hardnessaaaaaaaaaa
hardnessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a Goodyear type foaming rubber material, which is prepared from a first part and a second part, wherein the first part is prepared from the following raw materials: styrene-butadiene rubber, natural rubber, zinc oxide, octadecanoic acid, N-isopropyl-N'-phenyl p-phenylenediamine, 2,2,4-trimethyl-1,2-dihexahydro quinoline, a reinforcing agent, coumarone resin, short fibers and a foaming agent; the second part comprises sulfur, accelerant dibenzothiazyl disulfide, accelerant CZ and accelerant TMTD added on the basis of the first part. The foamed sole prepared from the rubber material has the advantages of being soft, good in elasticity, good in wear resistance, small in specific gravity and the like, and the foaming rubber material has high sticking degree with the upper.

Description

technical field [0001] The invention belongs to the technical field of foaming outsoles, and in particular relates to a Goodyear foaming rubber material. Background technique [0002] At present, most of the various shoe soles are made of natural rubber as the raw material. After masticating and mixing with other ingredients to make rubber shoe soles, the cost is relatively controllable, and the hardness and other properties can be adjusted according to needs. Basically, People's requests have been met. Since what is used is natural rubber, plastication is required, which consumes manpower and material resources and increases the cost. On the other hand, it is difficult to control the acidity and alkalinity of the mixed rubber during the preparation process with carbon black for rubber reinforcement, and it is difficult to meet the subsequent vulcanization process. In order to increase the softness of rubber shoes, a foaming agent is often added to the rubber material, and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L7/00C08L9/06C08L45/02C08K13/04C08K7/02C08K3/22C08K5/09C08K5/18C08K3/06C08K5/47C08J9/04A43B13/04
Inventor 肖慧
Owner JIHUA 3515 LEATHER & SHOES
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com