A kind of activated carbon fiber composite material and its preparation method and a kind of activated carbon fiber composite filter element

A technology of activated carbon fibers and composite materials, applied in chemical instruments and methods, multi-stage water/sewage treatment, water/sludge/sewage treatment, etc. It is not resistant to high temperature and other problems, and achieves the effect of overcoming poor strength, large adsorption capacity and uniform microporous structure.

Inactive Publication Date: 2018-02-13
GUANGDONG ZHENGYE TECH
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, the prepared filter element has poor adsorption and filtration effect, and most of the filter element structures listed above are not resistant to high temperature, and have poor acid and alkali resistance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of activated carbon fiber composite material and its preparation method and a kind of activated carbon fiber composite filter element
  • A kind of activated carbon fiber composite material and its preparation method and a kind of activated carbon fiber composite filter element
  • A kind of activated carbon fiber composite material and its preparation method and a kind of activated carbon fiber composite filter element

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0048] The present invention also provides a kind of preparation method of activated carbon fiber composite material, comprises the following steps:

[0049] After weighing activated carbon fiber chopped strands and / or activated carbon fiber powder, powdered activated carbon, short fibers, modified cellulose and auxiliary agents to obtain a mixed raw material, the mixed raw material is mixed with water evenly, and is prepared on a paper machine at one time. The net is shaped to form an activated carbon fiber composite material.

[0050] The present invention first weighs the activated carbon fiber chopped strands and / or activated carbon fiber powder, powdered activated carbon, short fiber, modified cellulose and auxiliary agents to obtain the mixed raw material, and then mixes the mixed raw material with water to obtain the mixed slurry material. Wherein, the mass ratio of the mixed raw material to water is preferably 1: (10-20), and in some specific embodiments of the presen...

Embodiment 1

[0073] 1. Raw material formula of activated carbon fiber composite material:

[0074] 20wt% activated carbon fiber, purchased from Ningxia Baoda Carbon Fiber Co., Ltd., iodine value 1500mg / g;

[0075] 30wt% coconut shell activated carbon with an iodine value of 800mg / g;

[0076] 35wt% wood pulp;

[0077] 10wt% carboxymethyl cellulose;

[0078] 5 wt% polyamide epichlorohydrin.

[0079] 2. Weigh the above materials according to the weight ratio, mix them with water at a ratio of 1:20, and form a net on a paper machine to obtain an activated carbon fiber composite material.

[0080] 3. Cut the activated carbon fiber composite material into a width of 254mm with a circular knife slitting machine, and then cut it into a length of 1200mm, and wind it on a 254mm long hollow cylindrical plastic skeleton covered with polypropylene microfiber cloth. The ethylene protective net and the upper and lower end caps are fixed to make a 10-inch activated carbon fiber composite filter element....

Embodiment 2

[0082] 1. Raw material formula of activated carbon fiber composite material:

[0083] 30wt% activated carbon fiber, purchased from Ningxia Baoda Carbon Fiber Co., Ltd., with an iodine value of 1500mg / g;

[0084] 20wt% coconut shell activated carbon with an iodine value of 800mg / g;

[0085] 35wt% wood pulp;

[0086] 10wt% carboxymethyl cellulose;

[0087] 5 wt% polyamide epichlorohydrin.

[0088] 2. Weigh the above materials according to the weight ratio, mix them with water at a ratio of 1:20, and form a net on a paper machine to obtain an activated carbon fiber composite material.

[0089] 3. Cut the activated carbon fiber composite material into a width of 254mm with a circular knife slitting machine, and then cut it into a length of 1200mm, and wind it on a 254mm long hollow cylindrical plastic skeleton covered with polypropylene microfiber cloth. The ethylene protective net and the upper and lower end caps are fixed to make a 10-inch activated carbon fiber composite fi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
sizeaaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention is made of activated carbon fiber, short fiber, powdered activated carbon, modified cellulose and processing aids, etc. to make activated carbon fiber composite material, as the adsorption material of high-efficiency activated carbon filter element, overcomes the disadvantages of poor strength of activated carbon fiber felt and easy shedding The problem is that the rich and uniform microporous structure of activated carbon fibers is retained, and there are a large number of mesopores (ie, mesopores) of high-quality powdered and granular activated carbons, so the adsorption capacity is large, and the range of applicable organic matter is wide, and the material is prepared. The filter element is resistant to high temperature, acid and alkali, and can be widely used in the electroplating production line of the PCB industry.

Description

technical field [0001] The invention belongs to the technical field of activated carbon filter elements, and in particular relates to an activated carbon fiber composite material, a preparation method thereof and an activated carbon fiber composite filter element. Background technique [0002] In the electroplating industry, in order to make the coating bright and dense, additives are generally added. Among them, the most important brightener, as an organic substance, inevitably has phenomena such as decomposition. After its decomposition, in addition to the decrease in the brightness of the coating, it may also cause disadvantages such as loose coating. In the past, regular carbon treatment was usually carried out on the plating solution, but carbon treatment will bring certain problems, such as loss of plating solution, difficulty in sedimentation of carbon powder, and subsequent filtration, etc., which increases the difficulty of operation and labor costs. [0003] The u...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C02F9/02
Inventor 徐地华徐地明苏华弟曹四峰吴国芳梅领亮
Owner GUANGDONG ZHENGYE TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com