Eureka AIR delivers breakthrough ideas for toughest innovation challenges, trusted by R&D personnel around the world.

A kind of high-speed printing flexographic water-based ink and preparation method thereof

A water-based ink, high-speed printing technology, applied in ink, household utensils, applications, etc., can solve the problems of being unable to adapt to high-speed flexographic printing, and achieve excellent leveling and overprinting effects, high color saturation, and good fluidity

Active Publication Date: 2017-10-24
山东布瑞特油墨有限公司
View PDF1 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The invention provides a flexographic water-based ink for high-speed printing and a preparation method thereof, which is used to solve technical defects such as the inability of the water-based ink in the prior art to adapt to high-speed flexographic printing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of high-speed printing flexographic water-based ink and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] The flexographic water-based ink of the high-speed printing of the present embodiment is made up of the following components by weight: 32.9 parts of acrylic acid film-forming emulsion, 5 parts of acrylic acid film-forming emulsion, 15 parts of acrylic resin solution A, 39 parts of water-based color paste, poly 1.5 parts of ethylene wax, 1 part of film-forming aid, 0.3 part of leveling agent, 0.1 part of defoamer, 0.2 part of pH regulator and 5 parts of deionized water.

[0030] Among the above-mentioned flexographic water-based inks:

[0031] Acrylic non-film-forming emulsion uses acrylic emulsion Basf Joncryl 89, its solid content is 48%, Tg value is 98°C, acid value is 50mgKOH / g, pH value is 8.3; acrylic film-forming emulsion uses acrylic emulsion Basf Joncryl 77, its solid content The content is 46%, the Tg value is 21°C, the acid value is 55mgKOH / g, and the pH value is 8.3; the polyethylene wax is specifically polyethylene wax MD-2000; the film-forming aid is speci...

Embodiment 2

[0043] The flexographic water-based ink of the high-speed printing of the present embodiment is made up of the following components by weight: 34.7 parts of acrylic acid film-forming emulsions, 5 parts of acrylic acid film-forming emulsions, 18 parts of acrylic resin solution A, 35 parts of water-based colorants, poly 1 part of ethylene wax, 1.5 parts of film-forming aid, 0.5 part of leveling agent, 0.1 part of defoamer, 0.2 part of pH regulator and 4 parts of deionized water; except for water-based color paste, other components are the same as in Example 1 .

[0044] The water-based color paste consists of the following components by weight: 45 parts of yellow pigment (PY14), 26 parts of acrylic resin solution B, 28.4 parts of deionized water, 1.5 parts of wetting and dispersing agent (TEGO dispersers 760) and defoamer BYK0930. 1 part; wherein: acrylic resin solution B is the same as in Example 1.

[0045] Above-mentioned flexographic water-based ink can be prepared by the f...

Embodiment 3

[0051] The flexographic water-based ink of the high-speed printing of the present embodiment is made up of the component of following parts by weight: 35 parts of acrylic acid film-forming emulsions, 6 parts of acrylic acid film-forming emulsions, 17 parts of acrylic resin solution A, 35 parts of water-based colorants, poly 1 part of ethylene wax, 1 part of film-forming aid, 0.5 part of leveling agent, 0.1 part of defoamer, 0.2 part of pH regulator and 4.2 parts of deionized water.

[0052] Among the above-mentioned flexographic water-based inks:

[0053] Acrylic non-film-forming emulsion uses acrylic emulsion Indulor SE900; acrylic film-forming emulsion uses acrylic emulsion Indulor SE 2872; polyethylene wax is specifically polyethylene wax AQUAACER552; film-forming aid is specifically butyl carbitol; leveling agent is specifically SURFYNOL 420; the defoamer is specifically TEGO 1488; the pH regulator is specifically AMP-95; all of them are commercially available.

[0054] A...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
glass transition temperatureaaaaaaaaaa
acid valueaaaaaaaaaa
glass transition temperatureaaaaaaaaaa
Login to View More

Abstract

The invention provides a high-speed printing flexographic water-based ink and a preparation method thereof. The flexographic water-based ink of the present invention comprises the following components by weight: 30-40 parts of acrylic non-film-forming emulsion, 5-10 parts of acrylic film-forming emulsion, 15-20 parts of acrylic resin solution, 30-40 parts of water-based color paste, 1-3 parts of polyethylene wax, 1-2 parts of film-forming aid, 0.3-1 part of leveling agent, 0.1-0.5 part of defoamer, 3-7 parts of deionized water and pH regulator; among them, acrylic acid is not The film emulsion is an acrylic emulsion with a Tg value ≥ 90°C, the acrylic film-forming emulsion is an acrylic emulsion with a Tg value < 30°C, the mass content of the pigment in the water-based color paste is 40-45%, and the pH regulator makes the pH of the flexographic water-based ink The value is 8 to 9.5. The water-based ink can be well adapted to the printing of high-speed satellite printing machines, and has good resolubility and excellent leveling and overprinting effects. The printed products have high color saturation, bright colors, good gloss, and a wide range of applications.

Description

technical field [0001] The invention relates to a water-based ink, in particular to a high-speed printing flexographic water-based ink and a preparation method thereof. Background technique [0002] Flexographic printing, referred to as flexographic printing, is a printing method that uses a flexographic plate and transfers ink through an anilox roller. Traditional flexographic printing uses a rubber letterpress, which cannot print high-quality images. It was not until DuPont of the United States developed a UV-cured resin plate that high-precision printing was achieved. In recent years, in the packaging industry, with the development of technologies such as plate materials, plate making, anilox rollers, and printing plate cylinder sleeve methods, flexographic printing has become the fastest growing and most expensive printing industry in the world. Vibrant typography. [0003] With the increasing safety requirements of product packaging and the increasing emphasis on envi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D11/107C09D11/03
Inventor 肖俊涛崔鸿雁
Owner 山东布瑞特油墨有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com