Material of cylinder body of pneumatic actuating mechanism and preparation method thereof

A technology for pneumatic actuators and cylinders, which is applied in the field of cylinder materials for pneumatic actuators and its preparation, can solve the problems of core material cylinders not meeting the requirements, poor sealing effect, short life, etc., and achieve transmission efficiency and The effect of high execution accuracy, good mechanical properties, and excellent hardness properties

Active Publication Date: 2015-10-14
WUXI CHENGTIANNUO ACTUATOR MFG CO LTD
View PDF6 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the pneumatic actuators used in the market still have problems such as material hardness, wear resistance, and poor corrosion resistance. The fit is not tight enough, the sealing effect is poor, the operation is not stable, the execution accuracy is low, and the temperature difference range of the applicable temperature is small. Problems such as short life and high operating costs have seriously affected the economic benefits of the enterprise.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Material of cylinder body of pneumatic actuating mechanism and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A cylinder material for a pneumatic actuator according to the present invention, its distribution ratio of each component in parts by weight is: Fe: 0.5%, Cu: 2%, Mg: 0.6%, Mn: 0.18%, Ni: 1.2%, Zn: 2%, B 2 o 3 : 0.4%, SiO 2 : 2.2%, TiC: 1.5%, and the rest is Al.

[0017] A method for preparing a cylinder body for a pneumatic actuator, comprising the following steps,

[0018] (1) Embryo making: Mix the prepared raw materials of each component and put them into the melting furnace, heat up to melt, and after the raw materials are completely melted, adjust the internal temperature of the melting furnace to 750°C for refining treatment, and then melt the Adjust the temperature inside the furnace to 720°C, carry out refining treatment, and finally cool slowly to obtain a Φ200mm cylindrical aluminum alloy billet;

[0019] (2) Billet pretreatment: clean the aluminum alloy billet and remove surface impurities such as oil stains, then heat the aluminum alloy billet to 560°C ...

Embodiment 2

[0024] A cylinder material for a pneumatic actuator according to the present invention, its distribution ratio of each component in parts by weight is: Fe: 0.55%, Cu: 1.6%, Mg: 0.8%, Mn: 0.17%, Ni: 1.5%, Zn: 2%, B 2 o 3 : 0.5%, SiO 2 : 1.8%, TiC: 2%, and the rest is Al.

[0025] A method for preparing a cylinder body for a pneumatic actuator, comprising the following steps,

[0026] (1) Embryo making: Mix the prepared raw materials of each component and put them into the melting furnace, heat up to melt, and after the raw materials are completely melted, adjust the internal temperature of the melting furnace to 755°C for refining treatment, and then melt the Adjust the temperature inside the furnace to 730°C, carry out refining treatment, and finally cool slowly to obtain a Φ400mm cylindrical aluminum alloy billet;

[0027] (2) Billet pretreatment: After cleaning the aluminum alloy billet and removing surface impurities such as oil stains, heat the aluminum alloy billet to...

Embodiment 3

[0032] A cylinder material for a pneumatic actuator according to the present invention, its distribution ratio of each component in parts by weight is: Fe: 0.6%, Cu: 2.2%, Mg: 0.9%, Mn: 0.16%, Ni: 1.6%, Zn: 1.8%, B 2 o 3 : 0.55%, SiO 2 : 1.6%, TiC: 2.2%, and the rest is Al.

[0033] A method for preparing a cylinder body for a pneumatic actuator, comprising the following steps,

[0034] (1) Embryo making: Mix the prepared raw materials of each component and add them to the melting furnace, heat up to melt, and after the raw materials are completely melted, adjust the internal temperature of the melting furnace to 760°C for refining treatment, and then melt the Adjust the temperature inside the furnace to 740°C for refining treatment, and finally cool slowly to obtain a Φ600mm cylindrical aluminum alloy billet;

[0035] (2) Billet pretreatment: After cleaning the aluminum alloy billet and removing surface impurities such as oil stains, heat the aluminum alloy billet to 580°...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a material of the cylinder body of a pneumatic actuating mechanism and a preparation method thereof. The material is composed of the following components in percentage by weight: 0.4 to 0.7% of Fe, 1 to 2.5% of Cu, 0.6 to 1.0% of Mg, 0.15 to 0.2% of Mn, 1 to 2% of Ni, 1.5 to 2.5% of Zn, 0.4 to 0.6% of B2O3, 1.5 to 2.5% of SiO2, 1 to 3% of TiC, and the balance being Al. The cylinder body is prepared by the following steps of blank preparation, blank pretreatment, mould pretreatment, forging and stamping, and moulding. The prepared cylinder body has the characteristics of high hardness, good corrosion resistant performance, little thermal expansion coefficient, low friction index, and high wear resistant performance. At the same time, the manufacture technology is improved to enable the cylinder body to have a good mechanical performance.

Description

technical field [0001] The invention relates to a cylinder body material and a preparation method thereof, in particular to a cylinder body material for a pneumatic actuator used in thermoelectric, petroleum, chemical and other industries and a preparation method thereof. Background technique [0002] Pneumatic actuator is an actuator that drives the opening and closing or regulating valve through air pressure. It is widely used in thermal power, chemical industry, petroleum and other industries with high safety requirements, so its quality requirements are very high. At present, the pneumatic actuators used in the market still have problems such as material hardness, wear resistance, and poor corrosion resistance. The fit is not tight enough, the sealing effect is poor, the operation is not stable, the execution accuracy is low, and the temperature difference range of the applicable temperature is small. Problems such as short life and high operating costs have seriously a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C21/00C22C21/18C22C21/10C22C32/00C22F1/04C22F1/053C22F1/057
Inventor 徐晶张莹
Owner WUXI CHENGTIANNUO ACTUATOR MFG CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com