Bare steel rust layer transforming agent for salt-contained environment

A rust layer conversion agent and bare steel technology, which is applied in the coating process of metal materials, etc., to achieve the effect of excellent anti-rust liquid sag performance and excellent anti-corrosion performance

Inactive Publication Date: 2015-09-23
武汉钢铁有限公司
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide a bare steel rust layer conversion agent for saline environment, which can effectively solve the problems of stabilization of bare steel rust layer and rust liquid hanging in saline environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Bare steel rust layer transforming agent for salt-contained environment

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] A bare steel rust conversion agent used in saline environment, its components by weight percent, titanium oxysulfate accounted for 0.1%, zinc dihydrogen phosphate accounted for 5%, sodium pyrophosphate accounted for 0.1%, tannic acid accounted for 2%, copper sulfate 0.1%, water 92.7%.

Embodiment 2

[0014] A bare steel rust conversion agent used in saline environment, its components by weight percent, titanium oxysulfate accounted for 3%, zinc dihydrogen phosphate accounted for 0.5%, sodium pyrophosphate accounted for 3%, tannic acid accounted for 0.1%, copper sulfate 3%, water 90.4%.

Embodiment 3

[0016] A bare steel rust conversion agent used in saline environment, its components by weight percentage, titanium oxysulfate accounted for 1%, zinc dihydrogen phosphate accounted for 1.5%, sodium pyrophosphate accounted for 2.5%, tannic acid accounted for 0.5%, copper sulfate 2%, water 92.5%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a bare steel rust layer transforming agent for a salt-contained environment. The rust laser transforming agent comprises the following components in percentage by weight: 0.1-3% of titanyl sulfate, 0.5-5% of zinc dihydrogen phosphate, 0.1-3% of sodium pyrophosphate, 0.1-2% of tannic acid, 0.1-3% of copper sulfate, and the balance of water. The rust layer transforming agent has excellent rust liquid sagging prevention; after the rust layer transforming agent is sprayed on the surface of a weather-resistant steel bare sample with removed scales, the formation of a stable rust layer is accelerated; the rust layer is excellent in corrosion resistance; and the rust layer transforming agent is suitable for coating bare steels.

Description

technical field [0001] The invention belongs to the technical field of metal protection, and specifically refers to a bare steel rust layer conversion agent used in a saline environment. Background technique [0002] Metal corrosion is a failure process of metals under the action of environmental corrosive media. It is a completely spontaneous and inevitable natural phenomenon, and it is the reverse process of metallurgical production. Atmospheric corrosion is an important cause of early failure and destruction of products, equipment, devices, and structural parts. The annual economic loss caused by atmospheric corrosion is extremely alarming. In the atmospheric natural environment, the formation of a stable protective rust layer on bare steel is a gradual process, which takes a long time, at least 3 years, and some bare steel surfaces form a dense and stable rust layer for more than 10 years. In the process of forming a stable rust layer, the phenomenon of early rust liqu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C23C22/07
Inventor 黄先球郎丰军程鹏庞涛马颖何锐刘建容王辉李安平刘继雄
Owner 武汉钢铁有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com