Longitudinal shearing splitting disc blade and manufacturing method thereof

A disc blade, slitting and slitting technology, which is applied in the direction of manufacturing tools, knives for shearing devices, shearing devices, etc., can solve the problems of poor toughness and wear resistance, easy deformation, etc., and achieve toughness and durability Good abrasiveness, high sharpness and long service life

Active Publication Date: 2015-09-23
安徽华天机械股份有限公司
View PDF7 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] Aiming at the problems of the existing large-size slitting disc blades in the process of easy deformation, poor toughness and wear resistance, the present invention provides a slitting and slitting disc blade and its manufacturing method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Longitudinal shearing splitting disc blade and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] Such as figure 1 As shown, a slitting and slitting disk blade includes a mounting hole and a blade. The surface roughness of the blade is 0.2, the thickness of the blade is 12±0.002mm, and the outer diameter of the slitting and slitting disk blade is 610mm.

[0043] The steps of manufacturing the above-mentioned slitting and slitting disk blades are:

[0044] (1) Preparation of rough raw materials:

[0045] It is made by using forging blanks for forging. The mass percentages of the forging blank components are: C: 1.32%, Mn: 0.55%, Si: 0.36%, Cr: 6.50%, W: 1.90%, V: 1.54%, Mo: 0.56%, Ni: 0.50%, S: ≤0.020%, P: ≤0.027%, the balance is Fe;

[0046] (2) Isothermal spheroidizing annealing treatment of forged blank:

[0047] The forged blank obtained in step (1) is annealed at a heating rate of s=20T / (h+D)°C / h=20×830 / (12+610)=27°C / h, where T is heat preservation Temperature, the unit is °C, h is the thickness of the cutter head, the unit is mm, D is the outer diameter of ...

Embodiment 2

[0064] Such as figure 1 As shown, a slitting and slitting disk blade includes a mounting hole and a blade, the surface roughness of the blade is 0.2, the blade thickness is 12±0.002mm, and the outer diameter of the slitting and slitting disk blade is 500mm.

[0065] The steps of manufacturing the above-mentioned slitting and slitting disk blades are:

[0066] (1) Preparation of rough raw materials:

[0067] It is made by using forging blanks for forging. The mass percentages of the components of the forging blanks are: C: 1.15%, Mn: 0.40%, Si: 0.40%, Cr: 5.00%, W: 1.50%, V: 1.65%, Mo: 0.40%, Ni: 0.45%, S: ≤0.020%, P: ≤0.027%, the balance is Fe;

[0068] (2) Isothermal spheroidizing annealing treatment of forged blank:

[0069] The forged blank obtained in the step (1) is annealed at a heating rate s=20T / (h+D)°C / h=20×820 / (12+500)=32°C / h, where T is heat preservation Temperature, the unit is °C, h is the thickness of the cutter head, the unit is mm, D is the outer diameter o...

Embodiment 3

[0086] Such as figure 1As shown, a slitting and slitting disk blade includes a mounting hole and a blade. The surface roughness of the blade is 0.2, the blade thickness is 12±0.002mm, and the outer diameter of the slitting and slitting disk blade is 700mm.

[0087] The steps of manufacturing the above-mentioned slitting and slitting disk blades are:

[0088] (1) Preparation of rough raw materials:

[0089] It is made by using forging blanks for forging. The mass percentages of the components of the forging blanks are: C: 1.40%, Mn: 0.65%, Si: 0.32%, Cr: 7.50%, W: 2.50%, V: 1.40%, Mo: 0.60%, Ni: 0.40%, S: ≤0.020%, P: ≤0.027%, the balance is Fe;

[0090] (2) Isothermal spheroidizing annealing treatment of forged blank:

[0091] The forged blank obtained in step (1) is annealed at a heating rate s=20T / (h+D)°C / h=20×840 / (12+700)=24°C / h, where T is heat preservation Temperature, the unit is °C, h is the thickness of the cutter head, the unit is mm, D is the outer diameter of the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Outer circle diameteraaaaaaaaaa
Outer circle diameteraaaaaaaaaa
Outer circle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a longitudinal shearing splitting disc blade and a manufacturing method thereof, and belongs to the technical field of tool machining. The longitudinal shearing splitting disc blade comprises a mounting hole and a cutting edge, the surface roughness of the cutting edge is 0.2, the thickness of the cutting edge is 12+ / -0.002 mm, and the diameter of the outer circle of the longitudinal shearing splitting disc blade ranges from 500 mm to 700 mm. Material components for manufacturing the disc blade comprise, by mass, 1.15 percent to 1.40 percent of C, 0.40 percent to 0.65 percent of Mn, 0.32 percent to 0.40 percent of Si, 5.00 percent to 7.50 percent of Cr, 1.50 percent to 2.50 percent of W, 1.40 percent to 1.65 percent of V, 0.40 percent to 0.60 percent of Mo, 0.40 percent to 0.50 percent of Ni, S smaller than or equal to 0.020 percent, P smaller than or equal to 0.027 percent and the balance Fe. In the annealing and heat treatment process, heating speed is strictly controlled, and the longitudinal shearing splitting disc blade is obtained through quenching by adopting quenching liquid with special components. The longitudinal shearing splitting disc blade has the advantages of being good in tenacity and wear resistance, not likely to deform in the machining process, low in defective percentage and the like.

Description

technical field [0001] The invention belongs to the technical field of tool processing, and more specifically relates to a slitting and slitting disc blade and a manufacturing method thereof. Background technique [0002] Slitter blade design is a harmonious combination of slitter blade geometry, cutting material and coating. Only by continuously introducing advanced slitting machine blade design technology and promoting the development and use of new slitting machine blades can we meet the development needs of advanced cutting processing technology. At present, the world's manufacturing industry is undergoing a profound strategic reorganization. Developed countries and regions such as Europe, America, Japan, and South Korea are carrying out a new round of optimal allocation of manufacturing resources on a global scale. An important market for large-scale industry transfer and beach landing. However, my country's manufacturing technology, especially the level of cutting pr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B23D35/00B23P15/40
Inventor 陶华
Owner 安徽华天机械股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com