Antibacterial, halogen-free, fire-retardant and reinforced polyethylene powder and preparation method thereof

A technology of polyethylene powder and flame retardant, which is applied in the field of antibacterial, halogen-free, flame-retardant reinforced polyethylene powder and its preparation, can solve the problems of insufficient antistatic performance, large molding shrinkage, and low heat resistance, and achieve good anti-static properties. Excellent electrostatic performance, stable performance, electrical performance, heat resistance and corrosion resistance

Inactive Publication Date: 2015-08-19
QINGDAO WANLI TECH
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the oxygen index of polyethylene is 17.0-17.5, which is a flammable material, which is very easy to cause fire. At the same time, polyethylene also has defects such as large molding shrinkage, insufficient antistatic performance, and low heat resistance, which limit its use in certain fields. application in

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0013] The technical solutions of the present invention will be further described below in conjunction with specific embodiments.

[0014] A kind of antibacterial halogen-free flame-retardant reinforced polyethylene powder, its components are proportioned by mass percentage: polyethylene 62%, halogen-free flame retardant 15%, alkali-free glass fiber 12%, SMA 6%, antistatic agent HKD -912 2%, silver ion antibacterial zeolite 1%, 2-hydroxy-4-methoxybenzophenone 1%, modified ethylene bis fatty acid amide TAF 0.8%, antioxidant 0.2%. Wherein, the halogen-free flame retardant is a compound composed of polydimethylsiloxane flame retardant and bisphenol A-bis(diphenyl phosphate) flame retardant with a mass ratio of 1:4; the SMA is styrene-grafted maleic anhydride; the antioxidant is a compound composed of hindered phenolic antioxidant 1010 and phosphite antioxidant 168 at a mass ratio of 1:1.

[0015] Its preparation method is: weigh each component according to the mass percentage ra...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention discloses antibacterial, halogen-free, fire-retardant and reinforced polyethylene powder and a preparation method thereof, wherein the antibacterial, halogen-free, fire-retardant and reinforced polyethylene powder comprises, by mass, 60-80% of polyethylene, 10-15% of a halogen-free fire-retardant agent, 5-12% of alkali-free glass fibers, 2-6% of SMA, 0.5-2% of an antistatic agent, 0.5-1% of an antibacterial agent, 0.1-1% of an anti-aging agent, 0.1-1% of modified ethylene bis fatty acid amide TAF, and 0.1-0.5% of an antioxidant. The antibacterial, halogen-free, fire-retardant and reinforced polyethylene powder of the present invention has beneficial effects of good halogen-free fire-retardant property, good antistatic property, anti-bacterial function, anti-mold function, good mechanical property, stable performance, strong aging resistance, broad antibacterial spectrum, excellent electrical property, excellent heat resistance, excellent corrosion resistance, good processing fluidity, simple preparation process, and low cost so as to provide good use effects and broad prospects.

Description

technical field [0001] The invention relates to the technical field of polymer materials, in particular to an antibacterial, halogen-free, flame-retardant reinforced polyethylene powder and a preparation method thereof. Background technique [0002] Polyethylene has the characteristics of light weight, non-toxicity, easy molding and processing, and high cost performance, and is widely used in many fields. However, the oxygen index of polyethylene is 17.0-17.5, which is a flammable material, which is very easy to cause fire. At the same time, polyethylene also has defects such as large molding shrinkage, insufficient antistatic performance, and low heat resistance, which limit its use in certain fields. in the application. Contents of the invention [0003] The object of the present invention is to provide an antibacterial, halogen-free, flame-retardant reinforced polyethylene powder and a preparation method thereof. [0004] The technical solution adopted by the present ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L23/06C08L35/06C08L83/04C08K13/04C08K7/14C08K5/20C08K5/523
CPCC08L23/06C08L2201/02C08L2201/04C08L2201/08C08L2201/22C08L2205/03
Inventor 不公告发明人
Owner QINGDAO WANLI TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products