Preparing method of high-performance polyurethane buffer cushion

A technology of polyurethane and cushioning pads, applied in the field of cushioning materials, can solve the problems of poor heat resistance, short validity period, easy hydrolysis, etc., and achieve the effects of reducing environmental load, excellent durability, balanced hardness and resilience

Active Publication Date: 2015-07-15
江苏向阳科技有限公司
View PDF3 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] On the other hand, the polyurethane automotive cushions currently produced in China cannot meet the antibacterial requirements, so they can only be used in the low-end automobile market or other markets that do not require high antibacterial requirements.
The preparation of antibacterial automobile buffer blocks in the world originated in the 1990s, mainly based on inorganic silver ion antibacterial agents and organic vanillin antibacterial agents. However, these antibacterial agents are poor in heat resistance, easy to hydrolyze, and have a short validity period. High-end automotive market needs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A preparation method of a high-performance polyurethane buffer pad, the specific steps are:

[0035] (1) Preparation of antibacterial polyols: the polyester polyols derived from plants are warmed up to 80° C., and after they are all melted, the traditional Chinese medicine antibacterial composition accounting for 0.8% of the total weight of polyester polyols is added to the polyester polyols, And the mixture of ester organic sulfonate, tertiary amine catalyst, water and organosiloxane accounting for 2.5% of the total weight of polyester polyol is stirred evenly to obtain antibacterial polyol;

[0036] (2) Preparation of prepolymer: polyether polyol, nano glass powder accounting for 4% of the total weight of polyether polyol, ester organic sulfonate accounting for 2% of the total weight of polyether polyol, titanic acid catalyst 1. The mixture of water and organosiloxane is put into the reaction kettle in proportion, the temperature is rapidly raised to 80°C, and the mod...

Embodiment 2

[0041] A preparation method of a high-performance polyurethane buffer pad, the specific steps are:

[0042](1) Preparation of antibacterial polyol: the polyester polyol derived from plants is warmed up to 85° C., after all melting, the traditional Chinese medicine antibacterial composition accounting for 1.5% of the total weight of polyester polyol is added to the polyester polyol, And the mixture of ester organic sulfonate, tertiary amine catalyst, water and organosiloxane accounting for 3% of the total weight of polyester polyol is stirred evenly to obtain antibacterial polyol;

[0043] (2) Preparation of prepolymer: polyether polyol, nano glass powder accounting for 5% of the total weight of polyether polyol, ester organic sulfonate accounting for 3% of the total weight of polyether polyol, titanic acid catalyst 1. The mixture of water and organosiloxane is put into the reaction kettle in proportion, and the temperature is rapidly raised to 85°C, and the modified isocyanate...

Embodiment 3

[0048] A preparation method of a high-performance polyurethane buffer pad, the specific steps are:

[0049] (1) Preparation of antibacterial polyol: the polyester polyol derived from plants is warmed up to 90° C., after all melting, the traditional Chinese medicine antibacterial composition accounting for 2% of the total weight of polyester polyol is added to the polyester polyol, And the mixture of ester organic sulfonate, tertiary amine catalyst, water and organosiloxane accounting for 3.5% of the total weight of polyester polyol is stirred evenly to obtain antibacterial polyol;

[0050] (2) Preparation of prepolymer: polyether polyol, nano glass powder accounting for 6% of the total weight of polyether polyol, ester organic sulfonate accounting for 4% of the total weight of polyether polyol, titanic acid catalyst 1. The mixture of water and organosiloxane is put into the reaction kettle in proportion, the temperature is rapidly raised to 90°C, and the modified isocyanate is...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
acid valueaaaaaaaaaa
hydroxyl valueaaaaaaaaaa
degree of unsaturationaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparing method of a high-performance polyurethane buffer cushion. The preparing method sequentially comprises the steps of antibiosis polyol preparing, prepolymer preparing, blending, casting moulding and vulcanizing. In the step of antibiosis polyol preparing, polyester polyol from plants is adopted, and self-made traditional Chinese medicine antibiosis composition is added in the preparing process. In the step of prepolymer preparing, low-single-alcohol polyol is adopted as polyether polyol, and nano glass micro powder and modified isocyanate are added in the preparing process. The raw materials for preparing the high-performance polyurethane buffer cushion mostly stem from the plants, and therefore the environment load can be reduced for responding to the social tendency facing the global environment protection recently. The high-performance polyurethane buffer cushion has balanced hardness, rebound resilience, superior durability and good antibacterial capability.

Description

technical field [0001] The invention relates to the field of buffer materials, in particular to a preparation method of a high-performance polyurethane buffer pad. Background technique [0002] In recent years, from the viewpoint of reducing environmental load, plant-derived resins obtained from plant resources have been sought instead of petroleum-derived resins that use petroleum resources as raw materials. That is, the plant-derived resin absorbs CO in the air from one side 2 , while forming raw materials obtained by photosynthetically growing plants, corresponding to CO even through post-use combustion processing 2 emitted into the atmosphere, the result also does not lead to atmospheric CO 2 Therefore, it is attracting attention as a material that contributes to reducing the environmental load. [0003] Polyurethane is a typical carbon-neutral resin. As the polyol component used as a raw material for polyurethane, polyols represented by petroleum-derived polyether po...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08G18/42C08G18/48A01N65/48C08K3/40
CPCY02A50/30
Inventor 陈薇
Owner 江苏向阳科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com