Carbon conductive slag for electroslag steel smelting

A technology of conductive slag and carbon powder, which is applied in the field of electroslag steel smelting, can solve the problems of being unsuitable for smelting low-titanium steel types, high Ti content at the bottom of electroslag steel ingots, and scrapping, etc., to achieve convenient arcing and slag melting, and high production efficiency , low-cost effect

Active Publication Date: 2015-07-01
DAYE SPECIAL STEEL CO LTD
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Because the titanium in the traditional titanium-based conductive slag has a certain influence on the Ti content at the bottom of the electroslag steel ingot, it is not suitable for smelting low-titanium steel.
For example, electroslag bearing steels GCr15 and GCr18Mo require Ti≤0.003%, and G20CrNi2MoA requires Ti≤0.005%. If titanium conductive slag is used for arcing and smelting, the bottom of the electroslag ingot (arcing end) will be due to excessive Ti content. High leads to scrapping

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Carbon conductive slag for electroslag steel smelting
  • Carbon conductive slag for electroslag steel smelting

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] Embodiment 1: according to the ratio in parts by weight: carbon powder: fluorite powder: Na 2 SiO 3 Aqueous solution = 72:24:4 ratio Weigh raw materials, first mix carbon powder, fluorite powder, and then Na 2 SiO 3 The aqueous solution is added to the mixture of carbon powder and fluorite powder, stirred, mixed evenly, made into small pieces using a molding die, and dried for later use; wherein Na 2 SiO 3 The concentration of the aqueous solution is 20%.

Embodiment 2

[0014] Embodiment 2: according to the ratio of parts by weight: carbon powder: fluorite powder: Na 2 SiO 3 Aqueous solution = 75:21:4 ratio to weigh raw materials, first mix carbon powder and fluorite powder evenly, and then Na 2 SiO 3 The aqueous solution is added to the mixture of carbon powder and fluorite powder, stirred, mixed evenly, made into small pieces using a molding die, and dried for later use; wherein Na 2 SiO 3 The concentration of the aqueous solution is 24%.

Embodiment 3

[0015] Embodiment 3: according to the ratio in parts by weight: carbon powder: fluorite powder: Na 2 SiO 3 Aqueous solution = 73:22:5 ratio to weigh raw materials, first mix carbon powder and fluorite powder evenly, and then Na 2 SiO 3 The aqueous solution is added to the mixture of carbon powder and fluorite powder, stirred, mixed evenly, made into small pieces using a molding die, and dried for later use; wherein Na 2 SiO 3 The concentration of the aqueous solution is 26%.

[0016] The carbonaceous conductive slag prepared according to the above examples 1-3 is respectively called carbonaceous conductive slag 1, carbonaceous conductive slag 2, and carbonaceous conductive slag 3. Use electric welding machine welding clips to test its conductivity and arcing stability, and the results As shown in Table 1.

[0017] Table 1 uses Na 2 SiO 3 Carbonaceous conductive slag in aqueous solution and Na-free 2 SiO 3 Performance comparison of carbonaceous conductive slag in aqueo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides carbon conductive slag suitable for electroslag steel smelting and a preparation method thereof. The conductive slag is prepared by carbon powder, fluorite and Na2SiO3 water solution, is excellent in electrical conductivity and arc starting performance, can play an important role in the low-titanium-content steel smelting, reduces the waste rate, and improves the production efficiency.

Description

technical field [0001] The invention relates to a carbonaceous conductive slag suitable for electroslag steel smelting and a preparation method thereof, belonging to the field of electroslag steel smelting. Background technique [0002] In the current electroslag steel smelting, the method of remelting smelting after arcing slag is widely used. The traditional conductive slag is usually titanium conductive slag. The raw materials of titanium conductive slag are titanium dioxide and fluorite (each accounting for 50%). They are placed in the crystallizer and smelted at high temperature using graphite electrodes, and then cooled and crushed for later use. Titanium conductive slag is widely used because of its stable arc starting and convenient operation. With the advancement of science and technology, the quality requirements of steel are getting higher and higher. Because the titanium in the traditional titanium-based conductive slag has a certain influence on the Ti content...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22B9/18
Inventor 张洲陈新余爱华黄志强
Owner DAYE SPECIAL STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com