Ardealite substrate wood-like floor and preparation method thereof

A wood-like floor and phosphogypsum technology, which is applied in the field of chemical building materials, can solve the problems of phosphogypsum storage burden, consumption of forest resources, waste of land resources, etc., reduce the defect rate of long solidification time, and improve solidification performance , enhance the effect of activity

Inactive Publication Date: 2015-06-17
GUIZHOU KAILIN GRP CO LTD
View PDF4 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

As a kind of building material, wooden floor is very popular because of its strong corrosion resistance and obvious thermal insulation effect; and the traditional production field of wooden floor is made of wood, or pressed with sawdust surface. It can be seen that the production process of these two kinds of wooden floors needs to consume a lot of forest resources, which will have a serious impact on the environment and cause serious damage to the ecology.
[0003] In addition, phosphogypsum is a waste generated in the wet-process phosphoric acid production process. Due to its huge annual output, a large amount of phosphogypsum needs to be stockpiled for disposal. Due to its own nature, phosphogypsum is When stockpiling, it will cause serious pollution to the environment, and it will also cause a lot of waste of land resources, causing serious damage to the ecology; based on this, some researchers have begun to do a lot of research on the resource utilization of phosphogypsum , such as adding phosphogypsum as an additive to paint production, and making building materials in cement production; some researchers even use it as the main raw material for sound field building bricks and building blocks; however, these consumption of phosphogypsum It is still difficult to solve the annual output of phosphogypsum waste, and it is still difficult to solve the burden of phosphogypsum stockpiling on the environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A phosphogypsum base material imitation wood floor, its raw material components are 30kg of phosphogypsum, 15kg of yellow phosphorus slag, 0.1kg of quicklime, 0.1kg of cement, 3kg of brine magnesium oxide mixture, 0.1kg of fiber, and 30kg of imitation wood paint.

[0029] Brine magnesium oxide mixture is a mixture of fluorine aqueous solution of halogen elements and magnesium oxide, the mixing ratio is 1:2.

[0030] The fibers are ceramic fibers.

[0031] The content of phosphorus pentoxide in phosphogypsum is 8%.

[0032] Sodium content in phosphogypsum 1%.

[0033] The preparation method of this phosphogypsum substrate imitation wood floor, comprises the following steps:

[0034] (1) Substrate preparation: add phosphogypsum, yellow phosphorus slag, quicklime, cement, brine magnesia mixture, and fiber into the mixing tank in sequence according to the ratio for mixing, and control the temperature in the mixing tank from the initial temperature to normal temperature ,...

Embodiment 2

[0039] A phosphogypsum base material imitation wood floor, its raw material components are 80kg of phosphogypsum, 60kg of yellow phosphorus slag, 10kg of quicklime, 5kg of cement, 5kg of brine magnesium oxide mixture, 2kg of fiber, and 40kg of imitation wood paint.

[0040] The brine magnesium oxide mixture is a mixture of aqueous solution of chlorine, a halogen element, and magnesium oxide, and the mixing ratio is 3:4.

[0041] The fibers are glass fibers.

[0042] The content of phosphorus pentoxide in phosphogypsum is 1%.

[0043] The sodium content in phosphogypsum is 0.1%.

[0044] The preparation method of this phosphogypsum substrate imitation wood floor, comprises the following steps:

[0045] (1) Substrate preparation: add phosphogypsum, yellow phosphorus slag, quicklime, cement, brine magnesia mixture, and fiber into the mixing tank in sequence according to the ratio for mixing, and control the temperature in the mixing tank from the initial temperature to normal t...

Embodiment 3

[0050] A phosphogypsum base material imitation wood floor, its raw material components are 40kg of phosphogypsum, 50kg of yellow phosphorus slag, 8kg of quicklime, 0.9kg of cement, 4kg of brine magnesium oxide mixture, 1kg of fiber, and 33kg of imitation wood paint.

[0051] Brine magnesium oxide mixture is a mixture of bromine aqueous solution of halogen elements and magnesium oxide, the mixing ratio is 2:3.

[0052] The fibers are PVP plastic fibers.

[0053] The content of phosphorus pentoxide in phosphogypsum is 5%.

[0054] The sodium content in phosphogypsum is 0.5%.

[0055] The preparation method of this phosphogypsum substrate imitation wood floor, comprises the following steps:

[0056] (1) Substrate preparation: add phosphogypsum, yellow phosphorus slag, quicklime, cement, brine magnesia mixture, and fiber into the mixing tank in sequence according to the ratio for mixing, and control the temperature in the mixing tank from the initial temperature to normal temper...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of chemical construction materials, in particular to an ardealite substrate wood-like floor and a preparation method thereof. Due to appreciate preparation of ardealite, yellow phosphorus slag, quick lime, cement, a brine and magnesium oxide mixed liquid, fiber and a wood-like coating in a mixing ratio, ardealite is sufficiently activated, the activity of ardealite is improved, the content of soluble impurities in ardealite is further reduced, and the curing property of ardealite is improved; particularly due to addition of the brine and magnesium oxide mixed liquid, sodium in ardealite can form a product which is hard to dissolve, can be fixed in an ardealite crystal cavity, and then is prevented from being exposed on the surface of an ardealite product, so that the phenomenon that the surface of the ardealite product is powdered because of sodium is avoided, the strength and the quality of the ardealite product are improved, and the property of the ardealite product is improved.

Description

technical field [0001] The invention relates to the technical field of chemical building materials, in particular to a phosphogypsum base material imitation wood floor and a preparation method thereof. Background technique [0002] With the continuous improvement and improvement of people's living environment, people's requirements for building decoration materials are also getting higher and higher. As a kind of building material, wooden floor is very popular because of its strong corrosion resistance and obvious thermal insulation effect; and the traditional production field of wooden floor is made of wood, or pressed with sawdust surface. It can be seen that the production process of these two kinds of wooden floors all needs to consume a large amount of forest resources, which will have a serious impact on the environment and cause serious damage to the ecology. [0003] In addition, phosphogypsum is a waste generated in the wet-process phosphoric acid production proces...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B28/32C04B28/14C04B41/70
Inventor 杨永彬向前勇杨步雷王伟刘小成胡新菊李泽钢
Owner GUIZHOU KAILIN GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products