Antiskid wear-resistant sole material and preparation method thereof
A shoe sole material and formula technology, applied in the field of shoe sole materials and its preparation, can solve the problems of low sole elasticity and reduced comfort, and achieve the effects of less environmental pollution, improved anti-slip coefficient, and low loss index
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0023] A kind of non-slip and wear-resistant shoe sole material, it is characterized in that, component and mass percentage thereof are as follows in the formula:
[0024] Natural 3L rubber 20%, butyl rubber 10%, styrene-butadiene rubber 15%, short fiber 5%, carbon black 15%, white carbon black (SiO2) 13%, stearic acid (SA) 1%, paraffin oil 2% , Disilane Tetrasulfide (Si-69) 3%, Sulfur (S) 6%, Active Agent 1%, Antioxidant 1076 or Antioxidant 103 0.5%, Zinc Oxide (ZnO) 3%, Magnesium Oxide 0.5%, D Promote agent, M accelerator and DM accelerator 2%, diatomaceous earth, graphite, carbon black, alumina powder 3%.
[0025] A method for making a non-slip and wear-resistant shoe sole material, comprising the following steps:
[0026] (1) According to the proportion of the formula, the natural rubber, butyl rubber, and styrene-butadiene rubber are kneaded in an open mill for 15-20 minutes to mature the rubber, and short fibers, carbon black, white carbon black (SiO2), stearic acid (SA...
Embodiment 2
[0032] A kind of non-slip and wear-resistant shoe sole material, it is characterized in that, component and mass percentage thereof are as follows in the formula:
[0033] Natural 3L rubber 20%, butyl rubber 15%, styrene-butadiene rubber 10%, short fiber 5%, carbon black 15%, white carbon black (SiO2) 13%, stearic acid (SA) 1%, paraffin oil 2% , Disilane Tetrasulfide (Si-69) 3%, Sulfur (S) 6%, Active Agent 1%, Antioxidant 1076 or Antioxidant 103 0.5%, Zinc Oxide (ZnO) 3%, Magnesium Oxide 0.5%, D Promote agent, M accelerator and DM accelerator 2%, diatomaceous earth, graphite, carbon black, alumina powder 3%.
[0034] A method for making a non-slip and wear-resistant shoe sole material, comprising the following steps:
[0035] (1) According to the proportion of the formula, the natural rubber, butyl rubber, and styrene-butadiene rubber are kneaded in an open mill for 15-20 minutes to mature the rubber, and short fibers, carbon black, white carbon black (SiO2), stearic acid (SA...
PUM
Property | Measurement | Unit |
---|---|---|
thickness | aaaaa | aaaaa |
thickness | aaaaa | aaaaa |
thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com