Asphalt regeneration agent as well as preparation method and application thereof

A technology of asphalt regeneration agent and plant asphalt, which is used in climate change adaptation, building components, building insulation materials, etc., can solve the problems of inability to obtain a large number of applications and small dosage, and restore and improve road performance and enhance adhesion. , the effect of good infiltration and diffusion ability and ductility

Active Publication Date: 2015-05-13
JIANGSU SOBUTE NEW MATERIALS +1
View PDF9 Cites 44 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although plant asphalt has certain applications at present, the amount of use is small. With the continuous development of my country's grain deep processing industry in recent years, the output of plant asphalt as a by-product is increasing, but it cannot be used in large quantities.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Asphalt regeneration agent as well as preparation method and application thereof
  • Asphalt regeneration agent as well as preparation method and application thereof
  • Asphalt regeneration agent as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] An asphalt rejuvenating agent, by mass percentage, consists of the following raw materials:

[0032] Vegetable asphalt, accounting for 70% of the total mass of asphalt rejuvenating agent;

[0033] The interface enhancement modifier adopts epoxy silicone resin, accounting for 4% of the total mass of the asphalt agent regenerant, and the content of epoxy groups in the interface enhancement modifier is 10wt%;

[0034] The plasticizer is carboxymethyl cellulose, accounting for 25% of the total mass of the asphalt regenerant;

[0035] The penetrant is n-octane, accounting for 0.5% of the total mass of the asphalt regenerant;

[0036] The anti-aging agent adopts dibutyl hydroxytoluene (BHT), accounting for 0.5% of the total mass of the asphalt regenerant;

[0037] According to the above ratio, taking the preparation of 100kg of asphalt regenerant as an example, the preparation process of the asphalt regenerant is as follows:

[0038] 75kg of vegetable pitch was heated to 1...

Embodiment 2

[0053] A kind of asphalt regeneration agent, by mass percentage, is made up of following raw materials:

[0054] Vegetable asphalt, accounting for 80% of the total mass of asphalt regenerant;

[0055] The reinforcement modifier adopts epoxy resin, which accounts for 3% of the total mass of the asphalt regenerant, and the epoxy group content in the interface reinforcement modifier is 40wt%.

[0056] The plasticizer is hydroxyethyl cellulose, accounting for 15% of the total mass of the asphalt regenerant;

[0057] The penetrating agent adopts trichlorethylene, accounting for 1% of the total mass of the asphalt regenerant;

[0058] The anti-aging agent adopts 2-hydroxy-4-methoxy-5-sulfobenzophenone (UV-284), accounting for 1% of the total mass of asphalt regenerant;

[0059] According to the above ratio, taking the preparation of 100kg asphalt rejuvenator as an example, the preparation process of asphalt rejuvenator is as follows

[0060] Take 80kg of plant asphalt and heat it...

Embodiment 3

[0075] A kind of asphalt regeneration agent, by mass percentage, is made up of following raw materials:

[0076] Vegetable asphalt, accounting for 65% of the total mass of asphalt regenerant;

[0077] The reinforcement modifier adopts epoxy aliphatic polyethylene polyamine, which accounts for 3% of the total mass of the asphalt regenerant, and the epoxy group content in the interface reinforcement modifier is 30wt%

[0078] Modified petroleum resin is used as plasticizer, accounting for 30% of the total mass of asphalt regeneration agent;

[0079] Chloroform is used as penetrating agent, accounting for 1% of the total mass of asphalt regenerant;

[0080] The anti-aging agent adopts butylated hydroxytoluene (BHT), which accounts for 1% of the total mass of the asphalt regenerant;

[0081] According to the above ratio, taking the preparation of 100kg asphalt rejuvenator as an example, the preparation process of asphalt rejuvenator is as follows:

[0082] Take 65kg of plant as...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an asphalt regeneration agent which is prepared from the following raw materials in percentage by mass: 65-80% of plant asphalt, 3-5% of an interface reinforcing modifier, 15-30% of a plasticizer, 0.3-1% of a penetrating agent and 0.5-1% of an anti-aging agent, wherein the interface reinforcing modifier is one or a mixture of more than two of epoxy aliphatic polyethylene polyamine, epoxy silicon resin and epoxy resin in any ratio; the content of the epoxy group in the interface reinforcing modifier is 10-40%. In addition, the invention further provides a preparation method of the asphalt regeneration agent, an asphalt mixed material prepared from the asphalt regeneration agent, and a preparation method of the asphalt mixed material. When the asphalt mixed material is prepared from the asphalt regeneration agent, the anti-rutting performance, the anti-water damage property and the low-temperature anti-cracking property can be greatly improved, and waste resources can be recycled.

Description

technical field [0001] The invention belongs to the field of road building materials, and in particular relates to an asphalt regenerant and a preparation method and application thereof. Background technique [0002] With the acceleration of highway construction in my country, the maintenance and repair tasks of roads are intensified. Every year, tens of millions of tons of old pavement materials (RAP) are generated in the process of road reconstruction, renovation or maintenance. How to deal with the old pavement materials reasonably and effectively, and how to effectively protect the ecological environment while the road is developing, will become an important issue. problems that must be faced. According to the existing research experience, the use of asphalt recycling technology to recycle old pavement materials will be an effective method to solve the problem of old pavement materials. The research idea of ​​the traditional asphalt mixture regeneration is to soften th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L95/00C08L1/28C08L63/00C08L57/02C08L83/04C08K5/13C08K5/01C08K5/02C08K5/132C04B26/26
CPCY02A30/30
Inventor 洪锦祥耿磊陈香张德育林俊涛张苏龙熊子佳魏唐中
Owner JIANGSU SOBUTE NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com