Precisely cast low-temperature modulated wax and preparation method thereof

A technology of precision casting and low temperature, which is applied in the field of precision casting low-temperature modulation wax and its preparation, which can solve the problems such as difficult to produce high-quality mold materials, and achieve the effects of good dimensional stability, easy demoulding, and high productivity

Inactive Publication Date: 2015-05-06
青岛新诺科铸造材料科技有限公司
View PDF0 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Obviously, the self-sufficient mold material production method of the investment casting production plant is difficult to produce high-quality mold material, so this situation is contradictory to modern mass production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A low-temperature modulation wax for precision casting, wherein the raw materials of the low-temperature modulation wax for precision casting include: 44-46 parts of microcrystalline wax, 2.5-3.5 parts of montan wax, 34-36 parts of rosin resin, ethylene-vinyl acetate copolymer 3.5-4.5 parts of compound, 12-14 parts of pure monomer resin.

[0026] The preparation method steps of the above-mentioned investment casting low temperature modulated wax include:

[0027] (1) Divide the rosin resin into two parts, heat half of it at 120 degrees, and keep stirring until it melts, then add the other half of the rosin, keep stirring, and continue heating until it melts to obtain molten rosin resin A;

[0028] (2) Continue heating the molten rosin resin A obtained in step (1) at a temperature of 100-120 degrees for 1-2 minutes, add montan wax, and keep stirring until it is completely melted to obtain a mixture B;

[0029] (3) Continue heating the mixture B obtained in step (2) at ...

Embodiment 2

[0035] A low-temperature modulation wax for precision casting, the raw materials of the low-temperature modulation wax for precision casting include: 44 parts of microcrystalline wax, 2.5 parts of montan wax, 34 parts of rosin resin, 3.5 parts of ethylene-vinyl acetate copolymer, pure Body resin 12 parts.

[0036] The preparation method steps of the above-mentioned investment casting low temperature modulated wax include:

[0037] (1) Divide the rosin resin into two parts, heat half of it at 120 degrees, and keep stirring until it melts, then add the other half of the rosin, keep stirring, and continue heating until it melts to obtain molten rosin resin A;

[0038] (2) Continue heating the molten rosin resin A obtained in step (1) at a temperature of 100-120 degrees for 1-2 minutes, add montan wax, and keep stirring until it is completely melted to obtain a mixture B;

[0039] (3) Continue heating the mixture B obtained in step (2) at a temperature of 110-120 degrees for 1-2...

Embodiment 3

[0045] A low-temperature modulation wax for precision casting, the raw materials of the low-temperature modulation wax for precision casting include: 46 parts of microcrystalline wax, 3.5 parts of montan wax, 36 parts of rosin resin, 4.5 parts of ethylene-vinyl acetate copolymer, pure Body resin 14 parts.

[0046] The preparation method steps of the above-mentioned investment casting low temperature modulated wax include:

[0047] (1) Divide the rosin resin into two parts, heat half of it at 120 degrees, and keep stirring until it melts, then add the other half of the rosin, keep stirring, and continue heating until it melts to obtain molten rosin resin A;

[0048] (2) Continue heating the molten rosin resin A obtained in step (1) at a temperature of 100-120 degrees for 1-2 minutes, add montan wax, and keep stirring until it is completely melted to obtain a mixture B;

[0049] (3) Continue heating the mixture B obtained in step (2) at a temperature of 110-120 degrees for 1-2...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
cone penetrationaaaaaaaaaa
shrinkageaaaaaaaaaa
cone penetrationaaaaaaaaaa
Login to View More

Abstract

The invention discloses a precisely cast low-temperature modulated wax and a preparation method thereof. The precisely cast low-temperature modulated wax comprises the following raw materials in parts by weight: 44-46 parts of microcrystalline wax, 2.5-3.5 parts of lignite wax, 34-36 parts of rosin resin, 3.5-4.5 parts of an ethylene-vinyl acetate copolymer and 12-14 parts of pure monomer resin. The wax disclosed by the invention is applied to a precision casting industry, has stability, hardly deforms due to high strength and hardly pollutes the metal cast due to low gray scale, is easy to demold, can be melted together with a wax mold to flow out of a shell during demolding; and the production rate can be effectively improved in the precision casting process.

Description

technical field [0001] The invention relates to the precision casting industry, in particular to a precision casting low-temperature modulated wax used in the precision casting industry and a preparation method thereof. Background technique [0002] With the development of society, precision castings have been widely used in all industrial sectors such as aviation and weapons, especially electronics, petroleum, chemical industry, transportation, light industry, textile, pharmaceutical, medical equipment, pump and valve components. The molding material used by most of the investment casting factories in my country is the paraffin-stearic acid low-temperature molding material made by the investment casting factory. Its quality is low, cost is high, and seriously affects the improvement of casting quality, and the casting produced is less competitive in the international market. However, many investment casting factories in our country hope to produce castings for export. If ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L91/06C08L93/04C08L23/08B22C7/02
Inventor 邵斌
Owner 青岛新诺科铸造材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com