Polyvinyl chloride grade-A fireproof material and preparation method thereof

A technology of polyvinyl chloride and fireproof materials, applied in the field of materials, can solve problems such as the improvement of fireproof grade, and achieve the effect of easy processing

Inactive Publication Date: 2015-04-29
SHENDUN FIREPROOF TECH
View PDF4 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

To sum up, the urgent problem to be solved for polyvinyl chloride materials is to improve the fire protection level.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyvinyl chloride grade-A fireproof material and preparation method thereof
  • Polyvinyl chloride grade-A fireproof material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] The flame-retardant polyether of this embodiment is composed of the following raw materials: 1 part of rare earth fluoride, 0.5 parts of butylene oxide, 1.5 parts of catalyst, and 1.5 parts of polytetrafluoroethylene; wherein, 1.5 parts of catalyst is composed of the following components: 0.6 parts Methanol, 0.5 parts of silicone oil, 0.3 parts of sodium silicate, 0.1 parts of sodium bicarbonate.

[0030] The preparation method of flame retardant polyether in the present embodiment comprises the following steps:

[0031] (1) Put the fluoride, butylene oxide, catalyst, and polytetrafluoroethylene of the proportioning amount into a cylindrical airtight reaction vessel (arc generator is set in the reaction vessel, and microwave is set at the 1.5m height of the reactor wall. Generator), after vacuuming, fill it with non-oxidizing gas, so that the pressure in the container is 75MPa;

[0032] (2) Under the conditions of a temperature of 560°C, a voltage of 15,000 volts, and ...

Embodiment 2

[0034] The difference between this embodiment and embodiment 1 is that the fluoride used in embodiment 2 is sodium fluoride.

Embodiment 3

[0036] The difference between this embodiment and embodiment 1 is that in embodiment 3, 3 parts of polytetrafluoroethylene are selected for use.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to the field of materials, in particular to a polyvinyl chloride grade-A fireproof material. The polyvinyl chloride grade-A fireproof material is prepared from the following constituents in parts by weight: 70-85 parts of PVC, 15-20 parts of expansible graphite, 10-15 parts of borax, 35-50 parts of hexabromocyclododecane, 15-25 parts of zinc borate, 13-18 parts of magnesium hydroxide, 13-20 parts of fire-retardant polyether, 8-12 parts of a carbon forming agent, 0.01-0.10 part of a stabilizer, 4-10 parts of a plasticizer, 3-8 parts of antimonous oxide, 3-8 parts of a phase solvent, 0.05-0.30 part of a coupling agent, and 13-18 parts of aluminum hydroxide. The polyvinyl chloride fireproof material provided by the invention can be up to grade A, has dampproof and mildewproof functions when being processed and molded to form a plate, a sheet, a tube stock, a sectional material or a foam material, meanwhile has thermal insulation and sound insulation properties, is free of oil paint, non-combustible, not afraid of burning, convenient to process, environment-friendly, and non-pollution, and further has various processing characteristics of the wood.

Description

technical field [0001] The invention relates to the field of materials, in particular to a class A polyvinyl chloride fireproof material and a preparation method thereof. Background technique [0002] Polyvinyl chloride is one of the plastic products with the largest output in the world. It is cheap and is a material with a wide range of uses. It is often used in our lives, such as PVC pipes, PVC floors, PVC wallpapers, PVC furniture, PVC leather, PVC interior decoration boards, sheets, profiles, etc. Adding different additives according to different uses, PVC plastics can exhibit different physical and mechanical properties. Adding an appropriate amount of plasticizer to polyvinyl chloride resin can make a variety of hard, semi-rigid, soft and transparent products. [0003] After searching, it was found that the invention patent application with publication number CN104072904A discloses a polyvinyl chloride plastic, including the following raw materials in parts by weight...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L27/06C08L71/00C08K13/02C08K3/04C08K3/38C08K3/22C08K5/02C08K5/098C08K5/12C08G65/20
CPCC08L27/06C08K2201/005C08L2201/02C08L2205/02C08L2205/035C08L71/02C08L27/18C08L91/00C08K13/06C08K9/06C08K3/04C08K3/38C08K5/02C08K2003/387C08K2003/2224C08K5/053C08K5/098C08K3/2279C08K5/12C08K2003/2227
Inventor 杨京学李保国杨继彬宫连仲宫怀叡
Owner SHENDUN FIREPROOF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com