Zinc-silver antimicrobial bibulous acrylic ester foam material as well as preparation method and application thereof

A technology of acrylate and foam materials, which can be used in absorbent pads, medical science, bandages, etc. It can solve the problems of easy breeding of bacteria and skin allergies, and achieve the effect of good water absorption and high absorption rate

Active Publication Date: 2015-03-11
佛山市联塑万嘉新卫材有限公司
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, when sanitary products are contaminated by body fluids such as urine, bacteria are likely to breed and cause skin allergies and other problems

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Zinc-silver antimicrobial bibulous acrylic ester foam material as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] S1. Prepare an oil phase system, weigh 7.2 g of isooctyl acrylate, 0.8 g of isooctyl methacrylate, 4.8 g of ethylene glycol dimethacrylate, 0.4 g of hexanediol diacrylate, and 1.6 g of silver zinc Antibacterial microparticles, 1.2 g of Tween-80, and the oil phase was stirred evenly for use, wherein the mass ratio of isooctyl acrylate to isooctyl methacrylate was 9:1.

[0050] S2. To prepare an aqueous phase system, weigh 0.096 g of calcium chloride, add water to 480 g to dissolve it, and at this time, the mass fraction of the electrolyte is 0.02%, ready for use; to prepare an initiator phase, weigh 1.71 g of ammonium persulfate , add water to 10g to make it dissolve, set aside.

[0051] S3. Transfer 320 g of the prepared water phase into a 1000ml three-necked flask, start stirring, heat up to 75°C, and stir at a speed of more than 800 rpm, then add the well-stirred oil phase into the three-necked flask, and wait until the emulsion becomes thick. , and then add 160g wat...

Embodiment 2

[0054] S1. Prepare an oil phase system, weigh 7 g of isooctyl acrylate, 1 g of isooctyl methacrylate, 4.8 g of ethylene glycol dimethacrylate, 0.4 g of hexanediol diacrylate, and 1.6 g of silver zinc antibacterial Microparticles, Tween-80 1.2g, stir the oil phase evenly and stand by, wherein the mass ratio of isooctyl acrylate to isooctyl methacrylate is 7:1.

[0055] S2. To prepare an aqueous phase system, weigh 0.096 g of calcium chloride, add water to 480 g to dissolve it, and at this time, the mass fraction of the electrolyte is 0.02%, ready for use; to prepare an initiator phase, weigh 1.71 g of ammonium persulfate , add water to 10g to make it dissolve, set aside.

[0056] S3. Transfer 320 g of the prepared water phase into a 1000ml three-necked flask, start stirring, heat up to 75°C, and stir at a speed of more than 800 rpm, then add the well-stirred oil phase into the three-necked flask, and wait until the emulsion becomes thick. , and then add 160g water phase dropwi...

Embodiment 3

[0059] S1. Prepare an oil phase system, weigh 12 g of isooctyl acrylate, 1.5 g of isooctyl methacrylate, 0.4 g of ethylene glycol dimethacrylate, 0.4 g of hexanediol diacrylate, and 0.8 g of silver zinc bacterial microparticles, Tween-80 0.8g, and the oil phase was stirred evenly for use, wherein the mass ratio of isooctyl acrylate to isooctyl methacrylate was 8:1.

[0060] S2. To prepare an aqueous phase system, weigh 0.096 g of calcium chloride, add water to 480 g to dissolve it, and at this time, the mass fraction of the electrolyte is 0.02%, ready for use; to prepare an initiator phase, weigh 1.71 g of ammonium persulfate , add water to 10g to make it dissolve, set aside.

[0061] S3. Transfer 320 g of the prepared water phase into a 1000ml three-necked flask, start stirring, heat up to 75°C, and stir at a speed of more than 800 rpm, then add the well-stirred oil phase into the three-necked flask, and wait until the emulsion becomes thick. , and then add 160g water phase ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
quality scoreaaaaaaaaaa
Login to View More

Abstract

The invention discloses a zinc-silver antimicrobial bibulous acrylic ester foam material as well as a preparation method and application thereof. The cellular size of the prepared foam material is micro; the average deionized water absorption rate, the average saline water absorption rate, the average artificial urine absorption rate and the average artificial blood absorption rate of the prepared foam material are respectively greater than 18g / g; the water retenticities of the indexes in one hour are over 85 percent respectively; the zinc-silver antimicrobial bibulous acrylic ester foam material is suitable for dispersing and storing water-containing fluid; in addition, by adding zinc-silver antibacterial particles, the foam material has good antibacterial performance; the antibacterial rates of the foam material for escherichia coli and staphylococcus aureus respectively reach over 95 percent. Therefore the block soft water-absorbing material disclosed by the invention is particularly suitable for the field of sanitation supplies.

Description

technical field [0001] The invention belongs to the field of water-absorbing materials, and in particular relates to a silver-zinc antibacterial water-absorbing acrylate foam material and a preparation method and application thereof. Background technique [0002] In today's hygienic products, the water-absorbing material inside is mainly granular synthetic resin. After absorbing water, urine or blood, it will form a gel, which is easy to form agglomerates, making it difficult to fix in one position. It is very uncomfortable in the actual use process. Comfortable. Therefore, it is of great significance to develop block-shaped soft water-absorbing materials. [0003] Normal blood is composed of blood cells, plasma, etc. The diameter of blood cells is about 8 μm, and the diameter of acrylic acid molecules is much smaller than that of blood cells. Therefore, blood cells are not easily absorbed by the gel-like superabsorbent resin, and can only stay on the surface of the super...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08F220/18C08F222/14C08F2/30C08K3/08C08J9/28A61L15/24
Inventor 梁永江
Owner 佛山市联塑万嘉新卫材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com