Metal organic frame material-based composite heat stabilizer for PVC (polyvinyl chloride) and application of metal organic frame material-based composite heat stabilizer

A composite thermal stabilizer and metal organic framework technology, applied in the field of material applications, can solve the problems of serious initial coloration and poor long-term thermal stability, and achieve the effects of good long-term thermal stability, improved thermal stability and good compatibility.

Inactive Publication Date: 2015-03-04
SHAOYANG UNIV
View PDF6 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Compared with lead salts and organotin heat stabilizers, it has defects such as serious initial coloring and poor long-term heat stability

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] The composite thermal stabilizer of this embodiment contains the following components in mass fractions: MOF-5: 35%, calcium stearate: 25%, hydrotalcite: 25%, and β-diketone: 15%.

[0016] To 100 parts of PVC powder, add 40 parts of dioctyl phthalate and 5 parts of composite heat stabilizer, mix at high speed for 5 minutes, knead on a double-roll mill at 170°C for 5 minutes, and roll to 1 mm Thickness of the sheet sample, and cut into 2 cm × 2 cm PVC sheet.

Embodiment 2

[0018] The composite heat stabilizer of this embodiment contains the following components in mass fraction: ZIF-4: 45%, calcium stearate: 25%, hydrotalcite: 20%, β-diketone: 10%.

[0019] Add 50 parts of dioctyl phthalate and 5 parts of composite heat stabilizer to 100 parts of PVC powder, mix at high speed for 4 minutes, knead on a double-roll mill at 180°C for 5 minutes, and roll to 1 mm Thickness of the sheet sample, and cut into 2 cm × 2 cm PVC sheet.

Embodiment 3

[0021] The composite thermal stabilizer of this embodiment contains the following components in mass fraction: ZIF-8: 40%, calcium stearate: 35%, hydrotalcite: 15%, and β-diketone: 10%.

[0022] Add 55 parts of dioctyl phthalate and 5 parts of compound heat stabilizer to 100 parts of PVC powder, mix at high speed for 5 minutes, knead on a double-roll mill at 190°C for 4 minutes, and roll to 1 mm Thickness of the sheet sample, and cut into 2 cm × 2 cm PVC sheet.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a metal organic frame material-based composite heat stabilizer for PVC (polyvinyl chloride) and application of the metal organic frame material-based composite heat stabilizer. The composite heat stabilizer comprises the following components by mass fraction: 10%-80% of a metal organic frame material, 5%-50% of calcium stearate, 10%-55% of hydrotalcite and 5%-20% of beta-diketone. According to the composite heat stabilizer, the initial hue and long-term heat stability of the PVC in the processing process can be significantly improved; and the comprehensive heat stability effect is superior to that of a calcium-zinc composite heat stabilizer of taking zinc stearate as a main component. In addition, various components of the composite heat stabilizer belong to non-toxic and environment-friendly materials, and the composite heat stabilizer is good in compatibility with the PVC, and low in migration rate.

Description

technical field [0001] The invention relates to a metal-organic frame material-based composite heat stabilizer for PVC and its application, belonging to the field of material application. Background technique [0002] PVC is easy to decompose at processing temperature, resulting in darkening of product color and changes in structure and properties. Therefore, during the processing of PVC, heat stabilizers must be added to prevent or reduce its decomposition. At present, commonly used heat stabilizers include lead salts, organotins, metal soaps and composite heat stabilizers. Lead salt heat stabilizer is the earliest developed PVC heat stabilizer with good heat stability. However, due to the strong toxicity of lead salt compounds, which pose a hazard to human and environmental safety, countries around the world are gradually restricting the use of lead salt heat stabilizers. Organotin heat stabilizers have good thermal stability and transparency, and low toxicity. They are...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08K13/02C08K5/00C08K5/098C08K3/26C08K5/07
CPCC08K3/26C08K5/005C08K5/07C08K5/098C08K13/02C08K2003/265C08L27/06
Inventor 周喜李海燕戴友志
Owner SHAOYANG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com