Method for processing rare earth photochromic color flash air-jet vortex spun yarns

A photochromic and processing method technology, applied in the direction of continuous winding spinning machine, yarn, spinning machine, etc., can solve the problems of novel, changeable and dreamy air-jet vortex yarn products that have never been seen before, and avoid dyeing. Difficult, uniform flashing effect, short technological process

Active Publication Date: 2014-12-24
SHAOXING UNIVERSITY
View PDF14 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] However, at present, air-jet vortex spinning mainly focuses on the development of natural color yarn and ordinary color spinning yarn, and there is no air-jet vortex yarn product with novel, changeable and dreamy colors.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for processing rare earth photochromic color flash air-jet vortex spun yarns

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] figure 1 It is a schematic diagram of the processing flow of the rare earth photochromic fiber light-colored air-jet vortex yarn in this embodiment. like figure 1 As shown, the rare earth photochromic polyester fiber with a content of 5% and the viscose natural color fiber with a content of 95% are carded and loosened respectively, and then coagulated and mixed by airflow, and finally the carding and three drawing processes are completed. Air-jet vortex spinning technology obtains 40 British-count rare earth photochromic fiber flashing color air-jet vortex yarn after drawing, twisting, winding, winding and other processing procedures. and other fields.

[0030] In this example, the rare earth photochromic polyester fiber is prepared by doping with rare earth oxides. The carding process adopts the technological principle of "light weight, low speed, large gauge, and small tension" to reduce fiber damage, so that the fibers can be fully carded and well transferred; the...

Embodiment 2

[0033] Comb and open the rare earth photochromic viscose fiber with 20% content, 5% metal wire fiber, 30% modal natural color fiber, and 45% light gray polyester fiber, and then use it under the condition of spraying antistatic agent The air flow is condensed and mixed (the workshop temperature is controlled at 26±2°C, and the relative humidity is controlled at 55±4%, so as to reduce the phenomenon of winding rubber rollers and aprons in the subsequent process), and finally complete the carding and three drawing frames, and finally use Air-jet vortex spinning technology obtains 30 lbs rare earth photochromic fiber flashing color air-jet vortex yarn after drawing, twisting, winding, winding and other processing procedures. The yarn prepared in this embodiment can be used for dyed fabrics, high-end fashion , Evening dresses and other products are under development.

[0034] In this example, the rare earth photochromic polyester fiber is prepared by hybridization of rare earth co...

Embodiment 3

[0037] The photochromic polyester fiber with a content of 60% rare earth and 40% natural fiber of bamboo pulp are carded and loosened respectively, and then condensed and mixed by airflow under the condition of spraying antistatic agent (the workshop temperature is controlled at 25±1°C, The relative humidity is controlled at 53±4% to reduce the phenomenon of winding cots and aprons in the back pass), and finally complete the carding and three drawing frames, and finally use the air-jet vortex spinning technology to go through drafting, twisting, winding, After winding and other processing steps, 30 lbs. rare earth photochromic fiber flashing air-jet vortex yarn was obtained. The yarn prepared in this embodiment can be used in the development of products such as colored fabrics, trademarks, patterns and decorative fabrics.

[0038] In this example, the rare earth photochromic polyester fiber is prepared by bonding with rare earth inorganic salts. The carding process adopts the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for processing rare earth photochromic color flash air-jet vortex spun yarns. The method comprises the following steps of carding and opening rare earth photochromic fibers and other fibers respectively; performing quantitative cohesion and blend on the rare earth photochromic fibers and other fibers by using airflow; carding cotton and performing a three-pass drawing procedure; drawing, twisting, spooling and winding blended fibers by using air-jet vortex spinning to obtain rare earth photochromic fiber color flash air-jet vortex spun yarns. The rare earth photochromic fibers and other natural color fibers, colored fibers in obvious contrast to the rare earth photochromic color, or a mixture of natural color fibers and colored fibers is blended, so that the characteristics of the rare earth photochromic fibers are fully utilized to enable the yarns to present a color flash effect, the prepared yarns do not require a dyeing procedure to avoid the problem that the rare earth photochromic fibers are difficultly dyed, and the production cost is reduced.

Description

technical field [0001] The invention belongs to the field of novel yarn processing, and in particular relates to a rare earth photochromic flashing air-jet vortex yarn processing method. Background technique [0002] Rare earth photochromic fiber is a fiber that changes color automatically after being stimulated by light conditions. The application of its products can greatly satisfy consumers' pursuit of novelty, diversity and fantasy in clothing colors. [0003] However, due to the addition of rare earth materials, the rare earth photochromic fiber affects the fiber's tensile properties and dyeing properties. 100% rare earth photochromic fiber yarn products face problems such as high production costs and difficult dyeing, which limits the application field. [0004] Air-jet vortex spinning technology is currently the yarn processing technology with the fastest spinning speed. Chinese patent CN101294319 B "air-jet vortex spinning device with low fiber fall" and Chinese pate...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D02G3/04D01H4/02
Inventor 戴淑娇邹专勇徐蓉蓉曾真
Owner SHAOXING UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com