Fast heat treatment method for controlling magnetic property of double-roller thin-strip casting non-oriented silicon steel

A twin-roll thin strip continuous casting and rapid heat treatment technology, applied in the field of metallurgy, can solve the problems of less research on control methods, affecting the magnetic properties of non-oriented silicon steel, etc., to achieve the easy realization of rapid heat treatment technology, obvious magnetic properties of products, and rapid heat treatment. technically simple effect

Inactive Publication Date: 2014-12-03
NORTHEASTERN UNIV LIAONING
View PDF3 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, at present, during the production of silicon steel by twin-roll thin strip continuous casting, there are few studies on the control methods affecting the magnetic properties of non-oriented silicon steel, especially the control methods for its structure and texture.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fast heat treatment method for controlling magnetic property of double-roller thin-strip casting non-oriented silicon steel
  • Fast heat treatment method for controlling magnetic property of double-roller thin-strip casting non-oriented silicon steel
  • Fast heat treatment method for controlling magnetic property of double-roller thin-strip casting non-oriented silicon steel

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] 1. Non-oriented silicon steel is prepared according to the mass percentage of chemical composition: C: 0.0032%, Si: 1.39%, Mn: 0.20%, Al: 0.32%, O: 0.0043%, S: 0.004%, N: 0.0072%, and the rest is Fe and unavoidable impurities; the non-oriented silicon steel is smelted into molten steel, the pouring temperature is controlled at 1560±2°C, and the molten steel is poured into the molten pool of the twin-roll strip continuous casting machine through the tundish, and the molten pool is formed by the rotating steel roll Composed of side sealing plates, the molten steel solidifies and forms rapidly after contacting the crystallized roll surface of the steel roll, and a cast strip with a thickness of 2.5±0.3mm is obtained. The cast strip structure is single-phase ferrite, which is uneven along the thickness direction. The surface layer is a larger columnar crystal with an average grain size of about 360 μm, such as figure 1 shown;

[0024] 2. Air-cool the cast strip to 699±1°C ...

Embodiment 2

[0031]1. Non-oriented silicon steel is prepared according to the mass percentage of chemical composition: C: 0.0032%, Si: 1.23%, Mn: 0.41%, Al: 0.20%, O: 0.0043%, S: 0.0042%, N: 0.0052%, and the rest is Fe and unavoidable impurities; the non-oriented silicon steel is smelted into molten steel, the pouring temperature is controlled at 1598±2°C, and the molten steel is poured into the molten pool of the twin-roll strip continuous casting machine through the tundish, and the molten pool is formed by the rotating steel roll Composed of side sealing plates, molten steel solidifies and forms rapidly after contacting the crystalline roll surface of the steel roll, and a cast strip with a thickness of 2.5±0.1mm is obtained. The cast strip structure is single-phase ferrite, and the surface layer and the middle and lower layers are fine and equiaxed crystal, the subsurface layer is columnar crystal, the average grain size is about 400μm;

[0032] 2. Air-cool the cast strip to 601±1°C be...

Embodiment 3

[0039] 1. Non-oriented silicon steel is prepared according to the mass percentage of chemical composition: C: 0.0032%, Si: 0.52%, Mn: 0.35%, Al: 0.40%, O: 0.0043%, S: 0.0035%, N: 0.0052%, and the rest is Fe and unavoidable impurities; the non-oriented silicon steel is smelted into molten steel, the pouring temperature is controlled at 1542±2°C, and the molten steel is poured into the molten pool of the twin-roll strip continuous casting machine through the tundish, and the molten pool is formed by the rotating steel roll Composed of side sealing plates, molten steel solidifies and forms rapidly after contacting the crystallized roll surface of the steel roll, and obtains a cast strip with a thickness of 2.5±0.2mm. The cast strip structure is single-phase ferrite, and the cast strip structure is uneven. The surface layer is Fine equiaxed crystals, the subsurface layer is coarse columnar crystals, the average grain size is about 390μm;

[0040] 2. Air-cool the cast strip to 501±...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of metallurgy and provides a fast heat treatment method for controlling the magnetic property of double-roller thin-strip casting non-oriented silicon steel aiming at enhancing the magnetic property of non-oriented silicon steel. The fast heat treatment method comprises the following steps: pouring molten non-oriented silicon steel into a double-roller thin-strip casting machine through a tundish to cast a casting strip with the thickness of 2.5+ / -0.3 mm; cooling the casting strip, then coiling, pickling the coiled casting strip, and then directly carrying out first-stage cold rolling to obtain a thin strip of 0.5 mm; and fast annealing the thin strip after the first-stage cold rolling, and removing the residual stress of the annealed thin strip by adopting stress relief annealing after punching to obtain a non-oriented silicon steel finished product. The magnetic property of the non-oriented silicon steel finished product is as follows: an iron loss value is P15 / 504.76-7.34 W / kg, and the magnetic induction is B501.793-1.840 T. According to the fast heat treatment method, the non-oriented silicon steel produced by controlling fast heat treatment and combining with thin-strip casting is simple in technology, easy to realize, controlled in structure and structural component and high in annealing efficiency, and a product is obviously enhanced in magnetic property.

Description

technical field [0001] The invention belongs to the technical field of metallurgy, and in particular relates to a rapid heat treatment method for controlling the magnetic properties of twin-roll strip continuous casting non-oriented silicon steel. Background technique [0002] Non-oriented silicon steel, also known as non-oriented electrical steel, is a Si-Fe alloy with very low carbon content. The grains in the steel plate / strip are distributed in random orientation. The nominal thickness of the product is 0.35, 0.5mm and 0.65mm. It is mainly used for the manufacture of electric motors and generators. The magnetic properties of silicon steel sheets are not only directly related to the loss of electric energy, but also determine the performance, volume, weight and cost of products such as motors and transformers. Loss value and increase the magnetic induction intensity are the goals that the non-oriented silicon steel manufacturing industry has been pursuing. [0003] In t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C21D8/12C22C38/06
Inventor 许云波张元祥方烽王洋卢翔焦海涛曹光明李成刚刘振宇王国栋
Owner NORTHEASTERN UNIV LIAONING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com