Flame-retardant acrylonitrile butadiene styrene (ABS) resin with excellent surface glossiness and high blackness and preparation method of ABS resin

An ABS resin and high-gloss technology, which is applied in the field of high-gloss, high-blackness flame-retardant ABS resin and its preparation, to achieve the effects of excellent surface, reduced pitting, and high surface gloss

Active Publication Date: 2014-10-08
SHANGHAI KUMHO SUNNY PLASTICS
View PDF3 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But there is no report about a kind of high gloss and high blackness flame retardant ABS resin with excellent surface

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Flame-retardant acrylonitrile butadiene styrene (ABS) resin with excellent surface glossiness and high blackness and preparation method of ABS resin
  • Flame-retardant acrylonitrile butadiene styrene (ABS) resin with excellent surface glossiness and high blackness and preparation method of ABS resin
  • Flame-retardant acrylonitrile butadiene styrene (ABS) resin with excellent surface glossiness and high blackness and preparation method of ABS resin

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0041] The preparation method of above-mentioned fire-retardant ABS resin, comprises the following steps:

[0042] (1) Put ABS rubber powder, AS resin, flame retardant synergist, brominated flame retardant, heat stabilizer, antioxidant, lubricant, carbon black dispersant and carbon black powder into a high-speed mixer and stir for 5- After 30min, discharging obtains mixture;

[0043] (2) The mixture obtained in step (1) is extruded and granulated through a twin-screw extruder, the temperature of the extruder is 180-220°C, the strict vacuum degree is greater than 0.09Mpa, and the screw speed is 180-600 rpm.

[0044] Embodiment 1-5 of the present invention and comparative example 1-2 used raw material are as shown in table 1:

Embodiment 1-5 and comparative example 1-2

[0047] Embodiment 1-5 and comparative example 1-2 are implemented according to the following steps:

[0048] Put ABS rubber powder, AS resin, flame retardant synergist, brominated flame retardant, heat stabilizer, antioxidant, lubricant, carbon black dispersant and carbon black powder into a high-speed mixer and stir for 5-30 minutes before leaving The obtained mixture is extruded and granulated through a twin-screw extruder, the temperature of the extruder is 180-220°C, the strict vacuum degree is greater than 0.09Mpa, and the screw speed is 180-600 rpm. The product is obtained by conveying, melting, shearing, extrusion, cooling and granulation.

Embodiment 1

[0050] Prepare raw materials according to the following components and parts by weight:

[0051] P / D190 35

[0052] SAN320 65

[0053] Sb 2 o 3 4

[0054] BTAC245 19

[0055] T-580 0.3

[0056] IG-1076 0.3

[0057] T-0004 0.2

[0058] P 121 0.2

[0059] 9550WA 2

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a flame-retardant acrylonitrile butadiene styrene (ABS) resin with excellent surface glossiness and high blackness. The ABS resin comprises the following components in parts by weight: 20-60 parts of ABS rubber powder, 40-80 parts of AS (Acrylonitrile-Styrene) resin, 2-6 parts of flame-retardant synergist, 5-25 parts of brominated flame retardant, 0.1-1 part of heat stabilizer, 0.1-1 part of antioxidant, 0.1-1 part of lubricating agent, 0.1-2 parts of carbon black dispersing agent and 0.1-5 parts of carbon black powder, wherein the carbon black dispersing agent is a block polymerization amphipathic siloxane compound of which one end is provided with a lipophilic group and of which the other end is provided with a hydrophilic group; the carbon black powder is pure carbon black or carbon black master-batches with polyolefin or ethylene vinyl acetate copolymer as a carrier. The invention also provides a method for preparing the flame-retardant ABS resin. The flame-retardant ABS resin has extremely high surface glossiness and balanced toughness and fluidity and is particularly suitable for household appliance industry with the requirements of high glossiness and flame retardant property.

Description

technical field [0001] The invention relates to the technical field of polymer modification, in particular to a high gloss and high blackness flame retardant ABS resin with excellent surface and a preparation method thereof. Background technique [0002] Styrene-acrylonitrile-butadiene copolymer (ABS) has high surface hardness, good impact resistance and heat and low temperature impact resistance, good creep resistance, good dimensional stability, small molding shrinkage, and excellent processability And other excellent properties, it has been widely used in the home appliance industry and the automobile industry. In the home appliance industry, there are generally UL94V0 flame retardant requirements. The flame retardant performance of ABS resin itself is relatively poor. For this reason, various methods are used at home and abroad to improve the flame retardant performance of ABS. Among them, the method of adding flame retardants to ABS resin is the most mature and effecti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L55/02C08L25/12C08K3/04C08K3/38C08K3/22C08K3/24C08J3/22
Inventor 魏绪英周霆罗明华辛敏琦
Owner SHANGHAI KUMHO SUNNY PLASTICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com