Double-layer reaction glaze and producing method thereof

A reactive glaze and double-layer technology, which is applied in the field of double-layer reactive glaze and its production, can solve the problem that the surface glaze cannot show patterns and other problems

Inactive Publication Date: 2014-07-30
LILING HUAWANG CERAMICS MFG
View PDF3 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing technology cannot well control the pattern to be presented, and even cause it to fail to present the pattern on the glaze

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A double-layer reactive glaze has a bottom glaze and a top glaze, and the components and parts by weight of the bottom glaze are as follows:

[0030] 30 parts of feldspar powder; 15 parts of quartz powder;

[0031] 5 parts of calcite; 3 parts of low-temperature frit;

[0032] 5 parts of kaolin; 2 parts of zinc oxide;

[0033] 5 parts of iron oxide;

[0034] The components and parts by weight of the described top glaze are as follows:

[0035] 20 parts of low-temperature frit; 10 parts of quartz powder;

[0036] 15 parts of calcite; 5 parts of zinc oxide; 4 parts of dolomite;

[0037] 4 parts of kaolin; 8 parts of pigment.

[0038] A kind of preparation method of double-layer reaction glaze, its steps are as follows:

[0039] (1) Prepare the bottom glaze and surface glaze according to the above components and parts by weight of each component:

[0040] (2) Bottom glaze according to bottom glaze: ball: water = 1: 1.5: 0.5, wet ball milling for about 13 hours, after...

Embodiment 2

[0044] A double-layer reactive glaze has a bottom glaze and a top glaze, and the components and parts by weight of the bottom glaze are as follows:

[0045] 50 parts of feldspar powder; 20 parts of quartz powder;

[0046] 12 parts of calcite; 5 parts of low-temperature frit;

[0047] 15 parts of kaolin; 8 parts of zinc oxide;

[0048] 20 parts of manganese carbonate;

[0049] The components and parts by weight of the described top glaze are as follows:

[0050] 45 parts of low-temperature frit; 20 parts of quartz powder;

[0051] 8 parts of calcite; 10 parts of zinc oxide; 8 parts of dolomite;

[0052] 12 parts of kaolin; 30 parts of pigment.

[0053] A kind of preparation method of double-layer reaction glaze, its steps are as follows:

[0054] (1) Prepare the bottom glaze and surface glaze according to the above components and parts by weight of each component:

[0055] (2) Bottom glaze: Bottom glaze material: ball: water = 1︰1.5︰0.5, wet ball milling for about 15 hou...

Embodiment 3

[0059] A double-layer reactive glaze has a bottom glaze and a top glaze, and the components and parts by weight of the bottom glaze are as follows:

[0060] 40 parts of feldspar powder; 18 parts of quartz powder;

[0061] 8 parts of calcite; 4 parts of low temperature frit;

[0062] 10 parts of kaolin; 5 parts of zinc oxide;

[0063] 13 parts of manganese carbonate;

[0064] The components and parts by weight of the described top glaze are as follows:

[0065] 33 parts of low-temperature frit; 15 parts of quartz powder;

[0066] 11 parts of calcite; 8 parts of zinc oxide; 6 parts of dolomite;

[0067] 8 parts of kaolin; 19 parts of pigment.

[0068] A kind of preparation method of double-layer reaction glaze, its steps are as follows:

[0069] (1) Prepare the bottom glaze and surface glaze according to the above components and parts by weight of each component:

[0070] (2) Bottom glaze: Bottom glaze material: ball: water = 1︰1.5︰0.5, wet ball milling for about 15 hours...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a double-layer reaction glaze and a producing method thereof. The double-layer reaction glaze comprises a ground-coat glaze and a cover-coat glaze. The ground-coat glaze comprises the following components in parts by weight: 30 parts-50 parts of a feldspar powder, 15 parts-20 parts of a quartz powder, 5 parts-12 parts of calcite, 3 parts-5 parts of low-temperature frits, 5 parts-15 parts of kaolin, 2 parts-8 parts of zinc oxide, and 5 parts-20 parts of manganese carbonate or iron oxide. The cover-coat glaze comprises the following components in parts by weight: 20 parts-45 parts of low-temperature frits, 10 parts-20 parts of a quartz powder, 8 parts-15 parts of calcite, 5 parts-10 parts of zinc oxide, 4 parts-8 parts of dolomite, 4 parts-12 parts of kaolin, and 8 parts-30 parts of a pigment. The double-layer reaction glaze can present a quite good pattern-flowing effect, so that decoration is rich and colorful, and is the most changeful.

Description

technical field [0001] The invention relates to a double-layer reactive glaze and a preparation method thereof. Background technique [0002] At present, in the ceramic industry, the shape of porcelain blanks is the basis of high-quality products. The deployment of glazes makes porcelain more dazzling. Porcelain blanks of the same shape often have different effects on consumers' vision due to different glazes. Driven by the tide of modern civilization, people's expectations and pursuit of the aesthetic level of ceramic products are becoming stronger and stronger. Ceramic products with different patterns make the field of ceramic effects more colorful. However, the existing technology cannot well control the pattern to be presented, and even cause it to fail to present the pattern on the glaze. Contents of the invention [0003] The technical problem to be solved by the present invention is to overcome the defects of the prior art and provide a double-layer reactive glaze,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B41/86C04B41/89
Inventor 谢浩飞廖虎钟建发
Owner LILING HUAWANG CERAMICS MFG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap