A kind of monodisperse polar heterogeneous janus core-shell structure gel microsphere and its preparation method and used microfluidic control device

A technology with opposite polarity and core-shell structure, which is applied in the direction of microsphere preparation, microcapsule preparation, chemical instruments and methods, etc., to achieve the effects of high yield, uniform particle size and simple method

Inactive Publication Date: 2016-01-20
UNIV OF SCI & TECH OF CHINA
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, there is no report on the successful preparation of such microspheres at home and abroad.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of monodisperse polar heterogeneous janus core-shell structure gel microsphere and its preparation method and used microfluidic control device
  • A kind of monodisperse polar heterogeneous janus core-shell structure gel microsphere and its preparation method and used microfluidic control device
  • A kind of monodisperse polar heterogeneous janus core-shell structure gel microsphere and its preparation method and used microfluidic control device

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] Mix 19.2g TPGDA and 0.8g HCPK, dissolve with magnetic stirring, and make a non-polar dispersed phase solution.

[0050] Take 2g of acrylamide, 0.3g of bisacrylamide, 0.1g of ammonium persulfate, mix them, add 0.1g of sodium dodecylbenzenesulfonate (SDBS), add water to 20g, stir and dissolve with magnetic force, and make polar dispersions respectively. phase solution and polar nucleation phase solution.

[0051] The above-mentioned polar dispersed phase solution, polar nucleation phase solution and non-polar dispersed phase solution were respectively filled into 1 mL syringes, placed on corresponding syringe pumps, and connected to microfluidic control devices. Then take simethicone as the continuous phase solution and place it in a 20mL continuous phase syringe, install it on the continuous phase syringe pump, and connect it to the microfluidic control device. Set the flow rate of the polar dispersed phase solution to 2 μL min -1 , the flow rate of the non-polar dispe...

Embodiment 2

[0054] Mix 19.2g TPGDA and 0.8g HCPK, dissolve with magnetic stirring, and make a non-polar dispersed phase solution.

[0055] Take 2g of acrylamide, 0.3g of bisacrylamide, 0.1g of ammonium persulfate, mix them, add 0.1g of sodium dodecylbenzenesulfonate (SDBS), add water to 20g, stir and dissolve with magnetic force, and make polar dispersions respectively. phase solution and polar nucleation phase solution.

[0056] The above-mentioned polar dispersed phase solution, polar nucleation phase solution and non-polar dispersed phase solution were respectively filled into 1 mL syringes, placed on corresponding syringe pumps, and connected to microfluidic control devices. Then take simethicone as the continuous phase solution and place it in a 20mL continuous phase syringe, install it on the continuous phase syringe pump, and connect it to the microfluidic control device. Set the flow rate of the polar dispersed phase solution to 2 μL min -1 , the flow rate of the non-polar dispe...

Embodiment 3

[0059] Mix 19.2g TPGDA and 0.8g HCPK, dissolve with magnetic stirring, and make a non-polar dispersed phase solution.

[0060] Take 2g of acrylamide, 0.3g of bisacrylamide, 0.1g of ammonium persulfate, mix them, add 0.1g of sodium dodecylbenzenesulfonate (SDBS), add water to 20g, stir and dissolve with magnetic force, and make polar dispersions respectively. phase solution and polar nucleation phase solution.

[0061] The above-mentioned polar dispersed phase solution, polar nucleation phase solution and non-polar dispersed phase solution were respectively filled into 1 mL syringes, placed on corresponding syringe pumps, and connected to microfluidic control devices. Then take simethicone as the continuous phase solution and place it in a 20mL continuous phase syringe, install it on the continuous phase syringe pump, and connect it to the microfluidic control device. Set the flow rate of the polar dispersed phase solution to 2 μL min -1 , the flow rate of the non-polar dispe...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a single-dispersity and opposite-polarity Janus gel microsphere with a core-shell structure, a preparation method and a microfluid control device used. The preparation method is characterized by comprising the following steps that two types of polar and non-polar dispersed phase solution, polar core-forming phase solution and continuous phase solution are prepared; firstly under the shearing action of the non-polar dispersed phase solution, the polar core-forming phase forms polar core drops in the non-polar dispersed phase solution; then under the shearing action of the non-polar dispersed phase solution, the polar dispersed phase solution and the non-polar dispersed phase solution are contacted to form two semispherical Janus drops with different polarities; and at the moment, the non-polar semispheres contain the polar core drops. The single-dispersity and opposite-polarity Janus gel microsphere disclosed by the invention has the advantages that the flow of the core-forming phase solution is controlled, the polar cores in the non-polar parts of the opposite-polarity Janus drops with the core-shell structures can be controlled; the flow ratio of the polar dispersed phase to the non-polar dispersed phase is controlled, so that the appearance of the opposite-polarity Janus drops with the core-shell structures can be controlled; the single-dispersity and opposite-polarity Janus gel microsphere with the size range being 500-600mum and the dispersion coefficient CV being less than 3% can be obtained by curing the drops.

Description

technical field [0001] The invention relates to the field of preparation of polar heterogeneous Janus core-shell structure gel microspheres, in particular to a monodisperse polar heterogeneity Janus core-shell structure microspheres with controllable morphology and core quantity, its preparation method and the device used . Background technique [0002] Janus particles refer to asymmetric particles that contain two different chemical compositions or have different properties on the surface, which are manifested in the differences in mechanical properties, magnetic properties, optical properties, electrical properties, and surface hydrophilic and hydrophobic properties (polarity) on both sides of the particles. Due to the asymmetric nature of the two parts, Janus particles have an additional directional force, and with the help of this directional force, the spatial assembly of particles can be realized. Due to the new ideas brought by the special physical and chemical prope...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J13/02B01J19/00
Inventor 常振旗吴林军
Owner UNIV OF SCI & TECH OF CHINA
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com