Electron radiation cross-linked polyolefin pearl foam and preparation method thereof

A technology of cross-linking polyolefin and electron radiation, applied in chemical instruments and methods, layered products, synthetic resin layered products, etc., to achieve the effects of excellent heat insulation, smooth and delicate surface, and light weight

Active Publication Date: 2014-06-11
HUBEI XIANGYUAN NEW MATERIAL TECH INC
View PDF3 Cites 26 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, there is no electron radiation crosslinked polyolefin pearlescent foam material in the market

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0047] A sort of The preparation method of electron radiation crosslinked polyolefin pearlescent foam comprises the following steps:

[0048] The first step: preparation of foam masterbatch:

[0049] Take 60-80Kg low-density polyethylene resin (LDPE), 20-26Kg AC foaming agent, 5-8Kg talcum powder, 1-2Kg polyethylene wax (PE wax), 1-2Kg zinc stearate, 0.8-1Kg antioxidant Add agent 1010, 0.8-1Kg antioxidant 168, 2-3Kg No. 10 white oil into a high-speed mixer, knead at room temperature for 3-5 minutes, and then discharge into a two-stage mixing and granulating machine for mixing and granulation to obtain Foam masterbatch. The working temperature of the two-stage mixing and granulating machine is: 85±5℃ in the first zone, 95±5℃ in the second zone, 100±5℃ in the third zone, 110±5℃ in the fourth zone, 115±5℃ in the fifth zone, and 115±5℃ in the sixth zone. 100±5°C.

[0050] The second step: preparation of flame retardant masterbatch:

[0051] Take 40-60Kg ethylene-vinyl acetate...

Embodiment 1

[0064] Example 1: The preparation method of electron radiation crosslinked polyolefin pearlescent foam, the preparation method comprises the following steps in sequence:

[0065] The first step: preparation of foam masterbatch:

[0066] Get 60Kg low-density polyethylene resin (LDPE), 20KgAC foaming agent, 5Kg talcum powder, 1Kg polyethylene wax (PE wax), 1Kg zinc stearate, 0.8Kg antioxidant 1010, 0.8Kg antioxidant 168, 2Kg10 No. white oil was added to a high-speed mixer, kneaded at room temperature for 5 minutes, and then discharged into a two-stage mixing and granulating machine for mixing and granulation to obtain foam masterbatches. The working temperature of the two-stage mixing and granulating machine is: 85°C in the first zone, 95°C in the second zone, 100°C in the third zone, 110°C in the fourth zone, 115°C in the fifth zone, and 100°C in the sixth zone.

[0067] The second step: preparation of flame retardant masterbatch:

[0068] Get 40Kg ethylene-vinyl acetate co...

Embodiment 2

[0083] Step 1: Take 80Kg low-density polyethylene resin (LDPE), 26Kg AC foaming agent, 8Kg talcum powder, 2Kg polyethylene wax (PE wax), 2Kg zinc stearate, 1Kg antioxidant 1010, 1Kg antioxidant 168 1. Add 3Kg No. 10 white oil into a high-speed mixer, knead at room temperature for 3 minutes, and then discharge it into a two-stage mixing and granulating machine for mixing and granulation to obtain foam masterbatches. The working temperature of the two-stage mixing and granulating machine is: 80°C in the first zone, 90°C in the second zone, 95°C in the third zone, 105°C in the fourth zone, 112°C in the fifth zone, and 95°C in the sixth zone.

[0084] The second step: take 60Kg ethylene-vinyl acetate copolymer (EVA), 30Kg linear low-density polyethylene (LLDPE), 100Kg flame retardant magnesium hydroxide, 30Kg flame retardant zinc borate, 20Kg flame retardant ammonium octamolybdate , 4Kg polyethylene wax (PE wax), 1Kg antioxidant 1010, 1Kg antioxidant 168, 3Kg No. 10 white oil, 2Kg...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Tensile strengthaaaaaaaaaa
Average cell diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to polyolefin pearl foam and a preparation method thereof. The method comprises the following steps: (1) preparing foaming master batch; (2) preparing flame retardant master batch; (3) preparing calcium carbonate filler master batch; (4) adding raw materials into a high-speed mixer to prepare an ingredient 1; (5) adding raw materials into the high-speed mixer to prepare an ingredient 2; (6) performing double-layer composite extruding: adding the ingredient 1 and the ingredient 2 into a hopper of a double-layer composite sheet extruder to extrude into double-layer composite sheets; (7) performing radiation crosslinking of the composite sheets; (8) foaming the composite sheets; (9) cutting the composite sheets to obtain a finished product. The polyolefin pearl foam prepared by using the method has the advantages of good luminescence effect, easily available raw materials and low preparation cost.

Description

technical field [0001] The invention relates to a polyolefin pearlescent foam and a preparation method thereof, in particular to an electron radiation crosslinked polyolefin pearlescent foam with good luminous effect, easy preparation of raw materials and low preparation cost and a preparation method thereof. Background technique [0002] In order to protect our company's foam series products and improve product appearance, our company has prepared and invented an electronic radiation cross-linked polyolefin pearlescent foam material with anti-counterfeiting effect and beautiful appearance. [0003] Electron radiation cross-linked polyolefin foam sheet, that is, IXPE (Irradiation crossicked polyethylene foam) foam material, is a polyolefin polymer and various additives blended and extruded, cross-linked by electron accelerator radiation, high temperature foaming Polymer foam material made by technology. At present, there are many kinds of products on the market, but there i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08J9/10C08J3/28C08J3/24C08J3/22B32B27/06B32B27/16B32B27/18B32B27/32B29C69/00B29C47/92B29C47/06B29C71/04B29B9/06B29C48/92B29C48/08B29C48/875
CPCB29B7/726B29B9/06B29C48/875B29C48/92B29C2948/92704B29C48/08B29C48/0022B29C2948/92561B29C2948/92828B29C2948/92895B29C2948/92923
Inventor 魏琼
Owner HUBEI XIANGYUAN NEW MATERIAL TECH INC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com