Graphene/carbon black composite material, preparation method and application thereof

A composite material and graphene technology, applied in the field of electrochemical materials, can solve the problems of easy agglomeration of graphene sheets, unusable energy storage, and low energy storage capacity of graphene, and achieve easy operation, high energy storage capacity, and process simple effect

Inactive Publication Date: 2014-06-04
OCEANS KING LIGHTING SCI&TECH CO LTD +2
View PDF4 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] As a two-dimensional monolayer material, graphene has a high specific surface area and high electrical conductivity. It is an ideal electrode material for electrochemical capacitors. However, graphene sheets are easy to agglomerate, resulting in many graphene sheets. The surface cannot be used for energy storage, so the energy storage capacity of graphene is not high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0026] The preparation method of the composite electrode material adopts an oxidation-reduction method, and the equipment and process are simple, easy to operate, and easy to realize large-scale industrial production.

[0027] The graphene / carbon black composite material prepared by the above preparation method comprises 50%-85% graphene and 15%-50% carbon black according to the mass ratio. The graphene / carbon black composite material has relatively low agglomeration of graphene sheets, so that the composite material has a high energy storage capacity when used as an electrode material of an electrochemical capacitor.

[0028] The following are the applications of graphene / carbon black composites

[0029] Graphene / carbon black composite materials are generally used as electrode materials for electrochemical capacitors. The following describes how to use this material to make electrochemical capacitors.

[0030] First, according to the mass ratio of 95:5, the graphene / carbon b...

Embodiment 1

[0036] The present invention prepares the technological process of graphene / carbon black composite material as follows:

[0037] Graphite → graphite oxide → graphene oxide / carbon black composite → graphene / carbon black composite

[0038] (1) Graphite: 99.5% purity;

[0039] (2) Graphite oxide: Weigh 1g of graphite with a purity of 99.5% in (1) and add it to a mixed solution consisting of 90ml of concentrated sulfuric acid (98% by mass fraction) and 25ml of concentrated nitric acid (65% by mass fraction). Place in an ice-water mixed bath environment and stir for 20 minutes, then slowly add 6g of potassium permanganate to the mixture, stir for 1 hour, then heat the mixture to 85°C and keep it for 30 minutes, then add 92ml of deionized water Continue to keep at 85°C for 30 minutes, finally add 10ml of hydrogen peroxide solution (mass fraction 30%), stir for 10 minutes, filter the mixture with suction, and then use 100ml of dilute hydrochloric acid and 150ml of deionized water to...

Embodiment 2

[0043] The present invention prepares the technological process of graphene / carbon black composite material as follows:

[0044] Graphite → graphite oxide → graphene oxide / carbon black composite → graphene / carbon black composite

[0045] (1) Graphite: 99.5% purity;

[0046](2) Graphite oxide: Weigh 5g of graphite with a purity of 99.5% in (1) and add it to a mixed solution consisting of 475ml of concentrated sulfuric acid (98% by mass fraction) and 120ml of concentrated nitric acid (65% by mass fraction). Place in an ice-water mixed bath environment and stir for 20 minutes, then slowly add 20g of potassium permanganate to the mixture, stir for 1 hour, then heat the mixture to 85°C and keep it for 30 minutes, then add 92ml of deionized water Continue to keep at 85°C for 30 minutes, finally add 30ml of hydrogen peroxide solution (mass fraction 30%), stir for 10 minutes, filter the mixture with suction, and then use 300ml of dilute hydrochloric acid and 450ml of deionized water ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the field of electrochemical materials, and discloses a graphene / carbon black composite material, a preparation method and an application thereof. The electrode material comprises, by mass, 50-85% of graphene and 15-50% of carbon black. According to the graphene / carbon black composite material, agglomeration of the graphene lamellas is low, such that the high energy storage capacity is provided when the composite material is adopted as the electrochemical capacitor electrode material.

Description

technical field [0001] The invention relates to the field of electrochemical materials, in particular to a graphene / carbon black composite material and its preparation method and application. Background technique [0002] As a new type of energy storage device, electrochemical capacitor is another energy storage device with great application potential and development value after lithium-ion batteries due to its fast charge and discharge rate, high power density, and long cycle life. However, low energy density is a key factor restricting the development and application of supercapacitors, and exploring how to increase the energy density of supercapacitors is the focus of current research in this field. According to the calculation formula of energy density , improving the energy density mainly starts from two aspects, one is to increase the voltage window of the electrochemical capacitor; the other is to increase the specific capacity of the electrode material. [0003] A...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C01B31/04C01B31/02H01G9/042C01B32/05C01B32/19
CPCY02E60/13
Inventor 周明杰钟辉王要兵刘大喜
Owner OCEANS KING LIGHTING SCI&TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com