maraging steel

A maraging steel, Vickers hardness technology, applied in the direction of V-belt, coating, belt/chain/gear, etc., can solve the problem of insufficient strength, and achieve excellent mechanical properties, high strength and fatigue strength properties , the effect of long fatigue life

Active Publication Date: 2016-08-17
HITACHI METALS LTD
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In response to such a high demand, the strength of the conventional maraging steel of the above-mentioned second method is not necessarily sufficient, and it is required to achieve more excellent fatigue strength and stable high strength

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • maraging steel
  • maraging steel
  • maraging steel

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0086] The present invention will be described in more detail using the following examples.

[0087] Seven kinds of steel ingots weighing 10 kg were produced using a vacuum induction melting furnace. In order to more reliably prevent contamination of Ti, Nb, Ta, and W, elements that should be restricted, high-purity alloy raw materials are used as the alloy raw materials to be added.

[0088] Homogenizing annealing was performed on the produced steel ingot, and then hot forging was performed. Then, it is made into maraging steel with a thickness of about 0.2mm by hot rolling and cold rolling, which is used as the maraging steel for the metal endless belt of CVT.

[0089] Table 1 shows the chemical composition and Al / Ti ratio of the obtained maraging steel. The content of C in all the maraging steels was adjusted to a range of 0.008% or less, thereby preventing a decrease in weldability. In addition, the Al content of the maraging steels No. 1, No. 2, and No. 7 exceeded the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
hardnessaaaaaaaaaa
hardnessaaaaaaaaaa
Login to View More

Abstract

The present invention provides a maraging steel which has excellent fatigue strength after nitriding and can obtain stable high strength. A maraging steel containing C: 0.008% or less, Si: 0.5% or less, Mn: 0.5% or less, Cr: 0.5%-1.5%, Ni: 16.0%-22.0%, Co: 3.0% to 7.0%, Mo: 3.0% to 7.0%, the thickness is less than 0.5mm, and has been subjected to nitriding treatment. The maraging steel also contains Al: 0.6% to 1.3% by mass percentage, and the rest Composed of Fe and impurities, as the above-mentioned impurities, Ti: 0.01% or less, Nb: 0.01% or less, Ta: 0.01% or less, W: 0.01% or less, and the ratio of Al to Ti satisfies Al / Ti≥250, According to Vickers hardness, the surface hardness of maraging steel is 800HV-1050HV, and the internal hardness is 570HV or less.

Description

technical field [0001] The present invention relates to a nitriding-treated maraging steel suitable for, for example, a metal endless belt for a CVT (Continuously Variable Transmission). Background technique [0002] Maraging steel has a very high tensile strength of about 2000 MPa. Therefore, for example, maraging steel can be processed into a steel strip of 0.5 mm or less, and used for metal endless belts requiring high strength in CVTs. [0003] In a typical composition of a maraging steel, 18% by mass % of Ni, 8% of Co, 5% of Mo, 0.45% of Ti, 0.1% of Al, and the balance is Fe. [0004] However, although the above-mentioned maraging steel can obtain very high tensile strength, its fatigue strength is not necessarily high. TiN inclusions are cited as the biggest cause of the decrease in the fatigue strength of maraging steel. The size of the TiN inclusions tends to be large, and the shape is also cubic, so fatigue fracture originating from the inclusions tends to occur. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/00C22C38/52C22C38/54C23C8/26
CPCC22C38/52C22C38/54C22C38/001C22C38/002C22C38/004C22C38/02C22C38/04C22C38/06C22C38/44C22C38/50C21D6/001F16G5/16C23C8/26
Inventor 大石胜彦上原利弘岸上一郎
Owner HITACHI METALS LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com