Chlorosulfonated polyethylene compound for power steering pipe and preparation method thereof

A technology of chlorosulfonated polyethylene and power steering tubes, which is applied in the field of synthetic rubber, can solve the problems that the qualified rate of products cannot meet the development needs, and achieve shortening of mixing time, elimination of vibration transmission, good elongation at break and The effect of resilience

Active Publication Date: 2016-04-06
浙江久运汽车零部件有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Since the connecting pipe in the power steering gear belongs to the high-pressure series and has been in contact with the fuel for a long time, its stability and reliability are related to the safety of the car and the person, so its technical content and standard requirements are getting higher and higher. However, the current Power steering hose products are far from meeting people's development needs for the modern automobile industry in terms of heat resistance, oil resistance, pressure resistance, aging resistance, pulse performance, product qualification rate and cost.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] The main raw materials are formulated according to the following proportions by weight:

[0044] Chlorosulfonated polyethylene rubber 100 parts, carbon black 55 parts, reinforcing agent GC66625 parts, stearic acid 0.5 parts, flow agent WB2121 parts, C9 petroleum resin 5 parts, acid absorbing agent 15 parts, plasticizer TOTM 15 parts, anti-aging 1.8 parts of agent, WS1802 parts of internal release agent, 5 parts of vulcanizing agent BIPB, and 6 parts of crosslinking auxiliary agent Activator-70P.

[0045] The concrete process step of preparation method is:

[0046]1) Material preparation: Weigh 100 parts by weight of chlorosulfonated polyethylene rubber, 30 parts by weight of carbon black N990, 25 parts by weight of carbon black N330, 25 parts by weight of reinforcing agent GC666, 0.5 parts by weight of stearic acid, The flow agent WB212 of 1 weight part, the C9 petroleum resin of 5 weight parts, the active magnesium oxide of 10 weight parts, the magnesium aluminum hydr...

Embodiment 2

[0051] The main raw materials are formulated according to the following proportions by weight:

[0052] Chlorosulfonated polyethylene rubber 100 parts, carbon black 50 parts, reinforcing agent GC66630 parts, stearic acid 0.4 parts, flow agent WB2121.2 parts, C9 petroleum resin 3 parts, acid absorbing agent 18 parts, plasticizer TOTM 19 parts , 1.5 parts of anti-aging agent, 1.5 parts of internal release agent WS180, 4 parts of vulcanizing agent BIPB, and 7 parts of cross-linking auxiliary agent Activator-70P.

[0053] The concrete process step of preparation method is:

[0054] 1) Material preparation: Weigh 100 parts by weight of chlorosulfonated polyethylene rubber, 28 parts by weight of carbon black N990, 22 parts by weight of carbon black N330, 30 parts by weight of reinforcing agent GC666, 0.4 parts by weight of stearic acid, The flow agent WB212 of 1.2 parts by weight, the C9 petroleum resin of 3 parts by weight, the active magnesium oxide of 12 parts by weight, the mag...

Embodiment 3

[0059] The main raw materials are formulated according to the following proportions by weight:

[0060] Chlorosulfonated polyethylene rubber 100 parts, carbon black 60 parts, reinforcing agent GC66620 parts, stearic acid 0.6 parts, flow agent WB2120.8 parts, C9 petroleum resin 7 parts, acid absorbing agent 11 parts, plasticizer TOTM 10 parts , 2.1 parts of anti-aging agent, 3 parts of internal release agent WS1803, 6 parts of vulcanizing agent BIPB, and 5 parts of cross-linking auxiliary agent Activator-70P.

[0061] The concrete process step of preparation method is:

[0062] 1) Material preparation: Weigh 100 parts by weight of chlorosulfonated polyethylene rubber, 32 parts by weight of carbon black N990, 28 parts by weight of carbon black N330, 20 parts by weight of reinforcing agent GC666, 0.6 parts by weight of stearic acid, 0.8 parts by weight of flow agent WB212, 7 parts by weight of C9 petroleum resin, 8 parts by weight of active magnesium oxide, 3 parts by weight of ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
adsorption capacityaaaaaaaaaa
tensile strengthaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to View More

Abstract

The invention discloses a sulfochlorination polyvinyl sizing material for a power steering pipe, and a preparation method thereof. The sulfochlorination polyvinyl sizing material comprises the following raw materials in parts by weight: 100 parts of chlorosulfonated polyethylene rubber, 50-60 parts of carbon black, 20-30 parts of a reinforcing agent GC666, 0.3-0.7 part of stearic acid, 0.8-1.2 parts of a flowable agent WB212, 3-7 parts of C9 petroleum resin, 11-19 parts of an acid accepter, 10-20 parts of a plasticiser TOTM, 1.4-2.2 parts of an antiager, 1-3 parts of an internal release agent WS180, 4-6 parts of a vulcanizator BIPB, and 5-7 parts of a crosslinking additive Activator-70P. The sulfochlorination polyvinyl sizing material is prepared by the steps of material preparation, seal smelting, cooling and open milling, and has the characteristics of high strength, low permanent compression set, low temperature resistance, aging resistance, oil resistance and the like, can completely meet the requirements of the power steering pipe, and meanwhile is nontoxic, flavourless and stable in storage.

Description

technical field [0001] The invention relates to the field of synthetic rubber, in particular to a chlorosulfonated polyethylene rubber material for a power steering pipe and a preparation method thereof. Background technique [0002] With the rapid development of the automobile industry, the application of power steering gears in automobile steering systems is becoming more and more common. Since the connecting pipe in the power steering gear belongs to the high-pressure series and has been in contact with the fuel for a long time, its stability and reliability are related to the safety of the car and the person, so its technical content and standard requirements are getting higher and higher. However, the current Power steering hose products are far from meeting people's development needs for the modern automobile industry in terms of heat resistance, oil resistance, pressure resistance, aging resistance, pulse performance, product qualification rate and cost. [0003] The...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/34C08L57/02C08K13/02C08K3/04C08K5/09C08K3/22C08K3/26C08K3/36C08K5/12B29B7/74
CPCB29B7/74C08K2201/014C08L23/34C08L2203/18C08L57/02C08K13/02C08K3/04C08K5/09C08K2003/222C08K2003/265
Inventor 魏新宝张利芳沈松泉
Owner 浙江久运汽车零部件有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com