A kind of UV nail phototherapy glue and preparation method thereof

A phototherapy glue and nail technology, applied in the field of UV nail phototherapy glue and its preparation, can solve the problems of containing formaldehyde and health hazards, and achieve the effects of good adhesion, good weather resistance and high gloss

Active Publication Date: 2016-11-23
广东神洲化学工业有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although this nail polish has a flash effect, it contains formaldehyde, etc., which is harmful to health

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of UV nail phototherapy glue and preparation method thereof
  • A kind of UV nail phototherapy glue and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1～4

[0025] Examples 1-4 are preparation examples of UV nail phototherapy glue, and the formulations (unit: kg) of Examples 1-4 are shown in Table 1.

[0026] Table 1

[0027]

[0028] The difunctional aliphatic urethane acrylic resin described in Table 1 can specifically adopt SM-582 produced by Shenzhen Sabis Technology Co., Ltd.; the hexafunctional aliphatic urethane acrylic resin can specifically adopt 6145-100 produced by Taiwan Changxing) .

[0029] The preparation method of the UV nail phototherapy glue of embodiment 1-4 all follows the steps:

[0030] Step 1, weigh each component by the formula of above table 1;

[0031] Step 2, put the monofunctional monomer and aliphatic polyurethane acrylic resin into the dispersion tank, and disperse at high speed for 10 to 15 minutes with a high-speed disperser;

[0032] Step 3, put in the leveling agent and disperse with a high-speed disperser for 10 to 15 minutes;

[0033] Step 4, put in photoinitiator, disperse with high-spee...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
Login to View More

Abstract

The invention provides an UV (Ultraviolet) nail phototherapy gel and a preparation method thereof. According to the formula, the phototherapy gel comprises the following components in percentage by mass: 40 to 50% of single functional monomer, 40 to 50% of aliphatic polyurethane acrylic resin, 8 to 11% of photoinitiator, 0.2 to 0.4% of flatting agent, and 0.1 to 0.2% of defoaming agent. The UV nail phototherapy gel shows an outstanding brightening effect with a coating, and also has the characteristics of being environmentally-friendly, convenient to coat, high in transparence, high in glossiness, natural, lightweight, high in toughness, no pungent smell, difficult to yellow and break, long in holding time, etc.

Description

technical field [0001] The invention relates to a UV glue coating, in particular to a UV nail phototherapy glue and a preparation method thereof. Background technique [0002] Ordinary nail polish contains a lot of chemical solvents such as toluene, ethyl acetate and alcohol, phthalates, formaldehyde, etc., which are harmful to health, and it is easy to fall off after drying, has a strong smell, and has low gloss retention. . [0003] The Chinese patent application with the publication number CN103479537 discloses a glittering nail polish. Its formula contains the following components: 20 grams of acetone, 15 grams of ethyl acetate, 75 grams of phthalate, 10 grams of Sudan red, 5 grams of formaldehyde, Glitter powder 25g. Although this nail polish has a flash effect, it contains formaldehyde, etc., which is harmful to health. Contents of the invention [0004] The purpose of the present invention is to make up for the deficiencies of the prior art, and to provide a UV n...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A61K8/895A61K8/87A61K8/81A61Q3/02
Inventor 周伟建刘化春王剑波卓少龙
Owner 广东神洲化学工业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More