Method for processing faux suede membrana dermalis coating

A coating treatment and suede technology, applied in the direction of coating, surface pretreatment, device for coating liquid on the surface, etc., can solve the problem of cracks easily caused by repeated bending of the coating film, so as to improve the dry and wet friction. Fastness, simple process, and the effect of improving the resistance to twisting and bending

Active Publication Date: 2015-04-01
DANDONG UNIK TEXTILE
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In the prior art, the suede-like dry film coating is directly coated with polyacrylate or polyurethane coating glue. Due to the hairiness on the surface of the suede, the coating film is thick, and the coating film is prone to appear after repeated bending during use. crack

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] (1) Preparation of film coating glue, weight ratio:

[0031] (1-1) Preparation of bottom coating:

[0032] Mix 100 parts of polyurethane resin with 0.5 parts of polyurethane thickener and stir evenly, then add 0.5 parts of melamine crosslinking agent and 5 parts of color paste, stir with a disperser to fully mix the liquid into the air to achieve a foaming state, and then add foam stabilizer 4 After one part is stirred evenly, add one part of foaming agent and stir evenly, so that the volume after foaming is increased by 1-1.5 times compared with that before adding foaming agent, and set aside;

[0033] (1-2) Preparation of surface coating:

[0034] Add 100 parts of cold-resistant matte coating glue, 5 parts of amino-modified polyorganosiloxane, 2 parts of melamine crosslinking agent, and 5 parts of color paste into the disperser in order to stir evenly, and set aside;

[0035] (2) Coating: direct coating by dry method;

[0036] (2-1) Coat (1-1) primer layer on the ...

Embodiment 2

[0039] (1) Preparation of film coating glue, weight ratio:

[0040] (1-1) Preparation of bottom coating:

[0041] Mix 100 parts of polyurethane resin with 0.7 parts of polyurethane thickener and stir evenly, then add 0.8 parts of melamine crosslinking agent and 5 parts of color paste, stir with a disperser to fully mix the liquid into the air to achieve a foaming state, and then add foam stabilizer 6 After one part is stirred evenly, add 1.5 parts of foaming agent and stir evenly, so that the volume after foaming is increased to 1.5-2 times relative to that before adding foaming agent, and set aside;

[0042] (1-2) Preparation of surface coating:

[0043] Add 100 parts of cold-resistant matte coating glue, 5 parts of amino-modified polyorganosiloxane, 1 part of melamine crosslinking agent, and 5 parts of color paste into the disperser in turn, stir evenly, and set aside;

[0044] (2) Coating: direct coating by dry method;

[0045] (2-1) Coat (1-1) primer layer on the suede...

Embodiment 3

[0048] (1) Preparation of film coating glue, weight ratio:

[0049] (1-1) Preparation of bottom coating:

[0050]Mix and stir 100 parts of polyurethane resin and 0.7 parts of polyurethane thickener evenly, then add 1 part of melamine crosslinking agent and 5 parts of color paste, stir with a disperser to fully mix the liquid into the air to achieve a foaming state, and then add foam stabilizer 8 After one part is stirred evenly, add 1.5 parts of foaming agent and stir evenly, so that the volume after foaming is increased to 1.5-2 times relative to that before adding foaming agent, and set aside;

[0051] (1-2) Preparation of surface coating:

[0052] Add 100 parts of cold-resistant matte coating glue, 10 parts of amino-modified polyorganosiloxane, 1 part of melamine crosslinking agent, and 5 parts of color paste into the disperser in order to stir evenly, and set aside;

[0053] (2) Coating: direct coating by dry method;

[0054] (2-1) Coat (1-1) bottom layer glue on the s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for processing a faux suede membrana dermalis coating. The method comprises the following steps: (1) bottom layer rubber coating preparation, namely, evenly stirring 100 parts of polyurethane resin, 0.5-1 part of polyurethane thickening agent, 0.5-2 parts of melamine cross-linking agents, 4-10 parts of foam stabilizers and 1-3 parts of foaming agents and increasing the foaming size to 1-3 times, (2) facial layer rubber coating preparation, namely, evenly stirring 100 parts of coldness-resistant lightless coating adhesive, 5-10 parts of amidogen modified polysiloxane, 0.5-2 parts of cross-linking agents and color paste, (3) adopting a dry method to coat directly, increasing the dry weight of the bottom layer rubber coating by 5-8g / m2, using a planishing mill for calendaring, and increasing the dry weight of the facial layer rubber coating by 7-10g / m2. The method is simple in technology and feasible, improves the distortion and bending resistance, elasticity and softness of fabric, improves dry-wet friction firmness, wear-resisting performance and coldness resistance of the fabric, and does not influence in index of the fabric.

Description

technical field [0001] The invention belongs to the technical field of finishing of textile fabrics, and specifically relates to a treatment method for a suede fabric coating, so as to improve the anti-distortion and bending performance of the suede fabric coating, and improve the softness, elasticity and durability of the product . Background technique [0002] In the textile industry, the fabric imitating the fur style of animal suede is called imitation suede. In the cloth market, suede has become a common name for various imitation suedes. The suede mentioned below is this kind of imitation suede. fleece fabric. Suede is a kind of fabric that uses natural fibers or natural fibers and superfine fibers to interweave cloth to make the surface of the fabric form a smooth and smooth hairiness style. Its unique style is very popular among consumers. [0003] Suede-like dry film coating is to use direct coating equipment to apply the coating glue on the surface of the fabric ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B05D1/38B05D3/02B05D3/12B05D7/24C09D175/08C09D183/04C09D7/12
Inventor 孟雅贤刘贝赵颖张迎春李晓霞李金华刘风兰韩庆
Owner DANDONG UNIK TEXTILE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap