Curable resin composition and reflective sheet

A curable resin and composition technology, applied in the field of reflective sheets, can solve the problems of flexible substrates, etc., and achieve the effects of excellent adhesion, excellent resolution, and excellent heat resistance

Active Publication Date: 2014-03-19
TAIYO HLDG CO LTD
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there is a problem that the cured product cannot be used for flexible substrates due to its brittleness.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Curable resin composition and reflective sheet
  • Curable resin composition and reflective sheet
  • Curable resin composition and reflective sheet

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0116] The present invention will be specifically described below by showing examples and comparative examples, but the present invention is not limited to the following examples.

[0117] Synthesis of resin solution 1:

[0118]Into a 2-liter detachable flask equipped with a stirrer, a thermometer, a reflux condenser, a dropping funnel, and a nitrogen inlet tube, 900 g of a solvent (diethylene glycol dimethyl ether), and 21.4 g of a polymerization initiator (tert-butyl 2-ethylhexanoate peroxide, manufactured by NOF Co., Ltd., trade name: Perbutyl O), heated to 90°C. After heating, 309.9 g of methacrylic acid, 116.4 g of methyl methacrylate, and 109.8 g of lactone-modified 2-hydroxyethyl methacrylate (manufactured by DAICEL CHEMICAL INDUSTRIES, LTD., commercial Name: PLACCEL FM1), and 21.4 g of a polymerization initiator (bis(4-tert-butylcyclohexyl)peroxydicarbonate, manufactured by NOF Corporation, brand name: PEROYL TCP). Further, by aging the mixture for 6 hours, a carboxy...

Embodiment （1））

[0121] Preparation of each curable resin composition (Examples 1-3, Comparative Examples 1-6):

[0122] The mixture in which each component was blended as described in Table 1 was stirred, and further dispersed by a three-roll mill to prepare curable resin compositions (Examples 1-3, Comparative Examples 1-6). In addition, Comparative Example 1 shows a composition in which the compounding amount of titanium oxide is less than the specified compounding amount of the present invention, Comparative Example 2 shows a composition in which the compounding amount of titanium oxide is larger than the specified compounding amount in the present invention, and Comparative Example 3 shows a composition as a light A composition containing only BAPO as a polymerization initiator, Comparative Example 4 shows a composition containing only MAPO as a photopolymerization initiator, and Comparative Example 5 shows a composition containing a photopolymerization initiator other than BAPO and MAPO a...

Embodiment （2））

[0162] Preparation of each curable resin composition (Examples 4-6, Comparative Examples 7-13):

[0163]The mixture in which each component was blended as described in Table 4 was stirred, and further dispersed in a three-roll mill to prepare curable resin compositions (Examples 4-6, Comparative Examples 7-13). In addition, Comparative Example 7 shows a composition without an antioxidant, Comparative Example 8 shows a composition in which a photopolymerizable monomer is added instead of urethane acrylate, and Comparative Example 9 shows a ratio of the compounding amount of titanium oxide to that specified in the present invention. A composition with a small compounding amount, Comparative Example 10 represents a composition in which the compounding amount of titanium oxide is larger than the compounding amount specified in the present invention, Comparative Example 11 represents a composition containing only BAPO as a photopolymerization initiator, and Comparative Example 12 re...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
acid valueaaaaaaaaaa
Login to View More

Abstract

A curable resin composition is provided which attains excellent resolution even when titanium oxide is contained therein in a large amount, and which gives a high-resolution cured object having a high reflectance. Also provided is a reflective sheet obtained from the composition. The curable resin composition is characterized by comprising a resin containing an ethylenically unsaturated group and a carboxy group in the molecule, a bisacylphosphine oxide photopolymerization initiator, a monoacylphosphine oxide photopolymerization initiator, titanium oxide, and an organic solvent.

Description

[0001] This application is a divisional application with the filing date of October 13, 2009, the application number 200980147621.X, and the title of the invention "curable resin composition and reflective sheet". technical field [0002] The present invention relates to a curable resin composition and a reflective sheet. [0003] Specifically, there are the following four types. [0004] One is a curable resin composition capable of forming a high-definition pattern even with a high reflectance, and a reflective sheet using the resin composition. [0005] The other is a curable resin composition capable of forming a high-definition pattern even with a high reflectance and obtaining a cured product having excellent adhesion to a difficult-to-adhesive thermoplastic substrate, and the use of the resin composition Reflective sheeting on difficult-to-bond thermoplastic substrates. [0006] The other is a curable resin composition capable of forming a high-definition pattern even...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): G03F7/029G03F7/033G03F7/038C08F283/00C08K3/22C08L63/00G02B1/04G02B5/08
CPCG03F7/029G03F7/105C08F283/008G03F7/033G02B1/04G03F7/0388C08L33/10C08L63/00B32B27/30C08K3/22
Inventor 能坂麻美角谷武德宇敷滋
Owner TAIYO HLDG CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com