Geopolymer-based inorganic artificial stone

A technology of artificial stone and geopolymer, applied in cement production and other directions, can solve the problems of easy fire or melting, high cost of artificial stone, and achieve the effect of green production process, low cost and good surface finish.

Inactive Publication Date: 2014-03-05
广西启利新材料科技股份有限公司
View PDF3 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a low-cost, natural and environmentally friendly material, rich source of raw materials, high hardness, waterproof, good weather resistance, high gloss, stable quality, simple preparation process, low requirements for production facilities, and green and environmentally friendly production process. Geopolymer-based inorganic artificial stone overcomes the shortcomings of traditional artificial stone that are prone to yellowing, deformation, aging, high cost, and prone to fire or melting when receiving heat radiation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] The raw materials of the geopolymer-based inorganic artificial stone according to the present invention are: 5% of water glass with a modulus of 1.5, 18% of slag powder, 70% of stone particles, 0.1% of pigment, and 0.1% of redispersible latex powder. , 1.5% fiber, 5.3% water, of which the composition of stone grains is 55% crushed stone, 20% broken glass, 5% natural colored sand, 10% broken ceramics, and 10% steel slag particles. Its preparation process is realized by the following process:

[0021] (1) Weigh various raw materials according to the proportion;

[0022] (2) Add various raw materials into the mixer and stir evenly, and the order of feeding can be in any order;

[0023] (3) Stir the slurry and pour it into the mold.

[0024] (4) After the slurry in the mold is flattened, use a 10MPa press to vibrate while pressing, and perform two extrusions to remove the gas in it. After the extrusion is completed, it will be cured together with the mold at a temperature...

Embodiment 2

[0026] The raw materials of the geopolymer-based inorganic artificial stone according to the present invention are as follows: 15% of water glass with a modulus of 1.8, 20% of slag powder, 60% of stone particles, 0.2% of pigment, and 0.2% of redispersible latex powder , 1.1% fiber, 3.5% water, of which the composition of stone grains is 50% crushed stone, 25% broken glass, 20% broken ceramics, and 5% steel slag particles. Its preparation process is realized by the following process:

[0027] (1) Weigh various raw materials in proportion;

[0028] (2) Add various raw materials into the mixer and stir evenly, and the order of feeding can be in any order;

[0029] (3) Stir the slurry and pour it into the mold.

[0030] (4) After the slurry in the mold is flattened, use a 10MPa press to vibrate while pressing, and perform two extrusions to remove the gas in it. After the extrusion is completed, it will be cured together with the mold at a temperature of 50°C for 2 hours to demou...

Embodiment 3

[0032] The raw materials of the geopolymer-based inorganic artificial stone according to the present invention are as follows: 10% of water glass with a modulus of 2.0, 15% of slag powder, 68% of stone particles, 0.2% of pigment, and 0.3% of redispersible latex powder , 3% fiber, and 3.5% water, of which the composition of stone particles is 80% crushed stone and 20% broken glass.

[0033] Its preparation process is realized by the following process:

[0034] (1) Weigh various raw materials in proportion;

[0035] (2) Add various raw materials into the mixer and stir evenly, and the order of feeding can be in any order;

[0036] (3) Stir the slurry and pour it into the mold.

[0037] (4) After the slurry in the mold is flattened, use a 10MPa press to vibrate while pressing, and perform two extrusions to remove the gas in it. After the extrusion is completed, it will be cured together with the mold at a temperature of 50°C for 2 hours to demould. Then the molding material is...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
modulusaaaaaaaaaa
Login to View More

Abstract

The invention relates to geopolymer-based inorganic artificial stone. The traditional artificial stone has the shortcomings of easy yellowing, deformation and aging, high cost, highly-possible fire or melting after receiving heat radiation and the like. The geopolymer-based inorganic artificial stone provided by the invention is prepared from the following raw materials in percentage by mass: 5-15% of water glass, 5-20% of superfine slag powder, 60-80% of stone particles, 0.1-0.3% of pigment, 0.1-0.5% of redispersible latex powder, 1-3% of fiber and 3-5% of water. The geopolymer-based inorganic artificial stone provided by the invention has the characteristics of stable structure, high strength, good wear resistance, environment-friendly raw materials, simple production process, low cost and high smooth finish, and is non-toxic and environment-friendly. Apart from low cost, high product hardness and good surface smoothness, the geopolymer-based inorganic artificial stone also has the advantages that the production process is simple and convenient, the raw materials are widely available, the production process is environment-friendly, and the raw materials are environment-friendly.

Description

technical field [0001] The invention relates to a geopolymer-based inorganic artificial stone, which belongs to the technical field of new materials. Background technique [0002] As a decorative material for interior and exterior decoration of buildings, floors and squares, stone is favored by the masses because of its high-end decoration, luxury, not easy to damage, good durability, and good cleanliness. my country is a large country of stone production, but stone is a natural resource and a non-recyclable resource. Due to long-term and large-scale mining, there are fewer and fewer mineral resources that can be used as stone. Therefore, using the scraps of stone mining to prepare artificial stone has become the development direction of stone. [0003] The main materials of traditional artificial stone are resin, crushed stone, pigment and other additives. Under a certain pressure, after the polymerization process of resin, it finally becomes a stone-like material. Under a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/26C04B14/06C04B14/02C04B14/48
CPCY02P40/10
Inventor 刘海锋巢启程峰黄承好高福欣
Owner 广西启利新材料科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com