Fast-curing indentation-proof water-based paint for galvanized sheet and preparation method thereof

A fast-curing, water-based coating technology, used in epoxy resin coatings, polyurea/polyurethane coatings, coatings, etc. Large-scale production, saving energy use, satisfying the effect of safe production

Inactive Publication Date: 2014-02-26
GUANGZHOU KINTE IND +1
View PDF8 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] There are several problems in the above-mentioned common coatings for galvanized sheets: inconvenient construction, high energy consumption, strict requirements on the construction environment, and all of them are solvent-based coatings, VOC emissions are not conducive to the development of green products
However, the galvanized sheet is bulky, and if it is baked at high temperature, the energy cost will be high, and the high temperature in the assembly of the kit may cause the kit to melt and deform, resulting in defective products
Although the water-based two-component system can be cross-linked at low temperature, the reaction speed is slow, and it is inconvenient to use and the cost is high, so it is difficult to adapt to the requirements of the existing fast production line

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fast-curing indentation-proof water-based paint for galvanized sheet and preparation method thereof
  • Fast-curing indentation-proof water-based paint for galvanized sheet and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0038]Some specific examples are listed below to illustrate the present invention. It should be pointed out that the following specific examples are only used to further illustrate the present invention, and do not represent limitations to the protection scope of the present invention. Some non-essential modifications and adjustments made by others according to the present invention still belong to the protection scope of the present invention.

[0039] The composition of the water-based coatings of Examples 1 to 4 is shown in Table 1. The preparation method is as follows: add 1 / 3 of the deionized water to the stirring tank, add the dispersant while stirring, then add 1 / 3 of the defoamer, add all the Pigment fillers are finally dispersed at high speed for 20 minutes, transferred to a sand mill and ground to a fineness of less than 15 microns.

[0040] (2) Add water-based resin, wetting and leveling agent, thixotropic agent, anti-flash corrosion agent, film-forming aid, remaini...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a fast-curing indentation-proof water-based paint for galvanized sheets. A formula of the paint comprises the following components by weight: 30-45% of water-based resin, 1-3% of a dispersant, 20-35% of a pigment filler, 0.3-1% of a wetting leveling agent, 0.5-1% of a thixotropic agent, 0.3-1% of a defoaming agent, 0.1-0.8% of a flash rust inhibitor, 1-3% of a coalescing agent, 0.1-0.5% of a pH regulator and 10-40% of deionized water. The invention also discloses a preparation method of the water-based paint. The paint film provided by the invention can cure fast, and is safe, energy-saving, environment-friendly and simple for construction, so as to meet the fast production requirements of an assembly line. The obtained galvanized sheet has excellent properties and performance indicators reaching the industrial standard for galvanized sheet coating.

Description

technical field [0001] The invention relates to a water-based paint, in particular to a fast-curing indentation-resistant water-based paint for galvanized sheets. The invention also relates to a method for preparing the coating. Background technique [0002] Galvanizing is an economical and effective steel plate corrosion protection method that is often used. About half of the world's zinc production is used in this process. In order to prevent the surface of the steel plate from being corroded and prolong its service life, a layer of metal zinc is coated on the surface of the steel plate, and the metal zinc on the surface can play a certain anti-corrosion effect. However, the galvanized layer on the surface of ordinary galvanized sheet is very thin, only 40g / m 2 Left and right, it will soon be damaged by corrosion in a relatively serious industrial corrosion environment. For this reason, the surface of galvanized sheet often needs to be coated to achieve anti-corrosion ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/00C09D163/10C09D175/14C09D7/12
Inventor 禹汉文许奕祥姚煌谢唯张红
Owner GUANGZHOU KINTE IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products