Eureka AIR delivers breakthrough ideas for toughest innovation challenges, trusted by R&D personnel around the world.

High-temperature underwater sound transmission rubber material and preparation method thereof

A sound-transmitting rubber and high-performance technology, applied in the field of preparation of high-performance underwater sound-transmitting rubber materials, can solve problems such as difficulty in having high water tightness, and achieve excellent physical and mechanical properties, high sound permeability and temperature stability, The effect of strong physical and mechanical properties

Active Publication Date: 2015-07-15
BEIJING UNIV OF CHEM TECH
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in order to ensure the high sound permeability of the material, the thickness is generally 2-4mm, and it is difficult for the rubber material to have high water tightness under such a thickness.
Again no temperature sensitivity issues related to neoprene

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-temperature underwater sound transmission rubber material and preparation method thereof
  • High-temperature underwater sound transmission rubber material and preparation method thereof
  • High-temperature underwater sound transmission rubber material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-5

[0029] Embodiment 1-5: A high-performance underwater sound-permeable rubber material, characterized in that: the parts by weight of each raw material are composed of:

[0030] Neoprene (CR322)

100 copies

Butadiene rubber (BR9000)

100 copies

Zinc oxide

5 copies

Zinc oxide

5 copies

lead oxide

5 copies

stearic acid

1 copy

Accelerator NA-22

1.5 servings

Accelerator PZ

1.5 servings

Accelerator M

0.5 parts

Accelerator CZ

2 copies

Accelerator TT

0.5 parts

Antiager D

2 copies

Antiager D

2 copies

DOP

12 copies

clay

5 copies

Coumarone resin

5 copies

Carbon black N330

30 copies

Carbon black N330

30 copies

Aromatic oil

10 copies

sulfur

1 copy

[0031] The neoprene and butadiene rubber are plasticized at room temperature with a double-roller mill respectively, and after passing the rolls for 3 ...

Embodiment 6-7

[0035] Embodiment 6-7: A high-performance underwater sound-permeable rubber material, characterized in that: the parts by weight of each raw material are composed of:

[0036] Neoprene (CR121, CR321) *

[0037] Note * , the combination of CR (CR121) and BR in the above formula is recorded as Example 6; the combination of CR-322 and BR is recorded as Example 7; the combination ratio of CR and BR is 70 / 30.

[0038] Preparation method: According to the preparation method of Example 1, a sound-permeable rubber sample was made, and its properties were tested as follows:

[0039] indicators

[0040] The sound-permeable material of the present invention can be used as a cladding material for underwater detection devices such as ship underwater acoustic equipment and seabed oil exploration equipment.

Embodiment 8-11

[0041] Embodiment 8-11: A high-performance underwater acoustic sound-permeable rubber material, characterized in that: the parts by weight of each raw material are composed of:

[0042] Neoprene (CR122)

100 copies

Butadiene rubber (BR9000)

100 copies

Zinc oxide

5 copies

Zinc oxide

5 copies

lead oxide

5 copies

stearic acid

1 copy

Accelerator NA-22

1.5 servings

Accelerator PZ

1.5 servings

Accelerator M

0.5 parts

Accelerator CZ

2 copies

Accelerator TT

0.5 parts

Antiager D

2 copies

Antiager D

2 copies

DOP

12 copies

clay

1, 2, 8, 10 copies

Coumarone resin

5 copies

Carbon black N330

30 copies

Carbon black N330

30 copies

Aromatic oil

10 copies

sulfur

1 copy

[0043] Note * , the ratio of CR and BR in the above formula is 70 / 30. According to the parts 1, 2, 8 and 10 parts of clay added i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
glass transition temperatureaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a high-temperature underwater sound transmission rubber material and a preparation method thereof. The crystallization of chloroprene rubbers is restrained through selecting the chloroprene rubbers with slow crystallization speed and using butadiene rubbers (BR) with a certain ratio, so that the sound transmission performance and the temperature stability of the rubber material are improved; a certain parts of nanometer clay are added in a formula system to improve the water tightness of the sound transmission material; quick low-temperature and low-pressure vulcanization (100-120 DEG C, 30-40 minutes) of the rubber material is realized through optimizing the rubber material formula and the processing technique design. The underwater sound transmission rubber material with high sound transmission performance, high temperature stability, high water tightness and excellent physical and mechanical properties can be prepared through the method. The material can satisfy the requirements of a coating material of ship underwater sound equipment, and is an excellent underwater sound transmission material.

Description

technical field [0001] The invention relates to a method for preparing a high-performance underwater acoustic sound-permeable rubber material. The prepared sound-permeable material can be used as a coating material for underwater detection devices such as ship underwater acoustic equipment and seabed oil exploration equipment. Background technique [0002] In marine engineering, using sonar detection technology to locate targets is a relatively common method in marine detection, and sonar mainly relies on its key component, the transducer, to transmit and receive acoustic signals, and to ensure the normal operation of the transducer is The basic premise of realizing the detection. Therefore, higher requirements are put forward for the cladding materials of transducers and other underwater acoustic equipment: on the one hand, they must have high sound permeability; on the other hand, they must have good water tightness; . Rubber materials with high sound permeability, good ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L11/00C08L9/00C08K13/04C08K7/00C08K3/34C08K3/22C08K5/405C08K5/47C08K5/40C08K5/09C08K3/06C08K5/01C08K5/12C08K3/04C08K5/39
Inventor 赵秀英王哲张立群谢晗范进良郭长明
Owner BEIJING UNIV OF CHEM TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More