Production method of tempered high-strength Q550E super-thick steel plate
A technology of Q550E and extra-thick steel plates, which is applied in the field of iron and steel smelting, can solve the problems of low pass rate of steel plate ultrasonic flaw detection and the inability of steel plates to be used as structural parts, and achieve the effect of easy process, simple process and reduced production cost
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0038] Example 1: Quenched and tempered high-strength Q550E extra-thick steel plate with a plate thickness of 100 mm.
[0039] The chemical composition mass percentage of steel is: C=0.14, Si=0.33, Mn=1.46, P=0.012, S=0.001, Als=0.044, Nb=0.014, Ti=0.016, Ni=0.64, Cr=0.38, Mo= 0.32, B=0.0018, the balance is Fe and unavoidable impurities; CEV=0.57.
[0040] The production process steps and parameters of steel are:
[0041] (1) Continuous casting: Produce 300X2280mm cross-section continuous casting slabs according to the clean steel production method, in which the superheat of the continuous casting tundish is less than 10°C, the light reduction is 4mm, and the electromagnetic stirring current is controlled by 300A (7Hz).
[0042] (2) Heating: The slab is heated at 1290-1300°C, the heating time is 12min / cm, the soaking time is 68min, the temperature of the upper surface is 19°C higher than that of the lower surface, and the temperature of the core of the slab out of the furnace...
Embodiment 2
[0050] Example 2: Quenching and tempering high-strength Q550E extra-thick steel plates with a plate thickness of 120 mm were refined.
[0051] The chemical composition mass percentage of steel is: C=0.15, Si=0.33, Mn=1.45, P=0.013, S=0.002, Als=0.047, Nb=0.016, Ti=0.015, Ni=0.65, Cr=0.40, Mo= 0.35, B=0.0017, the balance is Fe and unavoidable impurities; CEV=0.58.
[0052] The production process steps and parameters of steel are:
[0053] (1) Continuous casting: Produce 300X2280mm cross-section continuous casting slabs according to the clean steel production method, in which the superheat of the continuous casting tundish is less than 10°C, the light reduction is 4mm, and the electromagnetic stirring current is controlled by 300A (7Hz).
[0054] (2) Heating: The slab is heated at 1290-1300°C, the heating time is 11min / cm, the soaking time is 68min, the temperature of the upper surface is 16°C higher than that of the lower surface, and the temperature of the core of the slab ou...
PUM
Property | Measurement | Unit |
---|---|---|
yield strength | aaaaa | aaaaa |
thickness | aaaaa | aaaaa |
thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com