Production method of tempered high-strength Q620D super-thick steel plate
A technology of Q620D and extra-thick steel plates, which is applied in the field of iron and steel smelting, can solve the problems that steel plates cannot be used as structural parts, and the pass rate of ultrasonic flaw detection of steel plates is low, so as to achieve the effect of easy process, simple process and reduced production cost
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0039] Example 1: Quenching and tempering high-strength Q620D extra-thick steel plate with a plate thickness of 100 mm.
[0040] The mass percentage of chemical composition of steel is: C=0.13, Si=0.33, Mn=1.46, P=0.011, S=0.001, Als=0.045, Nb=0.030, Ti=0.014, Ni=0.45, Cr=0.38, Mo= 0.32, B=0.0016, the balance is Fe and unavoidable impurities; CEV=0.55.
[0041] The production process steps and parameters of steel are:
[0042] (1) Continuous casting: Produce 300X2280mm cross-section continuous casting slabs according to the clean steel production method, in which the superheat of the continuous casting tundish is less than 10°C, the light reduction is 4mm, and the electromagnetic stirring current is controlled by 300A (7Hz).
[0043] (2) Heating: The slab is heated at 1290-1300°C, the heating time is 11min / cm, the soaking time is 64min, the temperature of the upper surface is 15°C higher than that of the lower surface, and the temperature of the core of the slab out of the fu...
Embodiment 2
[0051] Example 2: Quenched and tempered high-strength Q620D extra-thick steel plate with a plate thickness of 120 mm.
[0052] The chemical composition mass percentage of steel is:
[0053] C=0.13, Si=0.28, Mn=1.48, P=0.011, S=0.001, Als=0.038, Nb=0.015, Ti=0.017, Ni=0.48, Cr=0.36, Mo=0.36, B=0.0016, balance It is Fe and unavoidable impurities; CEV=0.55.
[0054] The production process steps and parameters of steel are:
[0055] (1) Continuous casting: Produce 300X2280mm cross-section continuous casting slabs according to the clean steel production method, in which the superheat of the continuous casting tundish is less than 10°C, the light reduction is 4mm, and the electromagnetic stirring current is controlled by 300A (7Hz).
[0056] (2) Heating: The slab is heated at 1290-1300°C, the heating time is 13min / cm, the soaking time is 71min, the upper surface temperature is 18°C higher than the lower surface, and the core temperature of the slab is 1261°C.
[0057] (3) Rolli...
PUM
Property | Measurement | Unit |
---|---|---|
yield strength | aaaaa | aaaaa |
thickness | aaaaa | aaaaa |
thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com