PVC (polyvinyl chloride) combination for storage battery shell and preparation method thereof

A technology of polyvinyl chloride and battery, applied in battery pack parts, circuits, electrical components, etc., can solve the problems of high cost, large amount of heat-resistant modifier, low impact strength, etc., and achieve excellent impact performance, strong resistance Oxygen aging performance, the effect of superior heat resistance

Active Publication Date: 2014-01-22
CHINA PETROLEUM & CHEM CORP
View PDF7 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Improve the heat resistance of polyvinyl chloride resin, but the amount of heat-resistant modifier is large, the cost is high, and the impact strength is low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • PVC (polyvinyl chloride) combination for storage battery shell and preparation method thereof
  • PVC (polyvinyl chloride) combination for storage battery shell and preparation method thereof
  • PVC (polyvinyl chloride) combination for storage battery shell and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0035] Embodiment preparation method:

[0036] (1) Mixing of raw materials: Weigh the materials of Examples 3-8 according to the ratio of raw materials, then add them to a high-speed mixer and mix until the mixing temperature is 115°C, put the materials into a low-speed mixer, and wait for the temperature of the materials to cool to 40°C Time to discharge.

[0037] (2) Special material granulation process: The mixed material is granulated by twin-screw, and the process parameters are set as follows:

[0038] Table 5: Process parameters of twin-screw granulator

[0039]

zone 1

Zone 2

District 3

District 4

District 5

nose

Extruder temperature (°C)

120

130

135

140

145

145

[0040] The preparation method of embodiment 1, 2 is the same as embodiment 3~8, and difference is that mixing temperature is 100 ℃, and discharge temperature is 37 ℃;

[0041] The preparation method of embodiment 9,10 is the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
degree of polymerizationaaaaaaaaaa
degree of polymerizationaaaaaaaaaa
Login to View More

Abstract

The invention relates to a PVC (polyvinyl chloride) combination for a storage battery shell and a preparation method thereof, belongs to the field of material science and in particular relates to an injection molding heat-resisting PVC combination and a preparation method thereof, wherein the combination is applicable to producing the storage battery shell. By virtue of adopting PVC resins with low polymerization degree, and combining specific compound heat-resisting modifiers, size stabilizers and full-ester impact modifiers, the PVC combination which has higher vicat softening temperature and superior impact property is produced. Compared with the prior art, the PVC has the following advantages: by virtue of adopting the heat-resisting modifiers with specific components and combining the size stabilizers, the heat-resisting performance of the PVC resins is improved, and therefore the PVC combination for the storage battery shell provided by the invention has higher vicat softening temperature, and by virtue of adopting the full-ester impact modifiers, the material has superior impact property, and meanwhile the anti-photoaging performance is prevented from being reduced.

Description

technical field [0001] The invention discloses a polyvinyl chloride composition for battery casings and a preparation method thereof, belonging to the field of material science, and relates to an injection-molded heat-resistant polyvinyl chloride composition and a preparation method thereof, and the composition is suitable for producing battery casings. Background technique [0002] With the rapid development of the automobile and electric vehicle industry, the battery consumption is increasing. The service conditions of the battery require that the outer casing of the material must have a high heat distortion temperature, flame retardancy and light and heat aging resistance. At present, the main materials of the battery casing are polypropylene and ABS resin. Due to the poor flame retardancy of polypropylene and ABS resin, flame retardant modification must be carried out during use. Polyvinyl chloride resin itself has flame retardant properties, but its heat distortion tem...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L33/10C08L25/16C08L35/06C08K13/02C08K3/34C08K3/04C08K5/134B29C47/92B29B9/06H01M2/02B29C48/92H01M50/121
CPCY02E60/12Y02E60/10
Inventor 贾小波张新华张学明张桦
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com