Photocatalyst Li2WV2O9 with visible light response and preparation method thereof
A photocatalyst and visible light technology, applied in chemical instruments and methods, physical/chemical process catalysts, metal/metal oxide/metal hydroxide catalysts, etc., can solve the problem of limited photocatalyst types, poor stability, and low photoconversion efficiency and other problems, to achieve excellent catalytic performance, low cost, and simple preparation methods
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0018] (1) 99.9% analytically pure chemical raw material Li 2 CO 3 、WO 3 and V 2 o 5 , press Li 2 W V 2 o 9 Chemical formula weighing ingredients.
[0019] (2) Mix the raw materials prepared in step (1), put them into a ball mill jar, add zirconia balls and absolute ethanol, ball mill for 8 hours, mix and grind until fine, take it out and dry it, and pass through a 200-mesh sieve.
[0020] (3) Pre-fire the uniformly mixed powder in step (2) at 780°C, keep it warm for 6 hours, cool it down to room temperature naturally, and then use a ball mill to make the particle diameter smaller than 2 μm, that is, Li 2 W V 2 o 9 powder.
[0021] The prepared photocatalyst can remove 97.9% of methyl orange in 120 minutes under the irradiation of visible light with a wavelength greater than 420nm.
Embodiment 2
[0023] (1) 99.9% analytically pure chemical raw material Li 2 CO 3 、WO 3 and V 2 o 5 , press Li 2 W V 2 o 9 Chemical formula weighing ingredients.
[0024] (2) Mix the raw materials prepared in step (1), put them into a ball mill jar, add zirconia balls and absolute ethanol, ball mill for 8 hours, mix and grind until fine, take it out and dry it, and pass through a 200-mesh sieve.
[0025] (3) Pre-fire the uniformly mixed powder in step (2) at 790°C, keep it warm for 6 hours, cool it down to room temperature naturally, and then use a ball mill to reduce the particle diameter to less than 2 μm to obtain Li 2 W V 2 o 9 powder.
[0026] The prepared photocatalyst can remove 98.8% of methyl orange in 120 minutes under the irradiation of visible light with a wavelength greater than 420nm.
Embodiment 3
[0028] (1) 99.9% analytically pure chemical raw material Li 2 CO 3 、WO 3 and V 2 o 5 , press Li 2 W V 2 o 9 Chemical formula weighing ingredients.
[0029] (2) Mix the raw materials prepared in step (1), put them into a ball mill jar, add zirconia balls and absolute ethanol, ball mill for 8 hours, mix and grind until fine, take it out and dry it, and pass through a 200-mesh sieve.
[0030] (3) Pre-fire the uniformly mixed powder in step (2) at 800°C, keep it warm for 6 hours, cool it down to room temperature naturally, and then use a ball mill to make the particle diameter smaller than 2 μm, that is, Li 2 W V 2 o 9 powder.
[0031] The prepared photocatalyst can remove 98.4% of methyl orange in 120 minutes under the irradiation of visible light with wavelength greater than 420nm.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com