Moisture-proof insulative coating with visible light-blocking properties

A moisture-proof insulation and coating technology, which is applied in the direction of organic insulators, radiation-absorbing coatings, insulators, etc., can solve the problems such as no record of moisture-proof insulation coatings, and achieve the effect of high shielding and high electrical insulation reliability

Inactive Publication Date: 2013-12-04
SHOWA DENKO KK
View PDF9 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although this composition shows a covering rate of 95% or more in the paint test according to JISK5400, there is no description at all about the moisture-proof insulating paint

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Moisture-proof insulative coating with visible light-blocking properties
  • Moisture-proof insulative coating with visible light-blocking properties

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0120]23.78 g of D1155 (manufactured by Clayton Polymer Co., Ltd., 40% by mass of styrene content) as a styrene-butadiene-styrene block copolymer elastomer, and 23.78 g of Quinton (registered trademark) D100 (Nippon Zeon Co., Ltd.) as a tackifier Aliphatic-aromatic copolymer-based petroleum resin) 5.22 g, KP PLAST RED G as a dye (anthraquinone dye, Color Index Constitution Number 60505 manufactured by Kiwa Chemical Industry Co., Ltd.) 0.165 g, KP PLAST YELLOW MK (Kiwa Chemical Anthraquinone-based dyes manufactured by Kogyo Co., Ltd., Color Index Constitution Number 58839) 0.118 g, Oil Blue 2N (anthraquinone-based dyes manufactured by Orient Chemical Industry Co., Ltd., Color Index Constitution Number 61554) 0.329 g, methylcyclohexane (Maruzen Petroleum Co., Ltd.) as a solvent Chemical Co., Ltd. product name: Swakryln MCH) 20.00 g, ethylcyclohexane (Maruzen Petrochemical Co., Ltd. product name: Swakryln ECH) 39.00 g, n-butyl acetate (Kyowa Hakka Chemical Co., Ltd. product name: ...

Embodiment 2

[0122] 23.78 g of D1155 (manufactured by Clayton Polymer Co., Ltd., 40% by mass of styrene content) as a styrene-butadiene-styrene block copolymer elastomer, and 23.78 g of Quinton (registered trademark) D100 (Nippon Zeon Co., Ltd.) as a tackifier Aliphatic-aromatic copolymer-based petroleum resin) 5.22 g, KP PLAST RED G as a dye (anthraquinone dye, Color Index Constitution Number 60505 manufactured by Kiwa Chemical Industry Co., Ltd.) 0.165 g, KP PLAST YELLOW MK (Kiwa Chemical Anthraquinone-based dye manufactured by Kogyo Co., Ltd., Color Index Constitution Number 58839) 0.118 g, KP PLAST BLUE GR (anthraquinone-based dye manufactured by Kiwa Chemical Industry Co., Ltd., Color Index Constitution Number 61568) 0.329 g, methylcyclohexane as a solvent (Maruzen Petrochemical Co., Ltd. product name: Swakryln MCH) 20.00 g, ethylcyclohexane (Maruzen Petrochemical Co. Trade name: butyl acetate-P) 11.00 g were mixed together to obtain complex D2.

Embodiment 3

[0124] 23.78 g of D1155 (manufactured by Clayton Polymer Co., Ltd., 40% by mass of styrene content) as a styrene-butadiene-styrene block copolymer elastomer, and 23.78 g of Quinton (registered trademark) D100 (Nippon Zeon Co., Ltd.) as a tackifier Aliphatic-aromatic copolymer-based petroleum resin) 5.22 g, KP PLAST RED HB (Anthraquinone dye, Color Index Constitution Number 60510 manufactured by Kiwa Chemical Industry Co., Ltd.) 0.165 g, KP PLAST YELLOW MK (Kiwa Chemical Industry Co., Ltd. Anthraquinone-based dyes manufactured by Kogyo Co., Ltd., Color Index Constitution Number 58839) 0.118 g, Oil Blue 2N (anthraquinone-based dyes manufactured by Orient Chemical Industry Co., Ltd., Color Index Constitution Number 61554) 0.329 g, methylcyclohexane (Maruzen Petroleum Co., Ltd.) as a solvent Chemical Co., Ltd. product name: Swakryln MCH) 20.00 g, ethylcyclohexane (Maruzen Petrochemical Co., Ltd. product name: Swakryln ECH) 39.00 g, n-butyl acetate (Kyowa Hakka Chemical Co., Ltd. pr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
boiling pointaaaaaaaaaa
viscosityaaaaaaaaaa
thermal resistanceaaaaaaaaaa
Login to View More

Abstract

Provided is a moisture-proof insulative coating for electronic parts which exhibits superior electrical insulation reliability and visible light-shielding properties. The moisture-proofing insulating coating comprises a thermoplastic elastomer, two or more kinds of dyes and a solvent, and the total light transmittance of a coated film produced by coating and drying said coating is 5% or less when the film thickness is 100 [mu]m. The thermoplastic elastomer is preferably a styrene thermoplastic elastomer such as a styrene-butadiene-styrene block copolymer elastomer. At least one of the dyes is preferably an anthraquinone dye. The dye content is preferably 0.1 - 10 parts by mass with respect to 100 parts by mass of the thermoplastic elastomer. The moisture-proofing insulating coating preferably also comprises a tackifier such as a petroleum resin tackifier.

Description

technical field [0001] The present invention relates to a moisture-proof insulating paint having a high shielding property against visible light by coating and drying the coating film. More specifically, it relates to a moisture-proof insulating paint characterized in that the total light transmittance of a coating film produced by using two or more dyes and being able to be coated and dried is 5% or less at a film thickness of 100 μm. Furthermore, the present invention relates to a moisture-proof insulating material obtained by applying and drying the moisture-proof insulating paint. Furthermore, the present invention relates to an electronic component insulated by the moisture-proof insulating material. Background technique [0002] Electrical equipment tends to become smaller, lighter, and multifunctional every year. The mounted circuit boards that can control electrical equipment and are mounted on various electrical equipment are designed to prevent damage from moistur...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D201/00C09D5/25C09D7/12C09D125/04H01B3/40H01L23/29H01L23/31
CPCC09D7/001C09D5/32H01B3/28C09D7/007C09D7/12H01B3/442C09D153/02C09D7/20C09D7/41C09D5/00C09D125/04C09D201/00H01B3/40H01L23/29H01L23/31
Inventor 和田哲夫大賀一彦江夏宽人
Owner SHOWA DENKO KK
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com