Friction material for brake pad and preparation technology of friction material

A technology of friction material and preparation process, which is applied in the field of brake pads to achieve the effect of ensuring environmental performance and improving friction resistance parameters

Active Publication Date: 2013-11-27
句容市宝亚汽车摩擦材料配件有限公司
View PDF6 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, with the improvement of people's requirements for braking performance and environmental performance of brake pads, traditional brake pad friction materials contain heavy metal components, such as copper, etc., so it is urgent to study a brake pad friction material that does not contain heavy metals. The problem

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Friction material ratio: 15% epoxy resin by weight, 8% mica, 8% Lauren fiber, 8% glass fiber, 2% mineral fiber, 4% graphite, 3% coke, 8% Antimony sulfide, 3% barite, 8% friction powder, 20% tire powder, 4% friction enhancer, 4% potassium feldspar, 3% flame retardant and 2% vermiculite. The friction-increasing agent is mainly one or more of iron ore powder, magnesium oxide, zirconium oxide, and aluminum oxide.

[0024] The preparation process includes the following steps: Step 1: Mixing of raw materials, weighing epoxy resin, mica, Lauren fiber, glass fiber, mineral fiber, graphite, coke, antimony sulfide, barite, friction powder, tire powder according to the above ratio , friction agent, potassium feldspar, flame retardant and vermiculite, and then sent to the mixer to mix the friction material evenly; Step 2: Grinding of raw materials, sending the mixed friction material to the pulverizer, and its mesh number is controlled at 40 mesh or less; step 3: hot pressing proc...

Embodiment 2

[0027] Friction material ratio: 10% epoxy resin by weight, 8% mica, 10% Lauren fiber, 10% glass fiber, 3% mineral fiber, 5% graphite, 4% coke, 8% Antimony sulfide, 4% barite, 5% friction powder, 17% tire powder, 6% friction enhancer, 6% potassium feldspar, 3% flame retardant and 1% vermiculite. The friction-increasing agent is mainly one or more of iron ore powder, magnesium oxide, zirconium oxide, and aluminum oxide.

[0028] The preparation process includes the following steps: Step 1: Mixing of raw materials, weighing epoxy resin, mica, Lauren fiber, glass fiber, mineral fiber, graphite, coke, antimony sulfide, barite, friction powder, tire powder according to the above ratio , friction agent, potassium feldspar, flame retardant and vermiculite, and then sent to the mixer to mix the friction material evenly; Step 2: Grinding of raw materials, sending the mixed friction material to the pulverizer, and its mesh number is controlled at 40 mesh or less; step 3: hot pressing pr...

Embodiment 3

[0031] Friction material ratio: 20% epoxy resin by weight, 6% mica, 6% Lauren fiber, 5% glass fiber, 3% mineral fiber, 5% graphite, 2% coke, 5% Antimony sulfide, 2% barite, 6% friction powder, 25% tire powder, 4% friction enhancer, 3% potassium feldspar, 5% flame retardant and 3% vermiculite.

[0032] The preparation process includes the following steps: Step 1: Mixing of raw materials, weighing epoxy resin, mica, Lauren fiber, glass fiber, mineral fiber, graphite, coke, antimony sulfide, barite, friction powder, tire powder according to the above ratio , friction agent, potassium feldspar, flame retardant and vermiculite, and then sent to the mixer to mix the friction material evenly; Step 2: Grinding of raw materials, sending the mixed friction material to the pulverizer, and its mesh number is controlled at 40 mesh or less; step 3: hot pressing process, sending the ground friction material into the compression molding device to obtain the semi-finished brake pad friction ma...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a friction material for a brake pad, which is characterized by comprising epoxy resin, mica, Lauren fiber, glass fiber, mineral fiber, graphite, coke, antimony sulphide, barite, friction powder, tyre powder, friction adding agent, potassium feldspar, flame retardant and vermiculite. Through the steps of mixing the raw materials, grinding the raw materials, hot pressing process and shaping process, the preparation of the friction material for the brake pad is finished, so that the friction material for the brake pad with good environmental protection performance and high abrasion resistance coefficient is obtained.

Description

technical field [0001] The invention belongs to the brake pad industry and relates to a brake pad friction material and a preparation process thereof. Background technique [0002] Brake pads are the most critical components in the braking system. The moving parts are locked by the brake pads, but the quality of the brake pads determines the braking effect. The brake pads are installed on the steel plate of the brake, and the friction material is bonded to the steel plate with an adhesive, so that when braking, the friction material is used to resist the moving parts, so that there is friction between them and the moving parts, so that the brake is installed Vehicles or equipment, etc. slow down, or even lock up. However, the quality of the friction material is closely related to the braking effect of the brake. [0003] Friction materials are usually composed of four parts: reinforcing materials, adhesives, fillers and friction modifiers. Adhesives are an important part o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09K3/14C08L21/00C08L63/00C08K13/04C08K7/14C08K7/04C08J5/14F16D69/02
Inventor 韩宏超周正祥
Owner 句容市宝亚汽车摩擦材料配件有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com